Diffusion-hardened medical implant
First Claim
1. A method of making a surface hardened medical implant comprising the steps of:
- forming a medical implant of zirconium or zirconium alloy;
oxidizing or nitriding said implant at a temperature of from 500 degrees C. to 700 degrees C. to retain at least 0.1 microns of said oxide or nitride layer, to form at least 0.005 microns metallic hardened layer on top of said at least 0.1 microns thick oxide or nitride layer, and to form a diffusion zone having a thickness of at least 2 microns below said at least 0.1 microns thick oxide or nitride layer; and
wherein said treating step is performed for a period of time determined based at least on a desired thickness of the diffusion zone to be formed.
1 Assignment
0 Petitions
Accused Products
Abstract
Methods of making surface hardened medical implants comprising providing a biocompatible alloy with a surface comprising an oxide or nitride layer, diffusing at least a portion of the respective oxygen or nitrogen from the oxide or nitride layer the substrate for a period of time to form a diffusion hardened zone of desired thickness. The period of time is based at least on (1) the diffusivity of a diffusing specie in the oxide or nitride layer, (2) a desired hardness profile of at least a portion of said implant defined by a function selected from the group consisting of: an error function, an exponential function, a near uniform distribution function, and any sequential combination thereof, or (3) a desired thickness of said oxide or nitride layer to be retained.
-
Citations
12 Claims
-
1. A method of making a surface hardened medical implant comprising the steps of:
-
forming a medical implant of zirconium or zirconium alloy; oxidizing or nitriding said implant at a temperature of from 500 degrees C. to 700 degrees C. to retain at least 0.1 microns of said oxide or nitride layer, to form at least 0.005 microns metallic hardened layer on top of said at least 0.1 microns thick oxide or nitride layer, and to form a diffusion zone having a thickness of at least 2 microns below said at least 0.1 microns thick oxide or nitride layer; and
wherein said treating step is performed for a period of time determined based at least on a desired thickness of the diffusion zone to be formed. - View Dependent Claims (2, 3, 4, 5, 6)
-
-
7. A method of making a surface hardened medical implant comprising the steps of:
-
forming a medical implant of zirconium or zirconium alloy;
oxidizing or nitriding said implant at a temperature of from 500 degrees C. to 700 degrees C. to form an oxide or nitride layer having a thickness of at least 2 microns;treating said implant under vacuum or inert gas at a temperature less than 700 degrees C. to retain at least 0.1 microns of said oxide or nitride layer, to form at least 0.005 microns metallic hardened layer on top of said at least 0.1 microns thick oxide or nitride layer, and to form a diffusion zone having a thickness of at least 2 microns below said at least 0.1 microns thick oxide or nitride layer; and polishing the metallic hardened layer with mechanical, chemical, or electromechanical devices or substances; wherein said treating step is performed for a period of time determined based at least on a desired thickness of said oxide or nitride layer to be retained. - View Dependent Claims (8, 9, 10, 11, 12)
-
Specification