Cross-linkable compositions

• US 8,710,120 B2
• Filed: 09/29/2010
• Issued: 04/29/2014
• Est. Priority Date: 10/08/2009
• Status: Active Grant

• Current Assignee: Wacker Chemie AG (Dr. Alexander Wacker Familiengesellschaft Mit Beschrã¤Nkter Haftung)
• Original Assignee: Wacker Chemie AG (Dr. Alexander Wacker Familiengesellschaft Mit Beschrã¤Nkter Haftung)
• Inventors: Prasse, Marko
• Primary Examiner(s): NERANGIS, VICKEY M
• Application Number:
  US13/500,202
• Publication Number:
  US 20120202919A1
• Time in Patent Office: 1,308 Days
• Field of Search: 523/200, 524/425, 524/588
• US Class Current: 523/200
• CPC Class Codes: C08K 3/26 Carbonates; Bicarbonates
• CPC Class Codes: C08K 9/04 Ingredients treated with organic substances treated with macromolecular compounds C08K9/08
• CPC Class Codes: C08L 83/04 Polysiloxanes

Abstract

Crosslinkable compositions contain a calcium carbonate-rich filler coated with a carboxylic acid of the formula
R⁴—(OCR³₂—C(═O)OH)_y.

The compositions exhibit low modulus, good adhesion to substrates, and low skin formation time.

Claims

1. A crosslinkable composition comprising

(A) at least one crosslinkable compound selected from the group consisting of compounds (A1) of formula

A-[(CR¹₂)_b—

SiR_a(OR²)_3-a]_x 

 

(II)

where

A is an x-valent polymer radical bonded via nitrogen, phosphorus, oxygen, sulfur, carbon or a carbonyl group,

R are identical or different and are monovalent, optionally substituted hydrocarbyl radicals,

R¹ are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbyl radical which may be attached to the carbon atom via nitrogen, phosphorus, oxygen, sulfur or a carbonyl group,

R² are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbyl radical,

x is an integer from 1 to 10,

a is 0, 1 or 2 and

b is an integer from 1 to 10

with the proviso that at least two OR² groups per molecule are present, and

compounds (A2) of the formula

R⁵_cZ_dSiO_(4-c-d)/2 

 

(III)

where

R⁵ are identical or different and each is an optionally substituted hydrocarbyl radical which may be interrupted by oxygen atoms,

Z are identical or different and are a hydroxyl radical or hydrolyzable radical,

c is 0, 1, 2 or 3 and

d is 0, 1, 2 or 3

with the proviso that the sum of c+d is less than or equal to 4 and at least two Z radicals are present per molecule; and

(B) a calcium carbonate-containing filler (B0) surface-treated with carboxylic acids (C) of the formula

R⁴—

(OCR³₂—

C(═

O)OH)_y 

 

(I)

where

R³ are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbyl radical,

R⁴ is a y-valent, carbon-bonded, optionally substituted hydrocarbyl radical which may be interrupted by oxygen atoms, and

y is an integer from 1 to 3.

2. The crosslinkable composition of claim 1, wherein the calcium carbonate-containing fillers comprise ground natural limestone with a calcium carbonate content of more than 85% by weight, natural marble with a calcium carbonate content of more than 85% by weight and precipitated calcium carbonate with a calcium carbonate content of more than 95% by weight.

3. The crosslinkable composition of claim 2, wherein the carboxylic acids (C) are one or more of 3,6-dioxaheptanoic acid, 3,6,9-trioxadecanoic acid, 3,6-dioxaoctanedioic acid, 3,6,9-trioxaundecanedioic acid, poly(ethylene glycol) diacid with a molar mass of approx. 600 g/mol, glycolic acid ethoxylate 4-tert-butylphenyl ether with a mean molar mass of approximately 380 g/mol and glycolic acid ethoxylate lauryl ether with a mean molar mass of approximately 360 g/mol or approximately 460 g/mol.

4. The crosslinkable composition of claim 1, wherein the carboxylic acids (C) are one or more of 3,6-dioxaheptanoic acid, 3,6,9-trioxadecanoic acid, 3,6-dioxaoctanedioic acid, 3,6,9-trioxaundecanedioic acid, poly(ethylene glycol) diacid with a molar mass of approx. 600 g/mol, glycolic acid ethoxylate 4-tert-butylphenyl ether with a mean molar mass of approximately 380 g/mol and glycolic acid ethoxylate lauryl ether with a mean molar mass of approximately 360 g/mol or approximately 460 g/mol.

5. The crosslinkable composition of claim 1, wherein the composition contains component (B) in amounts of 5 to 300 parts by weight, based on 100 parts by weight of component (A).

6. The crosslinkable composition of claim 1, comprising

(A) at least one crosslinkable compound,

(B) calcium carbonate-containing fillers surface-treated with carboxylic acids (C) of the formula (I),

(D) optionally a catalyst,

(E) optionally a crosslinker,

(F) optionally a plasticizer,

(G) optionally filler(s),

(H) optionally adhesion promoter(s),

(I) optionally a additives, and

(L) further optionally organic solvent.

7. A process for producing a crosslinkable composition of claim 6, comprising mixing filler (B) containing surface-treated calcium carbonate with constituents (A) and optionally (D) to (L) in any sequence.

8. A process for producing a crosslinkable composition of claim 6, wherein untreated calcium carbonate-containing filler is mixed with carboxylic acid (C) and the other constituents (A) and optionally (D) to (L) in any sequence, such that filler is coated with component (C) in situ.

9. A shaped body produced by crosslinking a crosslinkable composition of claim 6.

10. A shaped body produced by crosslinking a crosslinkable composition of claim 1.