Diaper providing temperature insensitive liquid handling

• US 7,786,341 B2
• Filed: 08/06/2004
• Issued: 08/31/2010
• Est. Priority Date: 08/07/2003
• Status: Active Grant

• Current Assignee: The Procter & Gamble Company
• Original Assignee: The Procter & Gamble Company
• Inventors: van Gansewinkel, Olaf, Fuchs, Christopfer, Schneider, Manuela
• Primary Examiner(s): HAND, MELANIE JO
• Application Number:
  US10/912,991
• Publication Number:
  US 20050033252A1
• Time in Patent Office: 2,216 Days
• Field of Search: 604/365, 604/367, 604/368
• US Class Current: 604/367
• CPC Class Codes: A61F 13/537 characterised by a layer facilitating or inhibiting flow in one direction or plane, e.g. a wicking layer A61F13/538 takes precedence

Abstract

The present invention relates to absorbent articles, such as diapers and sanitary napkins, and acquisition members useful for such articles. More specifically, the invention relates to an acquisition member comprising a multitude of fibers and a latex binder, the liquid acquisition member having a void volume of at least 7 cubic centimeter per gram in the temperature range from 20° C. to 40° C., the binder comprising a dispersion of a polymer substance in an essentially aqueous medium, the polymer substance being capable of forming a film, said film having a tan δ value, as defined herein, at 20° C. and at 40° C., wherein the tan δ value at 40° C. is not greater than said tan δ value at 20° C.

Claims

1. A liquid acquisition member for an absorbent article, comprising:

a multitude of polyester fibers and a latex binder, said liquid acquisition member comprising about 20 to 40 weight percent of said binder and about 60 to 80 weight percent of said polyester fibers, wherein said polyester fibers comprise about 20 to 80 weight percent of a first type of fibers and about 20 to 80 weight percent of a second type of fibers, the second type of fibers comprising spiral-crimp fibers in the form of hollow chemically homogeneous bi-component fibers, and wherein said binder comprises a dispersion of a polymer substance in an essentially aqueous medium, said polymer substance being capable of forming a film, said film having a tan δ

value at 20°

C. and at 40°

C., wherein said tan δ

value at 40°

C. is not greater than said tan δ

value at 20°

C.

2. The liquid acquisition member according to claim 1 wherein said tan δ

value at 40°

C. is less than about 0.6.

3. The liquid acquisition member according to claim 1, wherein the binder comprises a styrene-butadiene latex binder.

4. The liquid acquisition member according to claim 1, wherein the binder comprises a styrene-butadiene latex binder and said styrene butadiene latex binder has a carboxylation level of at least about 10%.

5. The liquid acquisition member according to claim 1, wherein said fibers are polyester fibers and wherein the liquid acquisition member comprises about 20 to 40 weight percent of said binder, and about 60 to 80 weight percent of said polyester fibers.

6. The liquid acquisition member according to claim 1, wherein said fibers are polyester fibers and wherein the liquid acquisition member comprises about 20 to 40 weight percent of said binder, and about 60 to 80 weight percent of said polyester fibers and said polyester fibers comprise about 20 to 80 weight percent of a first type of fibers, and about 20 to 80 weight percent of a second type of fibers, the second type of fibers comprising spiral-crimp fibers.

7. The liquid acquisition member according to claim 1, wherein said fibers are polyester fibers and wherein the liquid acquisition member comprises about 20 to 40 weight percent of said binder, and about 60 to 80 weight percent of said polyester fibers and said polyester fibers comprise about 20 to 80 weight percent of a first type of fibers, and about 20 to 80 weight percent of a second type of fibers, and said second type of fibers comprises spiral-crimp fibers, and the first type of fibers exhibits a flat crimp.

8. The liquid acquisition member according to claim 1, wherein the polyester fibers are carded to form a nonwoven.

9. The liquid acquisition member according to claim 1, wherein said latex binder has a T_g of between −

10°

C. to +10°

C.