Method of producing a dental product
First Claim
Patent Images
1. A method of producing a dental product, the method comprising the steps of:
- providing a blank made from a green body of ceramic material,re-sintering at a temperature at a beginning of a neck area of a density versus temperature curve, wherein the neck area is where a relatively flat part of the curve is followed by a relatively sharply rising part of the curve,performing a machining operation on the blank, andsubsequently sintering the blank to its final density in a sintering operation performed at a heating rate in the range of 0.1-1°
C./minute and held at a temperature in the range of 1300°
C. to 1650°
C.
0 Assignments
0 Petitions
Accused Products
Abstract
Methods of producing a dental product are disclosed. Certain methods include the steps of providing a pre-sintered blank made from a green body of ceramic material, performing a machining operation on the blank, and subsequently sintering the blank to its final density in a sintering operation performed at a temperature in the range of 1300° C. to 1650° C. The pre-sintered blank that is provided may have a strength in the range of 53-107 MPa.
50 Citations
19 Claims
-
1. A method of producing a dental product, the method comprising the steps of:
-
providing a blank made from a green body of ceramic material, re-sintering at a temperature at a beginning of a neck area of a density versus temperature curve, wherein the neck area is where a relatively flat part of the curve is followed by a relatively sharply rising part of the curve, performing a machining operation on the blank, and subsequently sintering the blank to its final density in a sintering operation performed at a heating rate in the range of 0.1-1°
C./minute and held at a temperature in the range of 1300°
C. to 1650°
C. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 14, 15)
-
-
12. A method of producing a dental product, the method comprising the steps of:
-
providing a blank made from a green body of ceramic material, pre-sintering at a temperature at a beginning of a neck area of a density versus temperature curve, wherein the neck area is where a relatively flat part of the curve is followed by a relatively sharply rising part of the curve, performing a machining operation on the blank, and subsequently sintering the blank to its final density in a sintering operation, the blank being held at a temperature in the range of 1300°
C. to 1650°
C., wherein prior to pre-sintering, the green body blank has been isostatically pressed at a pressure of 200 MPa-300 MPa. - View Dependent Claims (16, 17)
-
-
13. A method of producing a dental product, the method comprising the steps of:
-
providing a blank made from a green body of ceramic material, pre-sintering at a temperature at a beginning of a neck area of a density versus temperature curve, wherein the neck area is where a relatively flat part of the curve is followed by a relatively sharply rising part of the curve, performing a machining operation on the blank, and subsequently sintering the blank to its final density in a sintering operation, the blank being held at a temperature in the range of 1300°
C. to 1650°
C. and sintered to a final density of 6.00 g/cm3- 6.09 g/cm3. - View Dependent Claims (18, 19)
-