Method for making silicone hydrogel contact lenses

• US 8,163,206 B2
• Filed: 06/16/2009
• Issued: 04/24/2012
• Est. Priority Date: 12/18/2008
• Status: Active Grant

• Current Assignee: Alcon Incorporated
• Original Assignee: Novartis Ag
• Inventors: Chang, Frank, Vogt, Jürgen, Pruitt, John Dallas, Qian, Xinming, Smith, Dawn A., Domschke, Angelika Maria, Holland, Troy Vernon, Turek, Richard Charles, Wu, Daqing
• Primary Examiner(s): Gupta, Yogendra
• Assistant Examiner(s): Abraham, Amjad
• Application Number:
  US12/456,364
• Publication Number:
  US 20100258961A1
• Time in Patent Office: 1,043 Days
• Field of Search: 264/1.38
• US Class Current: 264/1.38
• CPC Class Codes: C08F 283/124 on to polysiloxanes having carbon-to-carbon double bonds
• CPC Class Codes: C08L 51/085 on to polysiloxanes
• CPC Class Codes: C08L 83/04 Polysiloxanes
• CPC Class Codes: G02B 1/043 Contact lenses

Abstract

The invention provide a method for making silicone hydrogel based on the Lightstream Technology from a monomer mixture with a curing time of less than about 100 seconds. The present invention is also related to silicone hydrogel contact lenses made according to methods of the invention.

Claims

1. A method for producing silicone hydrogel contact lenses, comprising the steps of:

providing a mold for making a soft contact lens, wherein the mold has a first mold half with a first molding surface defining the anterior surface of a contact lens and a second mold half with a second molding surface defining the posterior surface of the contact lens, wherein said first and second mold halves are configured to receive each other such that a cavity is formed between said first and second molding surfaces;

introduce a monomer mixture of lens-forming materials into the cavity, wherein the monomer mixture comprises (1) from about 10% to about 50% by weight of a hydrophilic amide-type vinylic monomer, (2) from about 10% to about 40% by weight of a siloxane-containing (meth)acrylamide monomer, (3) from about 10% to about 40% by weight of a polysiloxane-containing vinylic macromer, (4) from about 0.1% to 1.3% by weight of a photoinitiator, and (5) from 0 to 5% by weight of a polymerizable UV-absorbing agent or a polymerizable latent UV-absorbing agent, wherein if one or more methacrylate monomers are present in the monomer mixture, the total amount of the methacrylate monomers is less than about 5% by weight and the monomer mixture is characterized by having a curing time of less than 100 seconds by a UV light having an UV-intensity of about 4.1 mW/cm2; and

irradiating, under a spatial limitation of actinic radiation, the monomer mixture in the mold for a time period of about 80 seconds or less, so as to crosslink the monomer

mixture to form the silicone hydrogel contact lens, wherein the produced contact lens comprises an anterior surface defined by the first molding surface, an opposite posterior surface defined by the second molding surface, and a lens edge defined by the spatial limitation of actinic radiation.

2. The method of claim 1, wherein the siloxane-containing (meth)acrylamide monomer is represented by formula (1)

3. The method of claim 2, wherein the polysiloxane-containing vinylic macromer is represented by formula (4)

Q-X₁-G₁-PDMS-G₂X₂-Q)_r 

 

(4)

in which

r is an integer of 0 or 1;

G₁ and G₂ independent of each other is a linear or branched C₁-C₁₀ alkylene divalent radical, a divalent radical of alk'"'"'-O_q alk- in which q is an integer of from 1 to 5 and alk and alk′

independent of each other is a C₁-C₆ alkylene divalent radical, or a divalent radical of —

R′

₁—

X₄-E-X₅—

R′

₂—

in which R′

₁ and R′

₂ independent of each other is a linear or branched C₁-C₁₀ alkylene divalent radical or a divalent radical of alk′

-O_q alk- as defined above, X₄ and X₅ independent of each other are a linkage selected from the group consisting of

4. The method of claim 2, wherein the hydrophilic amide-type vinylic monomer is selected from the group consisting of 2-acrylamidoglycolic acid, 2-acrylamido-2-methyl-1-propanesulfonic acid, 2-acrylamido-2-methyl-1-propanesulfonic acid or salt thereof, (3-acrylamidopropyl)trimethylammonium chloride, 3-acryloylamino-1-propanol, N-(butoxymethyl)acrylamide, N-tert-butylacrylamide, diacetone acrylamide, N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, N-[3-(dimethylamino)propyl]methacrylamide, N-hydroxyethyl acrylamide, N-(hydroxymethyl)acrylamide, N-(isobutoxymethyl)acrylamide, N-isopropylacrylamide, N-isopropylmethacrylamide, methacrylamide, N-phenylacrylamide, N-[Tris(hydroxymethyl)methyl]acrylamide, N-methyl-3-methylene-2-pyrrolidone, and a mixture thereof.

5. The method of claim 3, wherein the siloxane-containing (meth)acrylamide monomer is selected from the group consisting of N-[tris(trimethylsiloxy)silylpropyl]methacrylamide, N-[tris(trimethylsiloxy)-silylpropyl]acrylamide, N-[tris(dimethylpropylsiloxy)silylpropyl]acrylamide, N-[tris(dimethylpropylsiloxy)silylpropyl]methacrylamide, N-[tris(dimethyl-phenylsiloxy)silylpropyl]acrylamide, N-[tris(dimethylphenylsiloxy)silylpropyl]methacrylamide, N-[tris(dimethylethylsiloxy) silylpropyl]acrylamide, N-[tris(dimethylethylsiloxy)silylpropyl] methacrylamide, N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsily)ppropyloxy)propyl)-2- methyl acrylamide;

N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl) acrylamide;

N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N, N-bis[2-hydroxy-3-(3(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl] acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)acrylamide;

N, N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]acrylamide;

N-[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N42-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide;

N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N, N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide.

6. The method of claim 3, wherein the polysiloxane-containing vinylic macromer is represented by formula (4) in which D₁, D₂ and D₃ independently of each other are a divalent radical of formula (6).

7. The method of claim 3, wherein the monomer mixture comprises a polymerizable UV-absorbing agent or a polymerizable latent UV-absorbing agent in an amount from about 0.2% to about 5.0% by weight.

8. The method of claim 7, wherein the monomer mixture comprises a polymerizable UV-absorbing agent which comprises a benzotriazole- and/or benzophenone-moiety.

9. The method of claim 8, wherein the photoinitiator is a benzoylphosphine oxide photoinitiator.

10. The method of claim 7, wherein the monomer mixture comprises a polymerizable latent UV-absorbing agent.

11. The method of claim 3, wherein at least one of the first and second molding surfaces is permeable to UV radiation and optionally the other molding surface is poorly permeable to UV radiation.

12. The method of claim 11, wherein the mold is a reusable mold comprising a mask which is fixed, constructed or arranged in, at or on the mold half having the radiation-permeable molding surface, wherein the mask is UV-impermeable or at least of poor UV-permeability compared with the UV-permeable molding surface, wherein the mask extends inwardly right up to the mold cavity and surrounds the mold cavity so as to screen all areas behind the mask with the exception of the mold cavity.

13. The method of claim 12, wherein the monomer mixture in the mold is irradiated under the spatial limitation of actinic radiation for a time period of about 50 seconds or less.

14. The method of claim 2, wherein the monomer mixture comprises (1) from about 15% to about 45% by weight of the hydrophilic amide-type vinylic monomer;

(2) from about 15% to about 30% by weight of the siloxane-containing acrylate or acrylamide or methacrylamide monomer;

(3) from about 15% to about 35% by weight of the polysiloxane-containing vinylic macromer;

(4) from about 0.1% to 1.3% by weight of a photoinitiator; and

(5) from 0 to 5% by weight of a polymerizable UV-absorbing agent or a polymerizable latent UV-absorbing agent, provided that components (1) to (5) and any additional components add up to 100% by weight.

16. The method of claim 5, wherein the hydrophilic amide-type vinylic monomer is selected from the group consisting of 2-acrylamidoglycolic acid, 2-acrylamido-2-methyl-1-propanesulfonic acid, 2-acrylamido-2-methyl-1-propanesulfonic acid or salt thereof, (3-acrylamidopropyl)trimethylammonium chloride, 3-acryloylamino-1-propanol, N-(butoxymethyl)acrylamide, N-tert-butylacrylamide, diacetone acrylamide, N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, N-[3-(dimethylamino)propyl]methacrylamide, N-hydroxyethyl acrylamide, N-(hydroxymethyl)acrylamide, N-(isobutoxymethyl)acrylamide, N-isopropylacrylamide, N-isopropylmethacrylamide, methacrylamide, N-phenylacrylamide, N-[Tris(hydroxymethyl)methyl]acrylamide, N-methyl-3-methylene-2-pyrrolidone, and a mixture thereof.

17. The method of claim 6, wherein the polysiloxane-containing vinylic macromer is represented by formula (4) in which D₁, D₂ and D₃ independently of each other are a divalent radical of formula (6) and r, ν

and ω

are an integer of 1, wherein the hydrophilic amide-type vinylic monomer is selected from the group consisting of 2-acrylamidoglycolic acid, (3-acrylamidopropyl) trimethylammonium chloride, 3-acryloylamino-1-propanol, N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, N-hydroxyethyl acrylamide, N-(hydroxymethyl) acrylamide, N-[Tris(hydroxymethyl)methyl]acrylamide, N-methyl-3-methylene-2-pyrrolidone, and a mixture thereof, wherein the siloxane-containing (meth)acrylamide monomer is selected from the group consisting of N-[tris(trimethylsiloxy)silylpropyl]methacrylamide, N-[tris(trimethylsiloxy)-silylpropyl]acrylamide, N[tris(dimethylpropylsiloxy)silylpropyl]acrylamide, N-[tris(dimethylpropylsiloxy)-silylpropyl]methacrylamide, N-[tris(dimethylethylsiloxy) silylpropyl]acrylamide, N-[tris(dimethylethylsiloxy)silylpropyl]methacrylamide, N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl) acrylamide;

N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy) propyl]acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl) acrylamide;

N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]acrylamide;

N[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide;

N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide, and mixture thereof.

18. The method of claim 17, wherein the hydrophilic amide-type vinylic monomer is selected from the group consisting of N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, N-hydroxyethyl acrylamide, N-(hydroxymethyl)acrylamide, and mixture thereof, wherein the siloxane-containing (meth)acrylamide monomer is selected from the group consisting of N-[tris(trimethylsiloxy)silylpropyl]methacrylamide, N-[tris(trimethylsiloxy)-silylpropyl]acrylamide, N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)acrylamide, and mixture thereof.

19. The method of claim 18, wherein the monomer mixture comprises a polymerizable UV-absorbing agent which comprises a benzotriazole- and/or benzophenone-moiety.

20. The method of claim 14, wherein the polysiloxane-containing vinylic macromer is represented by formula (4) in which D₁, D₂ and D₃ independently of each other are a divalent radical of formula (6) and r, ν

and ω

are an integer of 1, wherein the hydrophilic amide-type vinylic monomer is selected from the group consisting of 2-acrylamidoglycolic acid, (3-acrylamidopropyl) trimethylammonium chloride, 3-acryloylamino-1-propanol, N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, N-hydroxyethyl acrylamide, N-(hydroxymethyl)acrylamide, N-[Tris(hydroxymethyl)methyl]acrylamide, N-methyl-3-methylene-2-pyrrolidone, and a mixture thereof, wherein the siloxane-containing (meth)acrylamide monomer is selected from the group consisting of N-[tris(trimethylsiloxy)silylpropyl]methacrylamide, N-[tris(trimethylsiloxy)-silylpropyl]acrylamide, N4tris(dimethylpropylsiloxy)silylpropyl]acrylamide, N-[tris(dimethylpropylsiloxy)silylpropyl]methacrylamide, N-[tris(dimethylethylsiloxy) silylpropyl]acrylamide, N-[tris(dimethylethylsiloxy)silylpropyl]methacrylamide, N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl) acrylamide;

N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy) propyl] acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl) acrylamide;

N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]acrylamide;

N[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide;

N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide.

15. A method for producing silicone hydrogel contact lenses, comprising the steps of:

providing a mold for making a soft contact lens, wherein the mold has a first mold half with a first molding surface defining the anterior surface of a contact lens and a second mold half with a second molding surface defining the posterior surface of the contact lens, wherein said first and second mold halves are configured to receive each other such that a cavity is formed between said first and second molding surfaces;

introduce a monomer mixture of lens-forming materials into the cavity, wherein the monomer mixture comprises (1) from about 10% to about 50% by weight of a hydrophilic amide-type vinylic monomer, (2) from about 10% to about 40% by weight of a siloxane-containing acrylate, (3) from about 10% to about 40% by weight of a polysiloxane-containing vinylic macromer, (4) from about 0.1% to 1.3% by weight, more preferably from about 0.5% to about 1.1% by weight, of a photoinitiator, and (5) from 0 to 5% by weight of a polymerizable UV-absorbing agent or a polymerizable latent UV-absorbing agent, wherein if one or more methacrylate monomers are present in the monomer mixture˜

the total amount of the methacrylate monomers is less than about 5% by weight and the monomer mixture is characterized by haying a curing time of less than about 100 seconds by a UV light having an UV-intensity of about 4.1 mW/cm2 within a time period of less than about 100 seconds; and

irradiating, under a spatial limitation of actinic radiation, the monomer mixture in the mold for a time period of about 80 seconds or less, so as to crosslink the monomer mixture to form the silicone hydrogel contact lens, wherein the produced contact lens comprises an anterior surface defined by the first molding surface, an opposite posterior surface defined by the second molding surface, and a lens edge defined by the spatial limitation of actinic radiation.