Patterned light extraction sheet and method of making same

• US 7,955,531 B1
• Filed: 03/15/2007
• Issued: 06/07/2011
• Est. Priority Date: 04/26/2006
• Status: Active Grant

• Current Assignee: Rohm and Haas Electronic Materials LLC (DuPont de Nemours, Inc.)
• Original Assignee: Rohm and Haas Electronic Materials LLC (DuPont de Nemours, Inc.)
• Inventors: Khanarian, Garo
• Primary Examiner(s): Vargot; Mathieu D.
• Application Number:
  US11/724,387
• Time in Patent Office: 1,545 Days
• Field of Search: 264/1.1, 264/1.21, 264/1.7, 264/1.9, 264/2.7, 257/79, 257/98, 257/100, 359/599, 362/606, 362/611, 362/613, 362/800, 156/60
• US Class Current: 264/1.7
• CPC Class Codes: G02B 6/0036 2-D arrangement of prisms, protrusions, indentations or roughened surfaces
• CPC Class Codes: H01L 33/22 Roughened surfaces, e.g. at the interface between epitaxial layers
• CPC Class Codes: H01L 33/56 Materials, e.g. epoxy or silicone resin
• CPC Class Codes: H10K 50/841 Self-supporting sealing arrangements
• CPC Class Codes: H10K 50/854 comprising scattering means
• CPC Class Codes: Y10T 156/10 Methods of surface bonding and/or assembly therefor

Abstract

A light extraction encapsulant sheet having a patterned encapsulant region is disclosed. A method of making that light extraction encapsulant sheet and of affixing that light extraction encapsulant sheet to a luminous stack surface of a multi-layer stack is also disclosed.

Claims

1. A method of preparing a light extraction encapsulant sheet, comprising the steps of:

A) providing an encapsulant block comprising a polymeric encapsulant material; and

B) forming a patterned encapsulant region having an exterior patterned encapsulant surface on a surface of said encapsulant block;

wherein said step of forming said patterned encapsulant region comprises;

a) forming a first recess set comprising at least one first recess;

b) filling said first recess with a first recess filler;

c) optionally, forming a second recess set comprising at least one second recess; and

filling said second recess with a second recess filler;

wherein at least one of said first recess set and said second recess set has a pattern wherein;

said pattern is a periodic pattern,

said pattern has a feature size, in at least one lateral dimension, of at least 5 nanometers and no more than 5,000 microns;

said periodic pattern has a period, in at least one lateral dimension, of at least 10 nanometers and no more than 5,000 microns;

said first recess has a maximum recess depth of at least 25 nanometers and no more than 10,000 microns;

said second recess has a maximum recess depth of at least 25 nanometers and no more than 10,000 microns;

at least one of said first recess and said second recess has a recess opening coincident with said exterior patterned encapsulant surface; and

said first recess filler differs in refractive index from at least one of said second recess filler and said encapsulant material by at least 0.001 and no more than 3.0.

2. The method of claim 1, wherein:

said pattern has a feature size, in at least one lateral dimension, of at least 5 nanometers and no more than 2,000 nanometers; and

said periodic pattern has a period, in at least one lateral dimension, of at least 10 nanometers and no more than 2,000 nanometers.

3. The method of claim 1, wherein at least one of said first recess filler and said second recess filler is selected from GaN, SiC, AlN, ZnS, TiO₂ ZnO, GaP, and high RI glass.

4. The method of claim 1, wherein at least one of said first recess filler and said second recess filler is a curable B-staged optical material comprising porogen particles having a mean particle size of at least 5 nm and no more than 50 nm, wherein said curable B-staged optical material is further subjected to the steps of:

curing said curable B-staged optical material; and

removing said porogen particles to form a cured B-staged optical material comprising pores,

wherein said pores have a mean pore size of at least 5 nm and no more than 50 nm; and

wherein said cured B-staged optical material has a porosity of at least 0.1 volume percent and no more than 95 volume percent, based on the volume of said cured B-stage optical material.

5. The method of claim 1, wherein said encapsulant material is a cured B-staged optical material comprising pores, wherein said encapsulant material is formed by the further steps of:

providing a curable B-staged optical material comprising porogen particles having a mean particle size of at least 5 nm and no more than 50 nm;

forming said curable B-staged optical material into a shape desired for said encapsulant block;

curing said curable B-staged optical material to form a cured B-stage optical material; and

removing said porogen particles to form said cured B-staged optical material comprising pores,

wherein said pores have a mean pore size of at least 5 nm and no more than 50 nm; and

wherein said cured B-staged optical material has a porosity of at least 0.1 volume percent and no more than 95 volume percent, based on the volume of said cured B-stage optical material.

6. The method of claim 1 further comprising the steps of:

C) affixing said light extraction encapsulant sheet to a multi-layer stack,

wherein said multi-layer stack comprises;

an n-doped layer;

a light-generating layer; and

a p-doped layer,

wherein said multi-layer stack has a luminous stack surface; and

wherein said exterior patterned encapsulant surface is disposed upon said luminous stack surface;

wherein said luminous stack surface has a topography selected from smooth surface and patterned multilevel surface; and

wherein said patterned multilevel surface has a periodic pattern; and

D) optionally removing all or a portion of said encapsulant material from contact with said any or said first recess set and said second recess set.

7. The method of claim 6,

wherein said multi-layer stack further comprises high refractive index top layer disposed upon said luminous stack surface,

wherein, after said affixing, said high refractive index top layer is an intervening high refractive index layer disposed between said exterior patterned encapsulant surface and said luminous stack.

8. The method of claim 6, further comprising the step of applying an optical adhesive to either or both of said exterior patterned encapsulant surface and said luminous stack surface before said step of affixing.

9. A light extraction encapsulant sheet suitable for encapsulating a light emitting device, formed by the method of claim 1, comprising:

a proximal patterned encapsulant region comprising a polymeric encapsulant material having a proximal patterned encapsulant surface, said region comprising;

a first recess set comprising at least one first recess comprising a first recess filler;

optionally, a second recess set comprising at least one second recess comprising a second recess filler; and

a proximal patterned encapsulant surface exterior to said encapsulant sheet;

wherein at least one of said first recess set and said second recess set has a pattern wherein;

said pattern is a periodic pattern,

said pattern has a feature size, in at least one lateral dimension, of at least 5 nanometers and no more than 5,000 microns;

said periodic pattern has a period, in at least one lateral dimension, of at least 10 nanometers and no more than 5,000 microns;

said first recess has a maximum recess depth of at least 25 nanometers and no more than 10,000 microns;

said second recess has a maximum recess depth of at least 25 nanometers and no more than 10,000 microns;

at least one of said first recess and said second recess has a recess opening coincident with said exterior patterned encapsulant surface; and

said first recess filler differs in refractive index from at least one of second recess filler and said encapsulant material by at least 0.001 and no more than 3.0.

10. The light extraction encapsulant sheet of claim 9,

wherein at least one of said first recess filler and said second recess filler is selected from GaN, SiC, AlN, ZnS, TiO₂ ZnO, GaP, and high RI glass;

and

wherein, optionally, at least one of said first recess filler and said second recess filler is a cured B-staged optical material comprising pores,

wherein said pores have a mean pore size of at least 5 nm and no more than 50 nm; and

wherein said cured B-staged optical material has a porosity of at least 0.1 volume percent and no more than 95 volume percent, based on the volume of said cured B-stage optical material.