Coatings, composition and method related to non-spalling low density hardface coatings
First Claim
1. A heterogeneous composite body adhered to a substrate with an adhesive strength of greater than about 10,000 pounds per square inch gauge, said heterogeneous composite body being spall resistant and comprising a discontinuous cermet phase formed by cermet regions in a metal rich matrix phase, said metal rich matrix phase having an average span between said cermet regions sufficient to permit said metal rich matrix phase to work harden, said discontinuous cermet phase including ceramic particles and a cermet binder, said ceramic particles having a Moh'"'"'s hardness of at least approximately 7.5, a modulus of less than approximately 46,000,000 pounds per square inch, and an average particle size of from about 0.1 to 10 microns, said heterogeneous composite body having a Vicker'"'"'s hardness number of greater than approximately 500, a strain to failure of more than 1 percent, exhibits residual stresses of generally between approximately 5,000 pounds per square inch compressive and approximately 3,000 pounds per square inch tensile, and a modulus of less than approximately 35,000,000 pounds per square inch;
- wherein said ceramic particles comprise at least one of Si3N4, zircon, mullite, VN, V2N, Nb2N, SiCN, or SiON.
4 Assignments
0 Petitions
Accused Products
Abstract
A heterogeneous composite body that is spall resistant and comprises a substantially discontinuous cermet phase in a substantially continuous metal rich matrix phase. The heterogeneous composite body is typically bonded to a substrate to form a hardfacing on the substrate. The heterogeneous composite body exhibits ductile phase toughening with a strain to failure of at least about 2 percent, a modulus of elasticity of less than about 35 million pounds per square inch, and a density of less than about 7 grams per cubic centimeter. The metal rich matrix phase between the ceramic rich regions in the heterogeneous composite body has an average minimum span of about 0.5 to 8 microns to allow ductility in the heterogeneous composite body. The heterogeneous composite body has a Vicker'"'"'s hardness number of greater than approximately 500. The ceramic rich regions exhibit high hardness as compared with the matrix phase.
-
Citations
18 Claims
-
1. A heterogeneous composite body adhered to a substrate with an adhesive strength of greater than about 10,000 pounds per square inch gauge, said heterogeneous composite body being spall resistant and comprising a discontinuous cermet phase formed by cermet regions in a metal rich matrix phase, said metal rich matrix phase having an average span between said cermet regions sufficient to permit said metal rich matrix phase to work harden, said discontinuous cermet phase including ceramic particles and a cermet binder, said ceramic particles having a Moh'"'"'s hardness of at least approximately 7.5, a modulus of less than approximately 46,000,000 pounds per square inch, and an average particle size of from about 0.1 to 10 microns, said heterogeneous composite body having a Vicker'"'"'s hardness number of greater than approximately 500, a strain to failure of more than 1 percent, exhibits residual stresses of generally between approximately 5,000 pounds per square inch compressive and approximately 3,000 pounds per square inch tensile, and a modulus of less than approximately 35,000,000 pounds per square inch;
- wherein said ceramic particles comprise at least one of Si3N4, zircon, mullite, VN, V2N, Nb2N, SiCN, or SiON.
- View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13)
-
14. A heterogeneous composite body, said heterogeneous composite body being spall resistant and adhered to a substrate with an adhesive strength of greater than about 10,000 pounds per square inch gauge, said heterogeneous composite body comprising a discontinuous cermet phase in a metal rich matrix phase, said discontinuous cermet phase including ceramic particles and a cermet binder, said ceramic particles having a Moh'"'"'s hardness of at least approximately 8, a modulus of less than approximately 46,000,000 pounds per square inch, and an average particle size of from about 0.1 to 10 microns, said heterogeneous composite body having a Vicker'"'"'s hardness number of greater than approximately 650, a strain to failure of at least about 2 percent, said heterogeneous composite body exhibiting strain tolerance wherein defects work harden and redirect strain away from a deformation zone, a density of less than about 7 grams per cubic centimeter, and a modulus of less than approximately 35,000,000 pounds per square inch, and said metal rich matrix phase having an average span sufficient to permit said metal rich matrix phase to work harden;
- wherein said ceramic particles comprise at least one of Si3N4, zircon, mullite, VN, V2N, Nb2N, SiCN, or SiON.
-
15. A heterogeneous composite body, said heterogeneous composite body being spall resistant and adhered to a substrate with an adhesive strength of greater than about 10,000 pounds per square inch gauge, said heterogeneous composite body comprising a discontinuous cermet phase in a metal rich matrix phase, said metal rich matrix phase having a modulus of less than approximately 42,000,000 pounds per square inch, said discontinuous cermet phase including ceramic particles and a cermet binder, said ceramic particles having a Moh'"'"'s hardness of at least approximately 8, a modulus of less than approximately 46,000,000 pounds per square inch, and an average particle size of from about 0.3 to 8 microns, said heterogeneous composite body having a Vicker'"'"'s hardness number of greater than approximately 750, a strain to failure of from at least about 2 to about 6 percent, said heterogeneous composite body exhibiting strain tolerance wherein defects work harden and redirect strain away from a deformation zone, a density of less than about 6 grams per cubic centimeter, residual stresses of generally between approximately 5,000 pounds per square inch compressive and approximately 3,000 pounds per square inch tensile, and a modulus of less than approximately 35,000,000 pounds per square inch, and said metal rich matrix phase has an average span of about 0.5 to 2 microns;
- wherein said ceramic particles comprise at least one of Si3N4, zircon, mullite, VN, V2N, Nb2N, SiCN, or SiON.
-
16. A heterogeneous composite body adhered to a substrate with an adhesive strength of greater than about 10,000 pounds per square inch gauge, said heterogeneous composite body being spall resistant and comprising a discontinuous cermet phase in a metal rich matrix phase, said discontinuous cermet phase including ceramic particles and a cermet binder, said metal rich matrix phase having an average span of about 0.4 to 8 microns and a modulus of less than approximately 42,000,000 pounds per square inch, said heterogeneous composite body having a Vicker'"'"'s hardness number of greater than approximately 650, a strain to failure of at least about 2 percent, said heterogeneous composite body exhibiting strain tolerance wherein defects work harden and redirect strain away from a deformation zone, and a modulus of less than approximately 35,000,000 pounds per square inch, there being little strain mismatch between said substrate and said heterogeneous composite body;
- wherein said ceramic particles comprise at least one of Si3N4, zircon, mullite, VN, V2N, Nb2N, SiCN, or SiON.
- View Dependent Claims (17, 18)
Specification