Reinforced porous coating

• US 7,901,727 B2
• Filed: 09/15/2006
• Issued: 03/08/2011
• Est. Priority Date: 09/16/2005
• Status: Expired due to Fees

• Current Assignee: Axis Biodental S.A., Debiotech S.A.
• Original Assignee: Debiotech S.A.
• Inventors: Neftel, Frederic, Piveteau, Laurent-Dominique, Hofmann, Heinrich
• Primary Examiner(s): Meeks; Timothy H
• Assistant Examiner(s): Sellman; Cachet I
• Application Number:
  US12/066,114
• Publication Number:
  US 20080249616A1
• Time in Patent Office: 1,635 Days
• Field of Search: 427/2.1, 427/2.24, 427/2.25, 427/180, 427/202, 427/203
• US Class Current: 427/2.1
• CPC Class Codes: A61L 2300/00 Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices
• CPC Class Codes: A61L 27/28 Materials for coating prostheses
• CPC Class Codes: A61L 27/54 Biologically active materials, e.g. therapeutic substances A61L27/227 takes precedence
• CPC Class Codes: A61L 27/56 Porous materials, e.g. foams or sponges
• CPC Class Codes: A61L 31/08 Materials for coatings
• CPC Class Codes: A61L 31/146 Porous materials, e.g. foams or sponges
• CPC Class Codes: A61L 31/16 Biologically active materials, e.g. therapeutic substances A61L31/047 takes precedence
• CPC Class Codes: Y10T 428/249978 Voids specified as micro

Abstract

The present invention relates to a process for manufacturing a porous coating with structures in the micro or nano-size domain characterized by the following steps: —providing a support having a surface, —depositing on said surface one mono-layer of temporary particles, —depositing a coating on said temporary particles in such a way that the thickness of said coating is less than the particle diameter, —eliminating said temporary particles and thereby obtaining a porous coating, the pores of said coating corresponding to the spaces previously occupied by the temporary particles and at least a part of the pores communicating with the external environment, —applying a coating fixation step, characterized by the fact that said temporary particles are deposited on said surface in such a way that, after particle deposition, more than 50% of the temporary particles are in contact with a maximum of two adjacent particles and otherwise are separated by an empty space. The invention also concerns a coating and an object which can be obtained with this process.

Claims

1. Process for manufacturing a porous coating with structures of micro or nano-size domain comprising the following steps:

providing a support having a surface,

depositing on said surface one mono-layer of temporary particles,

depositing a coating on said temporary particles in such a way that the thickness of said coating is less than the particle diameter,

eliminating said temporary particles and thereby obtaining a porous coating having pores, the pores of said coating corresponding to the spaces previously occupied by the temporary particles and at least a part of the pores communicating with the external environment,

applying a coating fixation step,

wherein said temporary particles are deposited on said surface in such a way that, after particle deposition, more than 50% of the temporary particles are in contact with a maximum of two adjacent particles and otherwise are separated from other particles by an empty space, and

wherein the process has no etching step after the depositing step.

2. Process according to claim 1 wherein, after particle deposition more than 70% of the temporary particles are in contact with a maximum of two adjacent particles and otherwise are separated from other particles by an empty space.

3. Process according to claim 1 wherein said temporary particles are charged and therefore repulsion occurs between particles maintaining a certain distance between them.

4. Process according to claim 1 wherein said temporary particles are coated with long polymeric chains extending towards the outside in such a way that steric repulsion provoked by these chains maintains a certain distance between the particles.

5. Process according to claim 1 wherein a layer of ceramic nanoparticles mixed with a dispersing agent is first deposited onto the substrate so that the presence of this layer limits the movements of the particles when they are then deposited onto the substrate and therefore counteract the capillary forces.

6. Process according to claim 1 wherein a soft layer is first deposited onto the substrate so that when particles are deposited onto this layer, they slightly penetrate the layer and therefore cannot move freely anymore.

7. Process according to claim 1 further comprising a filling step where said pores are at least partially filled with a liquid or solid substance.

8. Process according to claim 7 furthermore comprising a covering step wherein the porous coating is covered with a biodegradable substance that will dissolve over time.

9. Process according to claim 8 wherein the biodegradable substance contains a substance to be released for medical purpose.

10. Process according to claim 1 wherein said temporary particles have at least two different diameters.

11. Process according to claim 1 wherein said support is made of temporary particles.

12. Process according to claim 11 wherein more than 50% of the temporary particles which constitute said support are in contact with a maximum of two adjacent particles and otherwise are separated by an empty space.

13. Process according to claim 11 wherein the temporary particles which constitute said support have a larger diameter than the particles deposited on said support.

14. Process according to claim 13 wherein the pores formed on said support are at least partially filled with a liquid or solid substance.

15. Process according to claim 1 wherein the temporary particles and the coating are deposited together as a slurry.

16. Process according to claim 1 wherein the substrate is first partially or fully covered by a hydrophobic respectively hydrophilic layer creating hydrophobic respectively hydrophilic domains on the substrate.

17. Process according to claim 1 wherein hydrophobic respectively hydrophilic particles are used to build the mono-layer of temporary particles exclusively onto hydrophobic respectively hydrophilic domains of the substrate.

18. Process according to claim 1 wherein the coating fixation step takes place before the particle elimination step.

19. Process according to claim 1 wherein the coating fixation step takes place simultaneously with the particle elimination step.

20. Process according to claim 1 wherein the coating fixation step takes place after the particle elimination step.