Magnetic regenerator, a method of making a magnetic regenerator, a method of making an active magnetic refrigerator and an active magnetic refrigerator

• US 8,061,147 B2
• Filed: 12/19/2005
• Issued: 11/22/2011
• Est. Priority Date: 01/12/2005
• Status: Expired due to Fees

• Current Assignee: Technical University of Denmark
• Original Assignee: Technical University of Denmark
• Inventors: Dinesen, Anders Reves, Smith, Anders, Pryds, Nini, Linderoth, Soren
• Primary Examiner(s): Ali; Mohammad
• Application Number:
  US11/795,034
• Publication Number:
  US 20090113897A1
• Time in Patent Office: 2,164 Days
• Field of Search: 62/31, 62/6, 621/14, 62/56, 624/67, 296/021, 298/900.35, 165/4, 165/104.11, 361/133
• US Class Current: 62/3.1
• CPC Class Codes: F25B 21/00 Machines, plants or systems, using electric or magnetic effects
• CPC Class Codes: F25B 2321/002 by using magneto-caloric effects
• CPC Class Codes: H01F 1/012 adapted for magnetic entropy change by magnetocaloric effect, e.g. used as magnetic refrigerating material refrigeration systems using magnetic effects F25B21/00
• CPC Class Codes: H01F 41/16 the magnetic material being applied in the form of particles, e.g. by serigraphy , to form thick magnetic films or precursors therefor H01F41/18 -H01F41/24 take precedence
• CPC Class Codes: Y02B 30/00 Energy efficient heating, ventilation or air conditioning [HVAC]
• CPC Class Codes: Y10T 29/4902 Electromagnet, transformer or inductor
• CPC Class Codes: Y10T 29/49359 Cooling apparatus making, e.g., air conditioner, refrigerator

Abstract

The invention provides a method of making a magnetic regenerator for an active magnetic refrigerator, the method comprising: forming a magnetic regenerator from a slurry or a paste containing a magnetocaloric material the magnetic regenerator being formed to have plural paths therethrough for the flow of a heat transfer fluid; and varying the composition of the magnetocaloric material so that the magnetic transition temperature of the magnetic regenerator varies along the paths.

Claims

1. A method of making a magnetic regenerator for an active magnetic refrigerator, the method comprising:

forming a magnetic regenerator from a slurry or a paste containing magnetocaloric material, the magnetic regenerator being formed to have paths in the form of plural discrete channels therethrough for the flow of a heat transfer fluid; and

varying the composition of the magnetocaloric material and/or the slurry or paste so that the magnetic transition temperature of the magnetic regenerator varies along the channels.

2. A method according to claim 1, wherein the magnetocaloric material is selected from the group consisting of one or more of a metal, a metal oxide, a ceramic, or a combination thereof.

3. A method according to claim 2, wherein the magnetocaloric material is a ceramic, the method comprising:

forming mixtures of ceramic compositions having desired magnetocaloric properties;

processing the mixtures to generate component parts of the magnetic regenerator; and

,

arranging the component parts to form the magnetic regenerator.

4. A method according to claim 3, comprising:

varying the composition of the ceramic material to achieve a desired variation in the magnetic transition temperature of the magnetic regenerator along the channels.

5. A method according to claim 3, wherein forming mixtures of ceramic materials having desired magnetic properties comprises:

preparing slurries or pastes of powders having variable proportions of materials, wherein the proportions of materials used are selected such that the magnetic properties of the mixtures are as desired.

6. A method according to claim 3, wherein the step of processing the mixtures to generate component parts of the magnetic regenerator comprises:

tapecasting the mixtures to obtain layers of material having desired magnetic properties; and

,

sintering the layers to a desired density and form stability to obtain thin plates having a magnetic transition temperature which varies along the length of the plates.

7. A method according to claim 3, wherein the step of processing the mixtures to generate component parts of the magnetic regenerator comprises:

tapecasting the mixtures to obtain layers of material having desired magnetic properties;

forming strips of the tapecast material;

rolling the strips into tubes such that the magnetic transition temperature of the tube varies along the direction of the longitudinal axis of the tube; and

,

sintering the tubes to a desired density and form stability.

8. A method according to claim 3, wherein the step of processing the mixtures to generate component parts of the magnetic regenerator comprises:

extruding the mixtures to generate a substantially tubular member having a magnetic transition temperature that varies along the longitudinal axis of the tubular member; and

,

sintering the tubular member to a desired density and form stability.

9. A method according to claim 3, wherein the step of processing the mixtures to generate component parts of the magnetic regenerator comprises:

generating a block of material formed of layers each layer having a different magnetic transition temperature;

forcing plural longitudinal projections through the block thereby to form plural discrete channels in the material wherein the magnetic transition temperature varies along each of the channels; and

,

sintering the block to a desired density and form stability.

10. A method according to claim 3, wherein the step of processing the mixtures to generate component parts of the magnetic regenerator comprises:

generating a slab of material formed of strips each strip having a different magnetic transition temperature;

passing the slab through a calendar to form a thin plate; and

, sintering the plate to a desired high density and form stability.

11. A method according to claim 3, wherein the component parts of the magnetic regenerator are corrugated or patterned prior to sintering to increase their surface area.

12. A method according to claim 3, wherein mixtures are formed comprising the following compositions:

La_0.67Ca_0.33-xSr_xMnO₃, where x varies between 0 and 0.33, the magnetic transition temperature of a mixture being different for each value of x between 0 and 0.33.

13. A method according to claim 3, wherein mixtures are formed comprising the following compositions

(R,R′

,R″

)_1-x(A,A′

,A″

)_xMO<sub>3±

δ</sub>

,

in which

0.15≦

x≦

0.5 and 0≦

δ

≦

0.5;

R, R′

, R″

(which may be identical) are chosen from the group consisting of La, Pr, Y, Nd;

A, A′

, A′

(which may be identical) are chosen from the group Ca, Sr, Ba, Na, K; and

M is chosen from the group consisting of Mn, Cr, Co.

14. A method of making an active magnetic refrigerator, the method comprising:

providing a magnetic regenerator manufactured according to the method of claim 1;

providing a magnet for selectively applying and removing a magnetic field to the magnetic regenerator; and

providing a heat transfer fluid driver, for driving a heat transfer fluid back and forth through the magnetic regenerator in a synchronised manner as the magnetic field is applied and removed.

15. A method according to claim 1, wherein the channels are tubes of magnetocaloric material, or are longitudinal channels formed within a block of magnetocaloric material.

16. A method according to claim 3, wherein the channels are between plates of magnetocaloric material, the separation of the plates being from 0.1 mm to 5 mm.

17. A method according to claim 16, wherein the plates have a thickness from 0.1 mm to 5 mm.