Curable silicone impression materials with high tear strength and low consistency
First Claim
Patent Images
1. A curable material comprising:
- component (A) comprising at least two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule;
component (B) comprising organohydrogenpolysiloxane with at least three SiH groups per molecule;
component (D) comprising a catalyst for promoting the reaction between (A) and (B);
component (F) comprising filler; and
component (H) comprising at least one silane with at least two alkenyl groups per molecule,wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm.
1 Assignment
0 Petitions
Accused Products
Abstract
The invention relates to curable silicone compositions which contain silane based crosslinkers and a mixture of different organopolysiloxanes. The compositions are particularly suitable as curable impression materials in dental applications.
-
Citations
16 Claims
-
1. A curable material comprising:
-
component (A) comprising at least two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule; component (B) comprising organohydrogenpolysiloxane with at least three SiH groups per molecule; component (D) comprising a catalyst for promoting the reaction between (A) and (B); component (F) comprising filler; and component (H) comprising at least one silane with at least two alkenyl groups per molecule, wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9)
-
-
10. A curable material comprising:
-
component (A) comprising at least two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule, with the proviso that the component (A) siloxanes do not comprise aromatic groups; component (B) comprising organohydrogenpolysiloxane with at least three SiH groups per molecule; component (D) comprising a catalyst for promoting the reaction between (A) and (B); component (F) comprising filler; and component (H) comprising at least one silane with at least two alkenyl groups per molecule, wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm; and wherein, upon curing, the material has a Shore A hardness of no greater than about 70. - View Dependent Claims (11)
-
-
12. A curable material comprising:
-
component (A) comprising at least two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule; component (B) comprising organohydrogenpolysiloxane; component (D) comprising a catalyst for promoting the reaction between (A) and (B); component (F) comprising filler; and component (H) comprising at least one silane with at least two alkenyl groups per molecule wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm; wherein, upon curing, the material has an elongation at break value of 70 to 300%. - View Dependent Claims (13)
-
-
14. A curable material comprising:
-
component (A) consisting of two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule, with the proviso that the component (A) siloxanes do not comprise aromatic groups; component (B) comprising organohydrogenpolysiloxane with at least three SiH groups per molecule; component (D) comprising a catalyst for promoting the reaction between (A) and (B); component (F) comprising filler; and component (H) comprising at least one silane with at least two alkenyl groups per molecule;
wherein said at least one silane is selected from the group consisting of compounds that can be represented by the general formula (II)
Si(R1)n(R2)4-n
(II)wherein R1 is a linear, branched or cyclic monovalent ethylenically unsaturated substituent which can undergo an addition reaction with SiH-groups, having from 2 to 12 carbon atoms, R2 is a monovalent radical without groups that can undergo an addition reaction with SiH-groups and n is 2, 3 or 4, wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm. - View Dependent Claims (15, 16)
-
Specification