Method for forming a bioartificial guidance conduit

• US 7,790,080 B2
• Filed: 11/22/2005
• Issued: 09/07/2010
• Est. Priority Date: 11/22/2005
• Status: Expired due to Fees

• Current Assignee: National Taiwan University (Government of The Republic of China)
• Original Assignee: National Taiwan University (Government of The Republic of China)
• Inventors: Wang, De-Yao, Huang, Yi-You
• Primary Examiner(s): Johnson; Christina
• Assistant Examiner(s): SCHIFFMAN, BENJAMIN A
• Application Number:
  US11/283,956
• Publication Number:
  US 20070118156A1
• Time in Patent Office: 1,750 Days
• Field of Search: None
• US Class Current: 264/227
• CPC Class Codes: A61B 17/11 for performing anastomosis; Buttons for anastomosis
• CPC Class Codes: A61B 17/1128 of nerves
• CPC Class Codes: A61B 2017/00004 (bio)absorbable, (bio)resorbable, resorptive for implantable prostheses A61F2210/0004

Abstract

The present invention discloses a bioartificial guidance conduit formed by coaxially stacking a plurality of discs and the method for forming the same, wherein each disc contains at least one penetrating hole, and at least one penetrating hole on adjacent discs connects with each other while discs coaxially stacked, so as to run through the formed bioartificial guidance conduit.

Claims

1. A method for forming a bioartificial guidance conduit, comprising:

providing a substrate with a photoresist layer;

performing a lithographic process on said photoresist layer to form a mold that comprises at least one first pattern having a flat-bottom cave and at least one second pattern having a plurality of pillar-shaped structures extending from said flat-bottom cave, wherein the depth of said flat-bottom cave is substantially equal to the height of said pillar-shaped structure;

performing a mold-filling process to fill said mold with a biocompatible material, so as to form at least one disc, wherein the main body of said disc is formed by said first pattern, and at least one penetrating hole of said disc is formed by said second pattern;

performing a mold-releasing process to take out at least one said disc;

repeating said mold-filling process and said mold-releasing process to produce a plurality of said discs; and

performing a coaxially stacking process to stack said plurality of discs, and said bioartificial guidance conduit is then formed, wherein at least one said penetrating hole on adjacent said plurality of discs connects with each other, so as to run through said bioartificial guidance conduit, wherein the decomposing rate of said disc located at the middle of said bioartificial guidance conduit being slower than the decomposing rate of said disc located at the two ends of said bioartificial guidance conduit.

2. The method for forming a bioartificial guidance conduit in claim 1, wherein said first pattern is formed by etching through said substrate during said lithographic process, and a connecting structure is formed to connect said substrate with said second pattern during said lithographic process.

3. The method for forming a bioartificial guidance conduit in claim 1, wherein the material of said disc is selected as any one or any combination of the following group:

chitosan, poly (lactic acid), poly (glycolic acid) [PGA], poly (glycolide co-lactide) [PLGA], collage, polycarboxylic acid, alginate, polyamide and their derivatives.

4. The method for forming a bioartificial guidance conduit in claim 1, wherein the thickness of said disc ranges from 10 μ

m to 500 μ

m.

5. The method for forming a bioartificial guidance conduit in claim 1, wherein the cross-sectional area of said bioartificial guidance conduit ranges from 1 mm2 to 25 mm2.

6. The method for forming a bioartificial guidance conduit in claim 1, wherein the cross-sectional shape of said bioartificial guidance conduit is not perfect circle.

7. The method for forming a bioartificial guidance conduit in claim 1, wherein the cross-sectional shape of said bioartificial guidance conduit is ellipse.

8. The method for forming a bioartificial guidance conduit in claim 7, wherein the length of major axis and minor axis of the ellipse ranges from 1 mm to 5 mm.

9. The method for forming a bioartificial guidance conduit in claim 1, wherein the cross sectional area of said penetrating hole ranges from 100 μ

m2 to 106 μ

m2.

10. The method for forming a bioartificial guidance conduit in claim 1, further comprising a shell fabricating process to form a shell, so as to cover said coaxially stacked plurality of discs.

11. The method for forming a bioartificial guidance conduit in claim 10, wherein the method for fabricating said shell comprises:

coating a solution onto the outer surface of said coaxially stacked plurality of discs, wherein said solution comprises a biocompatible material; and

performing a drying process to gel said solution located on said coaxially stacked plurality of discs, and said shell is then formed.

12. The method for forming a bioartificial guidance conduit in claim 10, wherein the method for fabricating said shell comprises:

coating a solution onto the outer surface of said coaxially stacked plurality of discs to form an intermediate conduit, wherein said solution comprises a biocompatible material; and

performing a phase separation process to soak said intermediate conduit into a nonsolvent, so as to gel said solution located on said coaxially stacked plurality of discs, and said shell is then formed.

13. The method for forming a bioartificial guidance conduit in claim 10, wherein the method for fabricating said shell comprises:

providing a plate-shaped biocompatible material;

wrapping said plate-shaped biocompatible material around said coaxially stacked plurality of discs; and

performing a binding process to connect the outer surface of said coaxially stacked plurality of discs with said plate-shaped biocompatible material, so as to form said shell.

14. The method for forming a bioartificial guidance conduit in claim 10, wherein the material of said shell is selected as any one or any combination of the following group:

chitosan, poly (lactic acid), poly (glycolic acid) [PGA], poly (glycolide co-lactide) [PLGA], collage, polycarboxylic acid, alginate, polyamide and their derivatives.

15. A method for forming a bioartificial guidance conduit, comprising:

providing a substrate with a photoresist layer;

performing a lithographic process on said photoresist layer to form a first mold that comprises at least one first pattern having a flat-bottom cave and at least one second pattern having a plurality of pillar-shaped structures extending from said flat-bottom cave, the depth of said flat-bottom cave is substantially equal to the height of said pillar-shaped structure;

performing a first remolding process by said first mold and a first flexible material to fabricate a second mold;

performing a second remolding process by said second mold and a second flexible material to fabricate a third mold, wherein said third mold comprises substantially the same said first pattern and said second pattern;

performing a mold-filling process to fill said third mold with a biocompatible material, so as to form at least one disc, wherein the main body of said disc is formed by said first pattern, and at least one penetrating hole of said disc is formed by said second pattern;

performing a mold-releasing process to take out at least one said disc;

repeating said mold-filling process and said mold-releasing process to produce a plurality of said discs; and

performing a coaxially stacking process to stack said plurality of discs, so as to form said bioartificial guidance conduit, wherein at least one said penetrating hole on adjacent said plurality of discs connects with each other, so as to run through said bioartificial guidance conduit, wherein the decomposing rate of said disc located at the middle of said bioartificial guidance conduit being slower than the decomposing rate of said disc located at the two ends of said bioartificial guidance conduit.

16. The method for forming a bioartificial guidance conduit in claim 15, wherein said first pattern is formed by etching through said substrate during said lithographic process, and a connecting structure is formed to connect said substrate with said second pattern during said lithographic process.

17. The method for forming a bioartificial guidance conduit in claim 15, wherein said first flexible material and said second flexible material are independently selected from the following group:

poly(dimethyl siloxane) [PDMS], polyurethane.

18. The method for forming a bioartificial guidance conduit in claim 15, wherein said first flexible material and said second flexible material are the same.

19. The method for forming a bioartificial guidance conduit in claim 18, further comprising a surface modification process, performed after said first remolding process, to modify the surface of said second mold with hydrophobic property.

20. The method for forming a bioartificial guidance conduit in claim 15, wherein the material of said biocompatible material is selected as any one or any combination of the following group:

chitosan, poly (lactic acid), poly (glycolic acid) [PGA], poly (glycolide co-lactide) [PLGA], collage, polycarboxylic acid, alginate, polyamide and their derivatives.

21. The method for forming a bioartificial guidance conduit in claim 15, wherein the thickness of said disc ranges from 10 μ

m to 500 μ

m.

22. The method for forming a bioartificial guidance conduit in claim 15, wherein the cross-sectional area of said bioartificial guidance conduit ranges from 1 mm2 to 25 mm2.

23. The method for forming a bioartificial guidance conduit in claim 15, wherein the cross-sectional shape of said bioartificial guidance conduit is not perfect circle.

24. The method for forming a bioartificial guidance conduit in claim 15, wherein the cross-sectional shape of said bioartificial guidance conduit is ellipse.

25. The method for forming a bioartificial guidance conduit in claim 24, wherein the length of major axis and minor axis of the ellipse ranges from 1 mm to 5 mm.

26. The method for forming a bioartificial guidance conduit in claim 15, wherein the cross sectional area of said penetrating hole ranges from 100 μ

m2 to 106 μ

m2.

27. The method for forming a bioartificial guidance conduit in claim 15, further comprising a shell fabricating process to form a shell to cover said coaxially stacked plurality of discs.

28. The method for forming a bioartificial guidance conduit in claim 27, wherein the method for fabricating said shell comprises:

coating a solution onto the outer surface of said coaxially stacked plurality of discs, wherein said solution comprises a biocompatible material; and

performing a drying process to gel said solution located on said coaxially stacked plurality of discs, and said shell is then formed.

29. The method for forming a bioartificial guidance conduit in claim 27, wherein the method for fabricating said shell comprises:

coating a solution onto the outer surface of said coaxially stacked plurality of discs to form a intermediate conduit, wherein said solution comprises a biocompatible material; and

performing a phase separation process to soak said intermediate conduit into a nonsolvent, so as to gel said solution located on said coaxially stacked plurality of discs, and said shell is then formed.

30. The method for forming a bioartificial guidance conduit in claim 27, wherein the method for fabricating said shell comprises:

providing a plate-shaped biocompatible material;

wrapping said plate-shaped biocompatible material around said coaxially stacked plurality of discs; and

performing a binding process to connect the outer surface of said coaxially stacked plurality of discs with said plate-shaped biocompatible material, so as to form said shell.

31. The method for forming a bioartificial guidance conduit in claim 15, wherein the material of said shell is selected as any one or any combination of the following group:

chitosan, poly (lactic acid), poly (glycolic acid) [PGA], poly (glycolide co-lactide) [PLGA], collage, polycarboxylic acid, alginate, polyamide and their derivatives.

32. A method for forming a bioartificial guidance conduit, comprising:

providing a substrate with a photoresist layer;

performing a lithographic process on said photoresist layer to form a first mold that comprises at least one first pattern having a raised flat-top structure and at least one second pattern having a plurality of tubular holes extending into said substrate from said raised flat-top structure, wherein the height of said raised flat-top structure is substantially equal to the depth of said tubular hole;

performing a remolding process by said first mold and a flexible material to fabricate a second mold, wherein said second mold comprises a third pattern complementary to said first pattern and a fourth pattern complementary to said second pattern, and the height of said third pattern is substantially equal to the height of said fourth pattern;

performing a mold-filling process to fill said second mold with a biocompatible material, so as to form at least one disc, wherein the main body of said disc is formed by said third pattern, and at least one penetrating hole of said disc is formed by said fourth pattern;

performing a mold-releasing process to take out at least one said disc;

repeating said mold-filling process and said mold-releasing process to produce a plurality of said discs; and

performing a coaxially stacking process to stack said plurality of discs, so as to form said bioartificial guidance conduit, wherein at least one said penetrating hole on adjacent said plurality of discs connects with each other, so as to run through said bioartificial guidance conduit, wherein the decomposing rate of said disc located at the middle of said bioartificial guidance conduit being slower than the decomposing rate of said disc located at the two ends of said bioartificial guidance conduit.

33. The method for forming a bioartificial guidance conduit in claim 32, wherein said first flexible material and said second flexible material are independently selected from the following group:

poly(dimethyl siloxane) [PDMS], polyurethane.

34. The method for forming a bioartificial guidance conduit in claim 32, wherein the material of said biocompatible material is selected as any one or any combination of the following group:

chitosan, poly (lactic acid), poly (glycolic acid) [PGA], poly (glycolide co-lactide) [PLGA], collage, polycarboxylic acid, alginate, polyamide and their derivatives.

35. The method for forming a bioartificial guidance conduit in claim 32, wherein the thickness of said disc ranges from 10 μ

m to 500 μ

m.

36. The method for forming a bioartificial guidance conduit in claim 32, wherein the cross-sectional area of said bioartificial guidance conduit ranges from 1 mm2 to 25 mm2.

37. The method for forming a bioartificial guidance conduit in claim 32, wherein the cross-sectional shape of said bioartificial guidance conduit is not perfect circle.

38. The method for forming a bioartificial guidance conduit in claim 32, wherein the cross-sectional shape of said bioartificial guidance conduit is ellipse.

39. The method for forming a bioartificial guidance conduit in claim 38, wherein the length of major axis and minor axis of the ellipse ranges from 1 mm to 5 mm.

40. The method for forming a bioartificial guidance conduit in claim 32, wherein the cross sectional area of said penetrating hole ranges from 100 μ

m2 to 106 μ

m2.

41. The method for forming a bioartificial guidance conduit in claim 32, further comprising a shell fabricating process to form a shell to cover said coaxially stacked plurality of discs.

42. The method for forming a bioartificial guidance conduit in claim 41, wherein the method for fabricating said shell comprises:

coating a solution onto the outer surface of said coaxially stacked plurality of discs, wherein said solution comprises a biocompatible material; and

performing a drying process to gel said solution located on said coaxially stacked plurality of discs, and said shell is then formed.

43. The method for forming a bioartificial guidance conduit in claim 41, wherein the method for fabricating said shell comprises:

coating a solution onto the outer surface of said coaxially stacked plurality of discs to form a intermediate conduit, wherein said solution comprises a biocompatible material; and

performing a phase separation process to soak said intermediate conduit into a nonsolvent, so as to gel said solution located on said coaxially stacked plurality of discs, and said shell is then formed.

44. The method for forming a bioartificial guidance conduit in claim 41, wherein the method for fabricating said shell comprises:

providing a plate-shaped biocompatible material;

wrapping said plate-shaped biocompatible material around said coaxially stacked plurality of discs; and

performing a binding process to connect the outer surface of said coaxially stacked plurality of discs with said plate-shaped biocompatible material, so as to form said shell.

45. The method for forming a bioartificial guidance conduit in claim 32, wherein the material of said shell is selected as any one or any combination of the following group:

chitosan, poly (lactic acid), poly (glycolic acid) [PGA], poly (glycolide co-lactide) [PLGA], collage, polycarboxylic acid, alginate, polyamide and their derivatives.