Cerium-containing nanoparticles

• US 8,883,865 B2
• Filed: 05/13/2010
• Issued: 11/11/2014
• Est. Priority Date: 09/05/2006
• Status: Expired due to Fees

• Current Assignee: Cerion, LLC (Revstone Industries LLC)
• Original Assignee: Cerion Technology, Inc.
• Inventors: DiFrancesco, Albert Gary, Hailstone, Richard K., Reed, Kenneth J., Prok, Gary R.
• Primary Examiner(s): BOS, STEVEN J
• Application Number:
  US12/779,602
• Publication Number:
  US 20100242342A1
• Time in Patent Office: 1,643 Days
• Field of Search: 516/34, 516 88- 90, 423/263, 423/275
• US Class Current: 516/88
• CPC Class Codes: B01J 13/0034 Additives, e.g. in view of promoting stabilisation or peptisation
• CPC Class Codes: B01J 13/0047 containing a metal oxide
• CPC Class Codes: B82Y 30/00 Nanotechnology for materials or surface science, e.g. nanocomposites
• CPC Class Codes: C01F 17/235 Cerium oxides or hydroxides
• CPC Class Codes: C01F 17/32 oxide or hydroxide being the only anion, e.g. NaCeO2 or MgxCayEuO
• CPC Class Codes: C01G 25/00 Compounds of zirconium
• CPC Class Codes: C01G 25/02 Oxides
• CPC Class Codes: C01G 49/0054 containing one rare earth metal, yttrium or scandium
• CPC Class Codes: C01G 49/009 Compounds containing, besides iron, two or more other elements, with the exception of oxygen or hydrogen
• CPC Class Codes: C01G 49/02 Oxides; Hydroxides C01G49/0018 takes precedence
• CPC Class Codes: C01G 55/00 Compounds of ruthenium, rhodium, palladium, osmium, iridium, or platinum
• CPC Class Codes: C01P 2002/30 Three-dimensional structures
• CPC Class Codes: C01P 2002/52 containing elements as dopants
• CPC Class Codes: C01P 2002/72 by d-values or two theta-values, e.g. as X-ray diagram
• CPC Class Codes: C01P 2004/04 obtained by TEM, STEM, STM or AFM
• CPC Class Codes: C01P 2004/51 Particles with a specific particle size distribution
• CPC Class Codes: C01P 2004/52 highly monodisperse size distribution
• CPC Class Codes: C01P 2004/64 Nanometer sized, i.e. from 1-100 nanometer
• CPC Class Codes: C01P 2006/90 Other properties not specified above
• CPC Class Codes: C10G 25/02 with ion-exchange material
• CPC Class Codes: C10L 1/10 : containing additives
• CPC Class Codes: C10L 1/1233 : oxygen containing compounds, e.g. oxides, hydroxides, acids and salts thereof
• CPC Class Codes: C10L 1/1881 : carboxylic group attached to an aliphatic carbon atom
• CPC Class Codes: C10L 10/02 : for reducing smoke development
• CPC Class Codes: C10L 10/06 : for facilitating soot removal
• CPC Class Codes: C10L 2200/0222 : Group IV metals: Ti, Zr, Hf, Ge, Sn, Pb
• CPC Class Codes: C10L 2200/024 : Group VIII metals: Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt
• CPC Class Codes: C10L 2200/0245 : Lanthanide group metals: La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu
• CPC Class Codes: C10L 2200/0254 : Oxygen containing compounds
• CPC Class Codes: C10L 2230/22 : for improving fuel economy or fuel efficiency
• CPC Class Codes: C10L 2250/06 : Particle, bubble or droplet size
• CPC Class Codes: C10L 2270/026 : for diesel engines, e.g. automobiles, stationary, marine
• CPC Class Codes: Y02E 60/50 : Fuel cells
• CPC Class Codes: Y10T 428/2982 : Particulate matter [e.g., sphere, flake, etc.]

Abstract

A process for making cerium-containing oxide nanoparticles includes providing an aqueous reaction mixture containing a source of cerous ion, optionally a source of one or more metal ions (M) other than cerium, a source of hydroxide ion, at least one monoether carboxylic acid nanoparticle stabilizer wherein the molar ratio of said monoether carboxylic acid nanoparticle stabilizers to total metal ions is greater than 0.2, and an oxidant at an initial temperature in the range of about 20° C. to about 95° C. Temperature conditions are provided effective to enable oxidation of cerous ion to ceric ion, thereby forming a product dispersion of cerium-containing oxide nanoparticles, optionally containing one or more metal ions (M), Ce_1-xM_xO_2-δ, wherein “x” has a value from about 0.0 to about 0.95. The nanoparticles may have a mean hydrodynamic diameter from about 1 nm to about 50 nm, and a geometric diameter of less than about 45 nm.

Claims

1. A method for making a dispersion of cerium oxide nanoparticles that include at least one other metal, comprising:

a) forming an aqueous reaction mixture comprising;

i) a source of cerous ion and a source of one or more metal ions other than cerium, wherein said source of cerous ion and said source of one or more metal ions other than cerium are introduced into the reaction mixture concurrently;

ii) a source of hydroxide ion;

iii) at least one monoether carboxylic acid, wherein the molar ratio of said monoether carboxylic acid to total metal ions is greater than 0.2; and

iv) an oxidant at an initial temperature in the range of about 20°

C. to about 100°

C.;

b) maintaining the reaction mixture at a temperature permitting oxidation of cerous ion to ceric ion; and

c) thereby forming in the reaction mixture a dispersion of metal-containing cerium oxide nanoparticles, Ce_1-xM_xO_2-δ

, wherein x has a value from about 0.001 to about 0.95;

M represents said at least one other metal, and δ

has a value of about 0.0 to about 0.5.

2. The method of claim 1, wherein the nanoparticles have a mean hydrodynamic diameter of about 1 nm to about 50 nm.

3. The method of claim 1, wherein the nanoparticles have a mean hydrodynamic diameter of 1.5 to 8 nm.

4. The method of claim 1, wherein the nanoparticles have a mean hydrodynamic diameter of 2 to 4 nm.

5. The method of claim 1, wherein said other metal is selected from the group consisting of transition metals, rare earth metals, and combinations thereof.

6. The method of claim 1, wherein said other metal is selected from the group consisting of iron, zirconium, and combinations thereof.

7. The method of claim 1, wherein x has a value of about 0.30 to 0.60.

8. The method of claim 1, wherein said source of cerous ion is cerous nitrate.

9. The method of claim 1, wherein said monoether carboxylic acid is selected from the group consisting of ethoxyacetic acid, methoxyacetic acid, 3-methoxypropionic acid, and combinations thereof.

10. The method of claim 9, wherein said monoether carboxylic acid is methoxyacetic acid.

11. The method of claim 1, wherein said oxidant is hydrogen peroxide.

12. The method of claim 1, wherein the molar ratio of monoether carboxylic acid to total metal ions is greater than 0.3.

13. The method of claim 1, wherein the molar ratio of monoether carboxylic acid to total metal ions is greater than 0.6.

14. The method of claim 1, wherein the pH of the reaction mixture is less than or equal to 7.

15. The method of claim 1, wherein the pH of the reaction mixture is less than or equal to 5.

16. The method of claim 1, further comprising adding the metal-containing cerium oxide nanoparticles to diesel fuel as a fuel additive.

17. The method of claim 1, wherein said nanoparticles are characterized by a crystalline cubic fluorite structure.