Negative electrode for lithium secondary battery and method for producing same
First Claim
1. A negative electrode for the lithium secondary battery, comprisinga current collector;
- andan electrode layer that is formed on the current collector and contains at least a negative electrode active material, a conductive assistant and a binder component,wherein the negative electrode active material is composed of α
-Fe2O3 particles that generate a conversion electrode reaction and the binder component is a mixture of polyamide acid and partially imidized polyamide acid, a rate of imidization is 0.3 to 30%, and a concentration of the binder component of the electrode layer is configured so that the concentration decreases as distanced from the current collector.
1 Assignment
0 Petitions
Accused Products
Abstract
A negative electrode for a lithium secondary battery, in which α-Fe2O3 that is low in cost, has little environmental impact and has high theoretical capacity is used as an active material, maintains high adhesiveness between a current collector and an electrode layer, and can simultaneously achieve both of an improvement in the cycle characteristics and high capacity. In a negative electrode for a lithium secondary battery, which is configured of a current collector, and an electrode layer that is formed on the current collector and contains at least a negative electrode active material, a conductive assistant and a binder component, the negative electrode active material is composed of α-Fe2O3 particles that generate a conversion electrode reaction, the binder component is a mixture of polyamide acid and partially imidized polyamide acid. The electrode layer is configured so that a concentration of the binder component decreases as distanced from the current collector.
8 Citations
7 Claims
-
1. A negative electrode for the lithium secondary battery, comprising
a current collector; - and
an electrode layer that is formed on the current collector and contains at least a negative electrode active material, a conductive assistant and a binder component, wherein the negative electrode active material is composed of α
-Fe2O3 particles that generate a conversion electrode reaction and the binder component is a mixture of polyamide acid and partially imidized polyamide acid, a rate of imidization is 0.3 to 30%, and a concentration of the binder component of the electrode layer is configured so that the concentration decreases as distanced from the current collector. - View Dependent Claims (2, 5, 6, 7)
- and
-
3. A method for producing a negative electrode for a lithium secondary battery, comprising:
-
coating a slurry containing at least a negative electrode active material, a conductive assistant, a binder and a solvent on a current collector; and vacuum drying and pressing the current collector having a coating film to form an electrode layer containing at least the negative electrode active material, the conductive assistant and the binder component on the current collector, wherein as the negative electrode active material configuring the slurry,α
-Fe2O3 particles that generate a conversion electrode reaction are used, and as the binder configuring the slurry, polyamide acid is used, the slurry is adjusted to low viscosity of 2 to 3 Pa·
s at room temperature, the binder is allowed to naturally sediment in the coating film formed by coating the prepared low viscosity slurry, thereby a concentration of the binder component in the electrode layer formed on the current collector is configured so as to decrease as distanced from the current collector, andthe binder is partially imidized by vacuum drying and pressing to render the binder component contained in the electrode layer to a mixture of polyamide acid and partially imidized polyamide acid. - View Dependent Claims (4)
-
Specification