Time temperature indicator

• US 8,968,662 B2
• Filed: 06/15/2009
• Issued: 03/03/2015
• Est. Priority Date: 06/23/2008
• Status: Active Grant

• Current Assignee: Freshpoint Quality Assurance Ltd.
• Original Assignee: Freshpoint Quality Assurance Ltd.
• Inventors: Haarer, Dietrich, Salman, Husein, Gueta-Neyroud, Tal
• Primary Examiner(s): Smith, R. A.
• Assistant Examiner(s): COURSON, TANIA C
• Application Number:
  US13/001,049
• Publication Number:
  US 20110155043A1
• Time in Patent Office: 2,087 Days
• Field of Search: 116/201, 116/206, 116/207, 116216-220, 116/200, 156/273.3, 156/280, 422/420, 422/82.01, 436/2, 436/7, 374/100, 374102-107
• US Class Current: 422/82.01
• CPC Class Codes: G01K 3/04 in respect of time

Abstract

The present invention is generally in the field of measuring and indicating techniques and relates to a time-temperature indicator and methods of manufacturing and use thereof. More specifically, the time-temperature indicator comprises at least one metal layer or metal containing layer, and in direct contact to the metal layer or to the metal containing layer at least one pad member affixed onto a pad carrier layer,

wherein the pad member comprises a pad made of an absorbent material and a dopant medium, whereby the dopant medium comprises a liquid medium or a viscous medium or a viscoelastic medium which is doped with a dopant that destroys the metal/metal containing layers such as an acid, a base or a salt or a photolatent acid or a photolatent base.

Claims

1. A time temperature indicator, comprising:

a) a metal layer or metal containing layer; and

b) in direct contact with the metal layer or the metal containing layer, at least one pad member affixed onto a pad carrier layer,

wherein the pad member comprises a pad made of an absorbent material and a dopant medium, wherein the dopant medium comprises a liquid medium or a viscous medium or a viscoelastic medium, which liquid/viscous/viscoelastic medium includes as a component a dopant able to destroy the metal/metal containing layers, wherein, when said metal layer is part of a capacitive device with two capacitor plates and a dielectric/insulating layer therebetween, the pad member is not part of the dielectric/insulating layer between the conductive layers of the capacitive device.

2. A time temperature indicator according to claim 1, wherein the dopant is a salt.

3. A time temperature indicator according to claim 1, wherein the dopant is an acid.

4. A time temperature indicator according to claim 1, wherein the dopant is a base.

5. A time temperature indicator according to claim 1, wherein the dopant is a photolatent acid where the acid is released upon irradiation with light.

6. A time temperature indicator according to claim 1, wherein the dopant is a photolatent base where the base is released upon irradiation with light.

7. A time temperature indicator according to claim 1, wherein the dopant is present in the medium in a concentration of 1-20%.

8. The time temperature indicator according to claim 7, wherein the metal layer is a metal-containing layer consisting of or based on inks based on metal pigment dispersions.

9. The time temperature indicator according to claim 7, wherein the metal layer is a polymer matrix containing metal particles.

10. The time temperature indicator according to claim 7, wherein the metal/metal containing layer comprises at least two sections of different thickness.

11. The time temperature indicator according to claim 7, wherein the metal layer is part of a resistor device.

12. The time temperature indicator according to claim 7, wherein the metal layer is part of a capacitive device comprising two conductive layers with a dielectric/insulating layer therebetween.

13. A method for producing the time temperature indicator as described in claim 1, comprising:

a) doping a pad by adding to the pad a liquid medium or a viscous medium or a viscoelastic medium which is doped with a salt solution, a liquid acid or a liquid base, thus obtaining a reactive pad member;

b) applying the reactive pad member of step a) on a carrier, thus obtaining a reactive pad layer as one label;

c) applying a metal layer or a metal containing layer on a substrate, thus obtaining a second label; and

d) activating by applying the pad layer of step b) onto the metal layer of step c).

14. A method according to claim 13, wherein said steps a) and b) comprise:

i) submerging the pad in the liquid dopant or pouring the dopant upon the pad;

ii) sticking the pad member on a suitable carrier thus obtaining a first label; and

iii) removing the excess dopant.

15. A method for producing the time temperature indicator as described in claim 1, comprising:

a) doping a pad by adding to the pad a liquid medium or a viscous medium or a viscoelastic medium which is doped with a photolatent acid or a photolatent base, thus obtaining a reactive pad member;

b) activating the photolatent reactive pad member by irradiation with light, thus obtaining a reactive pad member; and

c) applying the pad member onto a metal layer or a metal containing layer affixed on a substrate, thus obtaining a label, whereby placing one layer atop the other may be done either before activation or after or at the same time.

16. In a method of monitoring storage temperatures of product packages and for detecting exceeded temperature limits using a time temperature indicator, the improvement wherein said time temperature indicator is the time temperature indicator of claim 1.