Frangible bullet and its manufacturing method

• US 8,365,672 B2
• Filed: 03/25/2010
• Issued: 02/05/2013
• Est. Priority Date: 03/25/2009
• Status: Expired due to Fees

• Current Assignee: Aleaciones de Metales Sinterizados, S.A. (Ames Tamarite SA)
• Original Assignee: Aleaciones de Metales Sinterizados, S.A. (Ames Tamarite SA)
• Inventors: Calero Martinez, Jose Antonio, Ribas, Joan Morato, Grillot, Luis Allut
• Primary Examiner(s): BERGIN, JAMES S
• Application Number:
  US12/731,704
• Publication Number:
  US 20100242778A1
• Time in Patent Office: 1,048 Days
• Field of Search: 102/501, 102/506, 102/517, 86/54, 86/55, 86/57
• US Class Current: 102/517
• CPC Class Codes: F42B 12/74 of the core or solid body

Abstract

This invention describes a frangible bullet made from particles of a copper-based metal powder with the aid of an organic lubricant, which have been pressed so that the pressed particles have a density of more than 6.9 g/cm³, where the composition has been treated with thermal oxidation.

Claims

1. A method for producing a frangible bullet, comprising:

providing a copper-based metal powder with a particle size distribution of more than 120 micrometers;

pressing the particles of the powder with the aid of an organic lubricant up to a density of more than 6.9 g/cm³, wherein the organic lubricant is a polymer selected from the group comprising polyethylenes, polyamides or polyvinyl alcohols, thereby favoring the cold welding of the particles; and

subjecting the pressed particles to an oxidative heat treatment thereby allowing physical bonds between polymer chains in the organic lubricant and oxygen as well as the growth of an oxidised layer on the pressed particles.

2. A method for producing a frangible bullet according to claim 1, wherein the heat treatment is performed at a temperature of less than 400°

C.

3. A method for producing a frangible bullet according to claim 1, wherein the heat treatment is performed in the presence of air.

4. A method for producing a frangible bullet according to claim 1, wherein during pressing up to 1% by weight of the organic lubricant is used with respect to the metal powder.

5. A method for producing a frangible bullet according to claim 1, wherein the copper-based powder is bronze or brass.

6. A method for producing a frangible bullet according to claim 1, wherein the pressed particles have a density of about 7.2 g/cm³ to about 7.5 g/cm³.

7. A method for producing a frangible bullet according to claim 1, wherein the organic lubricant is high-density polyethylene.

8. A method for producing a frangible bullet according to claim 1, wherein the copper-based powder consists in particles of a homogeneous pre-alloy of copper, tin and zinc, with a content of less than 41% by weight of Zn and/or less than 12% by weight of Sn.