Polymer electrolyte for a direct oxidation fuel cell, method of preparing the same, and direct oxidation fuel cell comprising the same

• US 7,811,694 B2
• Filed: 10/14/2005
• Issued: 10/12/2010
• Est. Priority Date: 10/14/2004
• Status: Expired due to Fees

• Current Assignee: Samsung SDI Company Limited
• Original Assignee: Samsung SDI Company Limited
• Inventors: Song, Min-Kyu, Kim, You-Mee, Kweon, Ho-jin, Rhee, Hee-Woo
• Primary Examiner(s): Mulcahy, Peter D.
• Assistant Examiner(s): HU, HENRY S
• Application Number:
  US11/251,579
• Publication Number:
  US 20060251945A1
• Time in Patent Office: 1,824 Days
• Field of Search: 429/33, 521/27, 521/28, 521/32, 526/243, 204/282
• US Class Current: 429/491
• CPC Class Codes: H01M 8/0239 Organic resins; Organic polymers
• CPC Class Codes: H01M 8/0289 Means for holding the electrolyte solid polymer electrolytes H01M8/1018
• CPC Class Codes: H01M 8/1023 having only carbon, e.g. polyarylenes, polystyrenes or polybutadiene-styrenes
• CPC Class Codes: H01M 8/1039 halogenated, e.g. sulfonated polyvinylidene fluorides
• CPC Class Codes: H01M 8/1051 Non-ion-conducting additives, e.g. stabilisers, SiO2 or ZrO2
• CPC Class Codes: H01M 8/106 characterised by the chemical composition of the porous support
• CPC Class Codes: Y02E 60/50 Fuel cells
• CPC Class Codes: Y02P 70/50 Manufacturing or production processes characterised by the final manufactured product

Abstract

A polymer electrolyte membrane for a direct oxidation fuel cell includes a porous polymer supporter having a plurality of pores, and a hydrocarbon fuel diffusion barrier layer which is formed on the polymer supporter and contains an inorganic additive dispersed in a cation exchange resin.

Claims

1. A polymer electrolyte membrane for direct oxidation fuel cells comprising:

a porous polymer supporter defining a plurality of pores; and

a hydrocarbon fuel diffusion barrier layer having a thickness between 2 and 10 μ

m on the porous polymer supporter and comprising an inorganic additive dispersed in a cation exchange resin,

wherein at least a portion of the hydrocarbon fuel diffusion barrier layer comprises a discrete layer over a top surface of the porous polymer supporter.

2. The polymer electrolyte membrane of claim 1, wherein the cation exchange resin and inorganic additive are present in at least some of the pores.

3. The polymer electrolyte membrane of claim 1, wherein the porous polymer supporter comprises a material selected from the group consisting of homopolymers of polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, polyimide, polybenzoxazole, polybenzimidazole, and copolymers thereof.

4. The polymer electrolyte membrane of claim 3, wherein the porous polymer supporter comprises a material selected from the group consisting of polytetrafluoroethylene, polyvinylidene fluoride, and copolymers thereof.

5. The polymer electrolyte membrane of claim 4, wherein the porous polymer supporter comprises a polytetrafluoroethylene homopolymer.

6. The polymer electrolyte membrane of claim 1, wherein the porous polymer supporter has a porosity of at least 80%.

7. The polymer electrolyte membrane of claim 6, wherein the porous polymer supporter has a porosity from 80% to 90%.

8. The polymer electrolyte membrane of claim 1, wherein the cation exchange resin comprises a polymer resin that includes at a side chain, a cation exchange group selected from the group consisting of a sulfonic acid group, a carboxylic acid group, a phosphoric acid group, a phosphonic acid group, and derivatives thereof.

9. The polymer electrolyte membrane of claim 1, wherein the cation exchange resin has an ion exchange ratio from 3 to 33, and an equivalent weight ranging from 700 to 2,000.

10. The polymer electrolyte membrane of claim 1, wherein the cation exchange resin comprises a proton conductive polymer selected from the group consisting of fluoro-based polymers, benzimidazole-based polymers, polyimide-based polymers, polyetherimide-based polymers, polyphenylenesulfide-based polymers, polysulfone-based polymers, polyethersulfone-based polymers, polyetherketone-based polymers, polyether-etherketone-based polymers, polyphenylquinoxaline-based polymers, and combinations thereof.

11. The polymer electrolyte membrane of claim 10, wherein the cation exchange resin is selected from the group consisting of fluoro-based polymers, polybenzimidazole-based polymers, polysulfone-based polymers, and combinations thereof.

12. The polymer electrolyte membrane of claim 1, wherein the inorganic additive is present in a delaminated form of nano-phase in the cation exchange resin.

13. The polymer electrolyte membrane of claim 1, wherein the inorganic additive comprises a material selected from the group consisting of silica, alumina, zeolite, bariumtitanate, ceramics, inorganic silicate;

zirconium hydrogen phosphate, α

-Zr(O_a1PCH_a2OH)_a(O_b1PC_b2H_b4SO_b5H)_b.nH₂O where a1, a2, a, b1, b2, b4, b5 and b are the same or different integers from 0 to 14 and n is an integer from 0 to 50, v-Zr(PO_a1) (H_a2PO_a3)_a(HO_b1PC_b2H_b3SO_b4H)_b.nH₂O where a1, a2, a3, a, b1, b2, b3, b4 and b are the same or different integers from 0 to 14 and n is an integer from 0 to 50, Zr(O_a1PC_a2H_a3)_aY_b where a1, a2, a3, a and b are the same or different integers from 0 to 14, Zr(O_a1PCH_a2OH)_aY_b.nH₂O where a1, a2, a and b are the same or different integers from 0 to 14 and n is an integer from 0 to 50, α

-Zr(O_a1PC_a2H_a3SO_a4H)_a.nH₂O where a1, a2, a3, a4 and a are the same or different integers from 0 to 14 and n is an integer from 0 to 50, α

-Zr(O_a1POH).H₂O where a1 is an integer from 0 to 14, (P₂O₅)_a(ZrO₂)_b glass where a and b are the same or different integers from 0 to 14, P₂O₅—

ZrO₂—

SiO₂ glass, and mixtures thereof.

14. The polymer electrolyte membrane of claim 13, wherein the inorganic additive is an inorganic silicate.

15. The polymer electrolyte membrane of claim 14, wherein the inorganic silicate is selected from the group consisting of pyrophylite-talc, montmorillonite (MMT), fluorohectorite, kaolinite, vermiculite, illite, mica, brittle mica, and combinations thereof.

16. The polymer electrolyte membrane of claim 14, wherein the inorganic silicate has an aspect ratio from 1/30 to 1/1000.

17. The polymer electrolyte membrane of claim 14, wherein the inorganic silicate has a long-axis length from 0.05 μ

m to 0.5 μ

m.

18. The polymer electrolyte membrane of claim 14, wherein the inorganic silicate has a delaminated layered structure with distances between silicate layers of at least 3 nm.

19. The polymer electrolyte membrane of claim 14, wherein the inorganic silicate is silicate treated by an organic modifying agent.

20. The polymer electrolyte membrane of claim 19, wherein the organic modifying agent comprises at least one compound selected from the group consisting of C1 to C20 alkylamines, C1 to C20 alkylene diamines, C1 to C20 quaternary ammonium salts, aminohexanes and nitrogen-containing heterocyclic compounds.

21. The polymer electrolyte membrane of claim 1, wherein the cation exchange resin is present in an amount from 50 to 90 wt %, the porous polymer supporter is present in an amount from 2 to 30 wt %, and the inorganic additive is present in an amount from 0.5 to 20 wt %.

22. The polymer electrolyte membrane of claim 21, wherein the cation exchange resin is present in an amount from 70 to 80 wt %, the porous polymer supporter is present in an amount from 2 to 15 wt %, and the inorganic additive is present in an amount from 0.5 to 10 wt %.

23. The polymer electrolyte membrane of claim 1, wherein the hydrocarbon fuel diffusion barrier layer further comprises an acrylate-based polymer having a low molecular weight.

24. The polymer electrolyte membrane of claim 1, wherein the hydrocarbon fuel diffusion barrier layer further comprises an acrylate-based polymer in an amount from 5 to 10 parts by weight based on 100 parts by weight of the cation exchange resin.

25. The polymer electrolyte membrane of claim 1, wherein the porous polymer supporter has a thickness from 10 to 15 μ

m.

26. The polymer electrolyte membrane of claim 1, wherein the polymer electrolyte membrane has a thickness from 5 to 100 μ

m.

27. The polymer electrolyte membrane of claim 1, wherein the conductivity difference between one side of the polymer electrolyte membrane and an opposite side of the polymer electrolyte membrane upon which a catalyst layer is formed is less than 5%.

28. The polymer electrolyte membrane of claim 1, wherein the polymer electrolyte membrane has a porosity from 1 to 10%.