Method of forming a stent pattern on a tube

• US 8,241,554 B1
• Filed: 06/29/2004
• Issued: 08/14/2012
• Est. Priority Date: 06/29/2004
• Status: Expired due to Fees

• Current Assignee: Advanced Cardiovascular Systems Incorporated
• Original Assignee: Advanced Cardiovascular Systems Incorporated
• Inventors: Abbate, Anthony J., Gale, David C., Kleine, Klaus, Atladottir, Svava Maria
• Primary Examiner(s): Thrower, Larry
• Application Number:
  US10/881,554
• Time in Patent Office: 2,968 Days
• Field of Search: 148/593, 623/1.15, 264/573
• US Class Current: 264/573
• CPC Class Codes: A61F 2/915 with bands having a meander structure, adjacent bands being connected to each other
• CPC Class Codes: A61F 2230/0054 V-shaped
• CPC Class Codes: A61F 2240/001 Designing or manufacturing processes
• CPC Class Codes: A61F 2250/0048 differing in mechanical expandability, e.g. in mechanical, self- or balloon expandability
• CPC Class Codes: B29L 2023/007 Medical tubes other than catheters catheters B29L2031/7542

Abstract

Methods of fabricating an implantable medical device from a tube or a sheet in an expanded or stretched state, respectively, are disclosed herein. The implantable medical device may be an endoprosthesis such as a stent. In one embodiment, the method may include radially expanding a tube about a cylindrical axis of the tube from a first diameter to a second diameter. The method may further include forming a pattern on at least a portion of the expanded tube. Additional embodiments may include forming a stent pattern on a stretched sheet from which a stent may be formed. In addition, a stent pattern may be formed on a tube that is formed from a stretched sheet.

Claims

1. A method for fabricating a medical device including a stent crimped to a balloon, the stent having a first diameter when crimped to the balloon, comprising the following sequential steps:

providing a cutting tool for forming a pattern in a polymer tube, the pattern being characterized by struts and a cut-out region separating the struts, the cut-out region being characterized by a circumferential length and longitudinal length, wherein the pattern is such that when formed in the tube and the tube is crimped from a second diameter to the first diameter a non-uniform decrease of the cut-out region occurs, whereby a non-uniform decrease is such that the circumferential length decreases by a lesser or greater degree than the longitudinal length relative to their respective lengths before crimping from the second diameter to the first diameter;

forming the tube including radially expanding the tube to the second diameter;

forming the pattern in the tube when the tube has the second diameter, followed by heat shrinking the tube to a third diameter, less than the second diameter, wherein the cut-out region decreases more uniformly when the heat shrunk tube is crimped from the third diameter to the first diameter than if the tube was crimped from the second diameter to the first diameter; and

crimping the heat-shrunk tube from the third diameter to the first diameter, thereby fabricating the medical device.

2. The method of claim 1, wherein the tube comprises a polymer, and wherein the temperature of the tube during expansion and forming is less than a melting temperature of the polymer.

3. The method of claim 1, wherein the temperature of the tube during an expansion to the second diameter is equal to or greater than a glass transition temperature of the polymer.

4. The method of claim 1, wherein the second diameter is less than or equal to a deployment diameter.