Low-smoke nitroguanidine and nitrocellulose based pyrotechnic compositions

• US 20020148540A1
• Filed: 04/12/2001
• Published: 10/17/2002
• Est. Priority Date: 04/12/2001
• Status: Active Grant

• Current Assignee: DMD Systems, LLC
• Original Assignee: DMD Systems, LLC
• Inventors: Hiskey, Michael A., Naud, Darren L.
• Granted Patent: US 6,599,379 B2
• Time in Patent Office: Days
• US Class Current: 149/19.8
• CPC Class Codes: C06B 33/00 Compositions containing particulate metal, alloy, boron, silicon, selenium or tellurium with at least one oxygen supplying material which is either a metal oxide or a salt, organic or inorganic, capable of yielding a metal oxide
• CPC Class Codes: C06C 15/00 Pyrophoric compositions; Flints chemical lighters C06C9/00; alloys in general C22C

Abstract

A low-smoke pyrotechnic composition comprising nitrocellulose; nitroguanidine; an oxidizing agent; and, at least one of a flame coloring agent and metal powder, and a method of processing the same is disclosed.

Claims

1. A low-smoke producing pyrotechnic composition comprising:

nitrocellulose;

nitroguanidine;

an oxidizing agent; and

,

at least one of a flame coloring agent and metal powder.

2. The pyrotechnic composition of claim 1 wherein the flame coloring agent comprises at least one metal salt.

3. The pyrotechnic composition of claim 2 wherein the at least one metal salt includes a metal selected from the group consisting of barium, strontium, iron, copper, boron, calcium, antimony, potassium, sodium, cadmium, uranium, gold, mercury, arsenic, and lead.

4. The pyrotechnic composition of claim 2 wherein the at least one metal salt comprises a carbonate salt.

5. The pyrotechnic composition of claim 2 wherein the oxidizing agent includes at least one compound selected from the group consisting of ammonium perchlorate, alkali metal perchlorates, alkali metal chlorates, and alkali metal nitrates.

6. The pyrotechnic composition of claim 1 wherein the oxidizing agent includes at least one compound selected from the group consisting of ammonium perchlorate, alkali metal perchlorates, alkali metal chlorates, and alkali metal nitrates.

7. The pyrotechnic composition of claim 1 wherein the metal powder includes at least one compound selected from the group consisting of titanium and titanium alloys.

8. The pyrotechnic composition of claim 1 wherein the metal powder includes at least one compound selected from the group consisting of iron and alloys of iron.

9. The pyrotechnic composition of claim 1 wherein the metal powder includes at least one compound selected from the group consisting of magnesium and alloys of magnesium.

10. The pyrotechnic composition of claim 1 wherein the metal powder includes at least one compound selected from the group consisting of aluminum and alloys of aluminum.

11. The pyrotechnic composition of claim 2 wherein the nitrocellulose is from about 30 to about 97 percent by weight, the nitroguanidine is from about 1 to about 70 percent by weight, the oxidizing agent is from about 1 to about 68 percent by weight, and the metal salt is from about 1 to about 20 percent by weight.

12. The pyrotechnic composition of claim 1 wherein the nitrocellulose is from about 30 to about 97 percent by weight, the nitroguanidine is from about 1 to about 70 percent by weight, the oxidizing agent is from about 1 to about 68 percent by weight, and the metal powder is from about 1 to about 20 percent by weight.

13. The pyrotechnic composition of claim 2 wherein the nitrocellulose is from about 30 to about 97 percent by weight, the nitroguanidine is from about 1 to about 70 percent by weight, the oxidizing agent is from about 1 to about 68 percent by weight, the metal salt is from about 1 to about 20 percent by weight, and the metal powder is from about 1 to about 20 percent by weight.

15. The method of claim 14 wherein the step of providing nitrocellulose includes providing damp nitrocellulose.

16. The method of claim 15 wherein the damp nitrocellulose contains about 30 percent by weight of water.

17. The method of claim 14 wherein a water-soluble binder is added prior to the step of mixing.

18. The method of claim 17 wherein the water-soluble binder is polyvinyl alcohol.

19. The method of claim 14 further comprising:

forming a geometrical shape from the pyrotechnic composition; and

,

air-drying said geometrical shape.

20. The method of claim 19 wherein the step of forming a geometrical shape includes the forming of right cylinders, and hollow core cylinders.

21. The method of claim 20 further comprising igniting the hollow core cylinders at the longitudinal ends of said hollow core cylinders.

14. A method of processing a low-smoke producing pyrotechnic composition comprising:

providing nitrocellulose from about 30 to about 97 percent by weight;

adding nitroguanidine from about 1 to about 70 percent by weight;

adding an oxidizing agent from about 1 to about 68 percent by weight, adding at least one of a flame coloring agent and a metal powder from about 1 to about 20 percent by weight; and

,

mixing the low-smoke producing pyrotechnic composition.