Multistage polymer dispersions, processes for preparing them, and use thereof

• US 8,754,151 B2
• Filed: 12/21/2011
• Issued: 06/17/2014
• Est. Priority Date: 12/21/2010
• Status: Expired due to Fees

• Current Assignee: BASF SE
• Original Assignee: BASF SE
• Inventors: Roller, Sebastian, Jahns, Ekkehard, Denu, Hans-Juergen
• Primary Examiner(s): BERNSHTEYN, MICHAEL
• Application Number:
  US13/333,231
• Publication Number:
  US 20120157577A1
• Time in Patent Office: 909 Days
• Field of Search: 524/5, 524/547, 524/817, 524/806, 524/460, 524/543, 524/458, 526/80, 526/87, 526/287, 526/288, 526/307.6, 526/317.1, 526/318.2, 526/286
• US Class Current: 524/5
• CPC Class Codes: C09D 141/00 Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a bond to sulfur or by a heterocyclic ring containing sulfur; Coating compositions based on derivatives of such polymers

Abstract

The present invention relates to aqueous multistage polymer dispersions obtainable by free-radically initiated aqueous emulsion polymerization, having a soft phase and a hard phase, and a hard-to-soft stage ratio of 25% to 95% by weight to 75% to 5% by weight, the glass transition temperature (Tg) of the soft phase, as first stage, being −30 to 0° C. and that of the hard phase, as second stage, being 20 to 60° C., comprising at least one monomer of the general formula I

in which the variables have the following definitions:

• • n=0 to 2,
  • R1, R2, R3=independently of one another hydrogen or methyl group,
  • X=O or NH,
  • Y=H, alkali metal or NH₄,
    to processes for preparing these aqueous polymer dispersions, and to the use thereof as binders in coatings, and also to coatings comprising the polymer dispersion of the invention.

Claims

1. An aqueous multistage polymer dispersion, comprising:

a soft phase having a glass transition temperature ranging from −

30°

C. to 0°

C.; and

a hard phase having a glass transition temperature ranging from 20°

C. to 60°

C.,

said soft phase and said hard phase each comprising at least one monomer of formula (I);

2. The aqueous polymer dispersion according to claim 1, wherein the monomer of formula (I) is at least one selected from the group consisting of 2-acrylamido-2-methylpropanesulfonic acid (AMPS), methacrylic acid 3′

-sulfopropyl ester, acrylic acid 3′

-sulfopropyl ester, and methacrylic acid 2′

-sulfoethyl ester.

3. The aqueous polymerization dispersion according to claim 1 or 2, wherein the soft phase, has a glass transition temperature ranging from −

20 to 0°

C., and the hard phase has a glass transition temperature ranging from 30 to 50°

C.

4. The aqueous polymer dispersion according to any one of claim 1 or 2, wherein a polymer of the soft phase is a soft-phase copolymer satisfying the following conditions:

(i) an amount of the soft-phase copolymer ranges from 5% to 50% by weight, based on 100 parts by weight of the total monomers polymerized in the soft phase and the hard phase;

(ii) the soft-phase copolymer comprises, to an extent of at least 80% and up to 99% by weight, at least one principal monomer selected from the group consisting of acrylamide, methacrylamide, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl (meth)acrylate or 1,4-butanediol monoacrylate, and mixtures of these monomers

(iii) the soft-phase copolymer comprises, to an extent of at least 0.1% and up to 5% by weight, of the at least one monomer of formula (I).

5. The aqueous polymer dispersion according to any one of claims 1 or 2, wherein the soft phase and the hard phase further comprise a silane monomer.

6. The aqueous polymer dispersion according to claim 5, wherein the silane monomer is a vinyltrialkoxysilane or a (meth)acryloyloxyalkyltrialkoxysilane.

7. The aqueous polymer dispersion according to claim 6, wherein an amount of the silane monomer is up to 2% by weight, based on a total weight of monomers in the soft phase and the hard phase.

8. A process for preparing the aqueous multistage polymer dispersion according to claim 1, the process comprising independently polymerizing the soft phase and the hard phase by free-radically initiated aqueous emulsion polymerization.

9. A coating composition, comprising the aqueous multistage polymer dispersion according to any one of claims 1 or 2.

10. A binder, comprising the aqueous multistage polymer dispersion according to any one of claims 1 or 2.

11. An additive suitable for mineral or non-mineral substances, the additive comprising the aqueous multistage polymer dispersion according to any one of claims 1 or 2.

12. A mineral molding, comprising a coating comprising the aqueous multistage polymer dispersion according to any one of claims 1 or 2.

13. A fiber cement sheet, comprising a coating comprising the aqueous multistage polymer dispersion according to any one of claims 1 or 2.

14. The aqueous polymer dispersion according to claim 1, wherein a polymer of the soft phase is a soft-phase copolymer satisfying the following conditions:

(i) an amount of the soft-phase copolymer ranges from 5% to 50% by weight, based on 100 parts by weight of the total monomers polymerized in the soft phase and the hard phase;

(ii) the soft-phase copolymer comprises, to an extent of at least 80% and up to 99% by weight, at least one principal monomer selected from the group consisting of acrylamide, methacrylamide, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl (meth)acrylate, and 1,4-butanediol monoacrylate, n-butyl acrylate, and methyl methacrylate;

(iii) the soft-phase copolymer comprises, to an extent of at least 0.1% and up to 5% by weight, of the at least one selected from the group consisting of 2-acrylamido-2-methylpropanesulfonic acid (AMPS), methacrylic acid 3′

-sulfopropyl ester, acrylic acid 3′

-sulfopropyl ester, and methacrylic acid 2′

-sulfoethyl ester.

15. The aqueous polymer dispersion according to claim 1, wherein a polymer of the soft phase is a soft-phase copolymer satisfying the following conditions:

(i) an amount of the soft-phase copolymer ranges from 5% to 50% by weight, based on 100 parts by weight of the total monomers polymerized in the soft phase and the hard phase;

(ii) the soft-phase copolymer comprises, to an extent of at least 80% and up to 99% by weight, at least one principal monomer selected from the group consisting of n-butyl acrylate, methyl methacrylate, and acrylamide;

(iii) the soft-phase copolymer comprises, to an extent of at least 0.1% and up to 5% by weight, of the at least one selected from the group consisting of 2-acrylamido-2-methylpropanesulfonic acid (AMPS), methacrylic acid 3′

-sulfopropyl ester, acrylic acid 3′

-sulfopropyl ester, and methacrylic acid 2′

-sulfoethyl ester.

16. The aqueous polymer dispersion according to claim 5, wherein the silane monomer is a vinyltrialkoxysilane selected from the group consisting of vinyltrimethoxysilane, alkylvinyldialkoxysilanes, and methylvinyldialkoxysilane, or a (meth)acryloyloxyalkyltrialkoxysilane selected from the group consisting of (meth)acryloyloxypropyltrimethoxysilane and (meth)acryloyloxypropyltriethoxysilane.