• US 8,162,202 B2
• Filed: 05/06/2011
• Issued: 04/24/2012
• Est. Priority Date: 06/03/2010
• Status: Active Grant

• Current Assignee: Rolls-Royce PLC (Rolls-Royce Holdings Plc)
• Original Assignee: Rolls-Royce PLC (Rolls-Royce Holdings Plc)
• Inventors: Milburn, Richard G.
• Primary Examiner(s): Ward, Jessica L
• Assistant Examiner(s): SAAD, ERIN BARRY
• Application Number:
  US13/102,483
• Publication Number:
  US 20110297734A1
• Time in Patent Office: 354 Days
• Field of Search: 228/227, 228/228, 228/233.1, 228/234.1, 228/235.1, 228/262.1, 228/127
• US Class Current: 228/234.1
• CPC Class Codes: B21D 26/021 Deforming sheet bodies
• CPC Class Codes: B21D 26/055 Blanks having super-plastic properties
• CPC Class Codes: B21D 26/059 Layered blanks
• CPC Class Codes: B21D 53/78 propeller blades; turbine blades
• CPC Class Codes: B23K 20/02 by means of a press ; Diffusion bonding B23K20/001, B23K20/04 take precedence
• CPC Class Codes: B23K 20/18 Zonal welding by interposing weld-preventing substances between zones not to be welded
• CPC Class Codes: B23K 2101/001 Turbines
• CPC Class Codes: B23P 15/04 turbine or like blades from several pieces

Abstract

In a method of manufacturing an article (28) by diffusion bonding and superplastic forming stop off material (122) is applied to prevent diffusion bonding in a predetermined pattern on a first surface (106) of a first metal workpiece (100) and the predetermined pattern is spaced from the edges of the first surface (106) of the first metal workpiece (100). Stop off material (124) to prevent diffusion bonding is applied in a predetermined position on the first surface (106) of the first metal workpiece (100) and the predetermined position extends from the predetermined pattern of stop of material (122) on the first surface (106) of the first metal workpiece (100) towards one edge of the first surface (106) of the first metal workpiece (100). A recess (130, 132) is provided in a second predetermined position on the second surface (108) of the first metal workpiece (100) or a fourth surface (112) of a second metal workpiece (102), the recess (130,132) extends towards the same edge of the first metal workpiece (100) or a corresponding edge of the second metal workpiece (102). The first and second metal workpieces (100, 102) are diffusion bonded together. During superplastic forming the recess (130, 132) and the stop off material (124) in the predetermined position define an inflation passage (148) for superplastic forming of the metal workpieces (100, 102) to a hollow article (28).

Claims

1. A method of manufacturing an article by diffusion bonding and superplastic forming comprising the steps of:

—

a) providing at least a first metal workpiece and a second metal workplace, the first metal workpiece having a first surface and a second surface, the second metal workpiece having a third surface and a forth surface,

b) applying stop off material to prevent diffusion bonding in a predetermined pattern on the first surface of the first metal workpiece, the predetermined pattern being spaced from the edges of the first surface of the first metal workplace,

c) applying stop off material to prevent diffusion bonding in a predetermined position on the first surface of the first metal workpiece or the third surface of the second metal workpiece, the predetermined position extending from the predetermined pattern of stop of material on the first surface of the first metal workpiece towards one edge of the first surface of the first metal workpiece,

d) providing a recess in a second predetermined position on the first surface of the first metal workpiece, the second surface of the first metal workpiece, the third surface of the second metal workpiece or the fourth surface of the second metal workpiece, the recess extending towards the same edge of the first metal workpiece or a corresponding edge of the second metal workpiece,

e) assembling at least the first metal workpiece and the second metal workpiece in a stack such that the first surface of the first metal workpiece faces the third surface of the second metal workpiece and the recess in the second predetermined position on the first surface of the first metal workplace, the second surface of the first metal workpiece, the third surface of the second metal workpiece or the fourth surface of the second metal workpiece is aligned with the stop off material arranged in the predetermined position on the first surface of the first metal workpiece,

f) sealing the edges of the first metal workpiece to the edges of the second metal workplace to form a sealed assembly,

g) evacuating the sealed assembly,

h) heating and externally pressurising the sealed assembly to diffusion bond the first and second metal workpieces together in areas other than the predetermined pattern and predetermined position to form a sealed integral structure,

i) connecting an inflation pipe to the stop off material in the first predetermined position on the first surface of the first metal workpiece of the sealed integral structure,

j) heating and internally pressurising the sealed integral structure to cause the first metal workpiece, or the second metal workpiece, where the stop off material was arranged in the predetermined position and the recess was arranged in the second predetermined position, to be hot formed to create an inflation passage within the sealed integral structure,

k) heating and internally pressurising the sealed integral structure to cause the first metal workpiece and/or the second metal workpiece where the stop off material was arranged in the predetermined pattern to be superplastically formed to create a hollow metal article.

3. A method as claimed in claim 1 wherein step d) comprises providing a first recess in a second predetermined position on the first surface of the first metal workpiece and a second recess in a third predetermined position on the third surface of the second metal workpiece, the first recess extending towards the same edge of the first metal workpiece and the second recess extending towards a corresponding edge of the second metal workpiece, step e) comprises assembling at least the first metal workpiece and the second metal workpiece in stack such that the first recess in the second predetermined position on the first surface of the first metal workpiece and the second recess in third surface of the second metal workpiece are aligned with the stop off material arranged in the predetermined position on the first surface of the first metal workpiece and step j) comprises heating and internally pressurising the sealed integral structure to cause the first metal workpiece and the second metal workpiece, where the stop off material was arranged in the predetermined position, the first recess was arranged in the second predetermined position and the second recess was arranged in the third predetermined position, to be hot formed to create an inflation passage within the sealed integral structure.

4. A method as claimed in claim 1 wherein step a) comprises providing a third metal workpiece, the third metal workpiece having a fifth surface and a sixth surface, step b) comprises applying stop off material to prevent diffusion bonding in a predetermined pattern on the third surface of the second metal workpiece, the predetermined pattern being spaced from the edges of the third surface of the second metal workpiece, step e) comprises assembling the first metal workpiece, the second metal workpiece and the third metal workpiece in a stack such that the first surface of the first metal workpiece faces the fifth surface of the third metal workpiece, the sixth surface of the third metal workpiece faces the third surface of the second metal workpiece and the recess in the second predetermined position on the first surface of the first metal workpiece, the second surface of the first metal workpiece, the third surface of the second metal workpiece or the fourth surface of the second metal workpiece is aligned with the stop off material arranged in the predetermined position on the first surface of the first metal workpiece.

5. A method as claimed in claim 1 wherein the article is selected from the group consisting of a fan blade and a fan outlet guide vane.

6. A method as claimed in claim 1 wherein the article is selected from the group consisting of a heat exchanger, a compressor blade and a compressor vane.

7. A method as claimed in claim 1 wherein the first metal workpiece, the second metal workpiece or the third metal workpiece comprises a titanium alloy.

8. A method as claimed in claim 7 wherein the titanium alloy consists of 6 wt % vanadium, 4 wt % aluminium and the balance titanium, minor elemental additions and incidental impurities.

9. A method as claimed in claim 1 wherein step d) comprises providing a recess in a second predetermined position on the first surface of the first metal workpiece, the recess extending towards the same edge of the first metal workpiece.

10. A method as claimed in claim 1 wherein step d) comprises providing a recess in a second predetermined position on the second surface of the first metal workpiece, the recess extending towards the same edge of the first metal workpiece.

11. A method as claimed in claim 1 wherein step h) comprises heating to a temperature greater than 850°

C. and applying a pressure greater than 20.26×

10⁵ Nm<sup>−

2</sup>.

12. A method as claimed in claim 11 wherein step h) comprises heating to a temperature between 900°

C. and 950°

C. and applying a pressure between 20.26×

10⁵ Nm<sup>−

2</sup> and 30.39×

10⁵ Nm<sup>−

2</sup>.

13. A method as claimed in claim 1 wherein step j) and step k) comprise heating to a temperature greater than 850°

C.

14. A method as claimed in claim 13 wherein step j) and step k) comprise heating to a temperature between 900°

C. and 950°

C.

2. A method as claimed in claim wherein step d) comprises providing a first recess in a second predetermined position on the second surface of the first metal workpiece and a second recess in a third predetermined position on the fourth surface of the second metal workpiece, the first recess extending towards the same edge of the first metal workpiece and the second recess extending towards a corresponding edge of the second metal workpiece, step e) comprises assembling at least the first metal workpiece and the second metal workpiece in stack such that the first recess in the second predetermined position on the second surface of the first metal workpiece and the second recess in fourth surface of the second metal workpiece are aligned with the stop off material arranged in the predetermined position on the first surface of the first metal workpiece and step j) comprises heating and internally pressurising the sealed integral structure to cause the first metal workpiece and the second metal workpiece, where the stop off material was arranged in the predetermined position, the first recess was arranged in the second predetermined position and the second recess was arranged in the third predetermined position, to be hot formed to create an inflation passage within the sealed integral structure.