Methods of making smooth reinforced cementitious boards

• US 7,846,278 B2
• Filed: 10/29/2003
• Issued: 12/07/2010
• Est. Priority Date: 01/05/2000
• Status: Expired due to Fees

• Current Assignee: Saint-Gobain Adfors Canada Ltd.
• Original Assignee: Saint-Gobain Technical Favbrics America Incorporated (Compagnie de Saint-Gobain SA)
• Inventors: Porter, John Frederick
• Primary Examiner(s): Maki; Steven D
• Application Number:
  US10/696,751
• Publication Number:
  US 20040084127A1
• Time in Patent Office: 2,596 Days
• Field of Search: 156/39, 156/44, 156/281, 156/319
• US Class Current: 156/39
• CPC Class Codes: B28B 19/0092 to webs, sheets or the like, e.g. of paper, cardboard
• CPC Class Codes: B32B 2255/02 on fibrous or filamentary layer
• CPC Class Codes: B32B 2255/26 Polymeric coating
• CPC Class Codes: B32B 2262/101 Glass fibres
• CPC Class Codes: B32B 2305/08 Reinforcements
• CPC Class Codes: B32B 2305/20 in the form of a non-woven mat
• CPC Class Codes: B32B 2305/38 Meshes, lattices or nets
• CPC Class Codes: B32B 2419/00 Buildings or parts thereof walls, panels B32B2607/00
• CPC Class Codes: B32B 27/16 specially treated, e.g. irradiated
• CPC Class Codes: B32B 5/022 Non-woven fabric
• CPC Class Codes: B32B 5/028 Net structure, e.g. spaced apart filaments bonded at the crossing points
• CPC Class Codes: B32B 5/26 another layer next to it also being fibrous or filamentary relative arrangement of fibres or filaments of different layers B32B5/12
• CPC Class Codes: D04H 1/52 by applying or inserting filamentary binding elements
• CPC Class Codes: D06B 3/10 of fabrics D06B3/24, D06B3/28, D06B3/32 take precedence; jiggers D06B3/32
• CPC Class Codes: E04C 2/06 reinforced
• CPC Class Codes: E04C 5/07 Reinforcing elements of material other than metal, e.g. of glass, of plastics, or not exclusively made of metal metal elements with non-structural coatings E04C5/01
• CPC Class Codes: Y10T 156/10 Methods of surface bonding and/or assembly therefor
• CPC Class Codes: Y10T 428/24994 Fiber embedded in or on the surface of a polymeric matrix
• CPC Class Codes: Y10T 442/10 Scrim [e.g., open net or mesh, gauze, loose or open weave or knit, etc.]
• CPC Class Codes: Y10T 442/105 Comprising a composite fiber
• CPC Class Codes: Y10T 442/133 : Inorganic fiber-containing scrim
• CPC Class Codes: Y10T 442/141 : Including a woven fabric which is not a scrim
• CPC Class Codes: Y10T 442/143 : Including a nonwoven fabric which is not a scrim
• CPC Class Codes: Y10T 442/159 : Including a nonwoven fabric which is not a scrim
• CPC Class Codes: Y10T 442/171 : Including a layer derived from a water-settable material [e.g., cement, gypsum, etc.]
• CPC Class Codes: Y10T 442/197 : Including a nonwoven fabric which is not a scrim
• CPC Class Codes: Y10T 442/674 : Nonwoven fabric with a preformed polymeric film or sheet

Abstract

A composite fabric for use in reinforcement of cementitious boards and similar prefabricated building wall panels. The fabric includes an open mesh first component of continuously coated, high modulus of elasticity strands and a nonwoven second component fabricated from alkali resistant thermoplastic material. The high modulus strands of the first component are preferably bundled glass fibers encapsulated by alkali and water resistant thermoplastic material. The composite fabric also has suitable physical characteristics for embedment within the cement matrix of the panels or boards closely adjacent the opposed faces thereof. The reinforcement provides long-lasting, high strength tensile reinforcement and impact resistance for the panels or boards. The reinforcement also enables the boards to have smooth outer faces suitable for painting, papering, tiling or other finishing treatment. Included as part of the invention are methods for making the reinforcement, cementitious boards and panels including the reinforcement, and methods for manufacturing such boards and panels.

Claims

1. A method of making a reinforced smooth cementitious board having a cement skin adjacent to an outer face, comprising:

(a) depositing a reinforcement fabric and a layer of hydraulic cementitious material, one on the other, wherein the reinforcement fabric comprises an open mesh united with a thin, porous nonwoven web;

(b) prior to depositing the reinforcement fabric and the layer of hydraulic cementitious material one on the other, applying a slurry having a cement powder and one or more of, hydrophilic additives, wetting agents, foaming agents and foam boosters to either or both of the open mesh and the thin, porous nonwoven web, and drying the slurry;

(c) penetrating the open mesh with the layer of hydraulic cementitious material and imbedding the open mesh in the layer of hydraulic material;

(d) promoting penetration through the thin, porous nonwoven web by a portion of the layer of hydraulic cementitious material to form the cement skin adjacent to the outer face by having the thin, porous nonwoven web comprise alkali resistant polymer fibers coated with a hydrophilic material;

(e) penetrating through the thin, porous nonwoven web by said portion of the layer of hydraulic cementitious material to form the cement skin adjacent to the outer face and embed the thin, porous web in the layer of hydraulic cementitious material at a depth from the outer face; and

(f) curing the layer of hydraulic cementitious material to form a layer of hardened cementitious material imbedding the open mesh and the thin, porous nonwoven web at a depth from the outer face, wherein a portion of the layer of hardened cementitious material comprises the cement skin adjacent to the outer face.

2. The method of claim 1, wherein the open mesh comprises glass fibers sheathed with alkali resistant material and the sheathed fibers are fused together at intersections of the open mesh.

3. The method of claim 1, comprising forming the open mesh by wrapping glass fibers with fibers of an alkali resistant material and applying heat to fuse the fibers of the alkali resistant material to provide sheathed glass fibers sheathed by the alkali resistant material, and joining the sheathed glass fibers at intersection areas thereof within the open mesh.

4. The method of claim 1, wherein the nonwoven web is a spunbonded web.

5. The method of claim 1, wherein the open mesh comprises glass fibers sheathed with alkali resistant material and the sheathed fibers are fused together at intersections of the open mesh, and wherein the nonwoven web is a spunbonded web.

6. A method of making a reinforced smooth cementitious board having a cement skin adjacent to an outer face, comprising:

(a) depositing a layer of hydraulic cementitious material onto a reinforcement fabric thereby depositing one on the other, wherein the reinforcement fabric comprises an open mesh united with a thin, porous nonwoven web;

(b) prior to depositing the layer of hydraulic cementitious material onto the reinforcement fabric, applying a slurry having a cement powder and one or more of, hydrophilic additives, wetting agents, foaming agents and foam boosters to either or both of the open mesh and the thin, porous nonwoven web, and drying the slurry;

(c) penetrating the open mesh with the layer of hydraulic cementitious material and imbedding the open mesh in the layer of hydraulic cementitious material;

(d) promoting penetration through the thin, porous nonwoven web by a portion of the layer of hydraulic cementitious material to form the cement skin adjacent to the outer face by having the thin, porous nonwoven web comprise alkali resistant polymer fibers coated with a hydrophilic material;

(e) penetrating through the thin, porous nonwoven web by said portion of the layer of hydraulic cementitious material to form the cement skin adjacent to the outer face and embed the thin, porous web in the layer of hydraulic cementitious material at a depth from the outer face;

(f) curing the layer of hydraulic cementitious material to form a layer of hardened cementitious material imbedding the open mesh and the thin, porous nonwoven web at a depth from the outer face, wherein a portion of the layer of hardened cementitious material comprises the cement skin adjacent to the outer face; and

(g) compacting the layer of hydraulic cementitious material and the reinforcement fabric.

7. A method of making a reinforced smooth cementitious board having a cement skin adjacent to an outer face, comprising:

(a) depositing a reinforcement fabric onto a layer of hydraulic cementitious material thereby depositing one on the other, wherein the reinforcement fabric comprises an open mesh united with a thin, porous nonwoven web;

(b) prior to depositing the reinforcement fabric onto the layer of hydraulic cementitious material, applying a slurry having a cement powder and one or more of, hydrophilic additives, wetting agents, foaming agents and foam boosters to either or both of the open mesh and the thin, porous nonwoven web, and drying the slurry;

(c) penetrating the open mesh with the layer of hydraulic cementitious material and imbedding the open mesh in the layer of hydraulic material;

(d) promoting penetration through the thin, porous nonwoven web by a portion of the layer of hydraulic cementitious material to form the cement skin adjacent to the outer face by having the thin, porous nonwoven web comprise alkali resistant polymer fibers coated with a hydrophilic material;

(e) penetrating through the thin, porous nonwoven web by said portion of the layer of hydraulic cementitious material to form the cement skin adjacent to the outer face and embed the thin, porous web in the layer of hydraulic cementitious material at a depth from the outer face;

(f) curing the layer of hydraulic cementitious material to form a layer of hardened cementitious material imbedding the open mesh and the thin, porous nonwoven web at a depth from the outer face, wherein a portion of the layer of hardened cementitious material comprises the cement skin adjacent to the outer face; and

(g) compacting the reinforcement fabric and the layer of hydraulic cementitious material.