Polymer blends

• US 7,956,129 B2
• Filed: 08/12/2004
• Issued: 06/07/2011
• Est. Priority Date: 08/19/2003
• Status: Active Grant

• Current Assignee: Ineos Sales (Uk) Limited (Ineos AG)
• Original Assignee: Ineos Europe Limited (China National Petroleum Corporation)
• Inventors: Chai, Choon Kooi
• Primary Examiner(s): Nutter; Nathan M
• Application Number:
  US10/567,927
• Publication Number:
  US 20070083009A1
• Time in Patent Office: 2,490 Days
• Field of Search: 525/191, 525/240, 524/515
• US Class Current: 525/191
• CPC Class Codes: C08L 2205/02 containing two or more polymers of the same C08L -group
• CPC Class Codes: C08L 23/06 Polyethene
• CPC Class Codes: C08L 2666/06 Homopolymers or copolymers of unsaturated hydrocarbons; Derivatives thereof
• CPC Class Codes: C09D 123/0815 Copolymers of ethene with aliphatic 1-olefins

Abstract

Novel polymer blends comprise (a) 1-99% by weight of a copolymer of ethylene and an alpha olefin having from 3 to 10 carbon atoms, said copolymer having (iv) a density in the range 0.905 to 0.940 g cm⁻³, (v) a melt elastic modulus G′ (G″=500 Pa) in the range 10 to 150 Pa, and (vi) a melt index in the range 5 to 50, and (b) from 1-99% by weight of a low density polyethylene (LDPE) polymer having a density from 0.914 to 0.928 g cm⁻³ wherein the sum of (a) and (b) is 100%. The copolymers of component (a) are typically prepared by use of metallocene catalysts. The blends exhibit advantageous melt elastic modulus in the range 30 to 200 Pa. The blends are particularly suitable for extrusion coating applications.

Claims

1. A polymer blend comprising:

(a) 1-99% by weight of a copolymer of ethylene and an alpha olefin having from 3 to 10 carbon atoms, said copolymer having

(i) a density in the range 0.905 to 0.940 g cm<sup>−

3</sup>,

(ii) a melt elastic modulus G′

(G″

=500 Pa) in the range 10 to 150 Pa, and

(iii) a melt index (190°

C./2.16 kg) in the range 5 to 50 g/10 ml, and

(b) from 1-99% by weight of a low density polyethylene (LDPE) comprising a homopolymer of ethylene having a density from 0.914 to 0.928 g cm<sup>−

3</sup>,

wherein the sum of (a) and (b) is 100%.

2. A polymer blend according to claim 1 wherein the copolymer of component (a) has a density in the range 0.907 to 0.915 g cm⁻

3.

3. A polymer blend according to claim 1 wherein the copolymer of component (a) has a melt index in the range 12 to 50 g/10 ml.

4. A polymer blend according to claim 1 wherein the copolymer of component (a) has a melt elastic modulus G′

in the range 11 to 90 Pa.

5. A polymer blend according to claim 1 wherein the copolymer of component (a) has a flow activation energy (Ea) in the range 28 to 50 kJ/mol.

6. A polymer blend according to claim 1 wherein the copolymer of component (a) has a Mw/Mn in the range 2 to 3.5.

7. A polymer blend according to claim 1 wherein the copolymer of component (a) exhibits more than one differential scanning calorimetry (DSC) melting peaks between 30°

and 150°

C.

8. A polymer blend according to claim 1 wherein the LDPE of component (b) has a melt index in the range 0.1 to 25 g/10 ml.

9. A polymer blend according to claim 1 wherein the LDPE of component (b) has a melt elastic modulus G′

in the range 80 to 200 Pa.

10. A polymer blend according to claim 1 wherein the ratio of component (a) to component (b) is in the range 60:

75 to 40;

25 by weight.

11. A polymer blend according to claim 1 wherein the blend has a melt elastic modulus G′

in the range 30 to 200 Pa.

12. A polymer blend according to claim 11 wherein the blend has a melt elastic modulus G′

in the range 30 to 200 Pa.

13. A polymer blend according to claim 12 wherein the blend has a melt elastic modulus G′

in the range 60 to 120 Pa.

14. A polymer blend according to claim 13 wherein the melt elastic modulus G′

is in the range 75-100 Pa.

16. A polymer blend according to claim 1 wherein the copolymer of component (a) is prepared by use of a catalyst system comprising a transition metal compound.

17. A polymer blend according to claim 16 wherein the transition metal compound is a metallocene.

18. A polymer blend according to claim 17 wherein the metallocene has the general formula:

19. A polymer blend according to claim 16 wherein the copolymer is prepared in the gas phase.

20. A polymer blend according to claim 1 wherein the low density polyethylene (LDPE) of component (b) is prepared by a high pressure process.

15. A polymer blend comprising:

(a) 1-99% by weight of a copolymer of ethylene and an alpha olefin having from 3 to 10 carbon atoms, said copolymer having

(iv) a density in the range 0.905 to 0.940 g cm<sup>−

3</sup>,

(v) a melt elastic modulus G′

(G″

=500 Pa) in the range 10 to 150 Pa, and

(vi) a melt index (190°

C./2.16 kg) in the range 5 to 50 g/10 ml, and

(b) from 1-99% by weight of a low density polyethylene (LDPE) comprising a homopolymer of ethylene having a density from 0.914 to 0.928 g cm<sup>−

3</sup>, and

(c) from 0-98% by weight of a copolymer of ethylene and an alpha-olefin having 3 to 10 carbon atoms or a low density polyethylene (LDPE),

wherein the sum of (a), (b) and (c) is 100%.

21. An extrusion coating comprising a polymer blend comprising:

(a) 1-99% by weight of a copolymer of ethylene and an alpha olefin having from 3 to 10 carbon atoms, said copolymer having

(i) a density in the range 0.905 to 0.940 g cm<sup>−

3</sup>,

(ii) a melt elastic modulus G′

(G″

=500 Pa) in the range 10 to 150 Pa, and

(iii) a melt index (190°

C./2.16 kg) in the range 5 to 50 g/10 ml, and

(b) from 1-99% by weight of a low density polyethylene (LDPE) comprising a homopolymer of ethylene having a density from 0.914 to 0.928 g cm<sup>−

3</sup>,

wherein the sum of (a) and (b) is 100%.

22. An extrusion coating comprising a polymer blend comprising:

(a) 1-99% by weight of a copolymer of ethylene and an alpha olefin having from 3 to 10 carbon atoms, said copolymer having

(i) a density in the range 0.905 to 0.940 g cm<sup>−

3</sup>,

(ii) a melt elastic modulus G′

(G″

=500 Pa) in the range 10 to 150 Pa, and

(iii) a melt index (190°

C./2.16 kg) in the range 5 to 50 g/10 ml,

(b) from 1-99% by weight of a low density polyethylene (LDPE) comprising a homopolymer of ethylene having a density from 0.914 to 0.928 g cm<sup>−

3</sup>, and

(c) from 0.98% by weight of a copolymer of ethylene and an alpha olefin having 3 to 10 carbon atoms or a low density polyethylene (LDPE) polymer wherein the sum of (a), (b) and (c) is 100%.