Electric wire or cable
First Claim
Patent Images
1. A method for producing an aluminum-alloy strand from an aluminum-alloy comprising:
- Fe;
0.1% by mass or more to less than 1.0% by mass;
Zr;
0 to 0.08% by mass;
Si;
0.02 to 2.8% by mass;
at least one of Cu;
0.05 to 0.63% by mass and Mg;
0.04 to 0.45% by mass; and
the remainder being aluminum and unavoidable impurities,the method comprising the steps of;
(1) forming a wire rod using the aluminum-alloy;
(2) wire-drawing the wire rod without a thermal treatment until becoming a desired final wire diameter; and
(3) continuously annealing or batch-wise annealing the wire rod which has been wire-drawn.
2 Assignments
0 Petitions
Accused Products
Abstract
There is provided an aluminum-alloy material having sufficient electric conductivity and tensile strength as a wiring material and excellent in wire-drawing property, and an electric wire or cable using the same. An electric wire or cable includes an aluminum-alloy strand formed of an aluminum-alloy including Fe: 0.1% by mass or more to less than 1.0% by mass, Zr: 0 to 0.08% by mass, Si: 0.02 to 2.8% by mass, at least one of Cu: 0.05 to 0.63% by mass and Mg: 0.04 to 0.45% by mass, and the remainder being aluminum and unavoidable impurities.
7 Citations
1 Claim
-
1. A method for producing an aluminum-alloy strand from an aluminum-alloy comprising:
-
Fe;
0.1% by mass or more to less than 1.0% by mass;Zr;
0 to 0.08% by mass;Si;
0.02 to 2.8% by mass;at least one of Cu;
0.05 to 0.63% by mass and Mg;
0.04 to 0.45% by mass; andthe remainder being aluminum and unavoidable impurities, the method comprising the steps of; (1) forming a wire rod using the aluminum-alloy; (2) wire-drawing the wire rod without a thermal treatment until becoming a desired final wire diameter; and (3) continuously annealing or batch-wise annealing the wire rod which has been wire-drawn.
-