Overmolded transponder

• US 20020180602A1
• Filed: 07/10/2002
• Published: 12/05/2002
• Est. Priority Date: 05/17/1999
• Status: Active Grant

• Current Assignee: Jay Yoakum
• Original Assignee: Jay Yoakum
• Inventors: Yoakum, Jay
• Granted Patent: US 6,778,089 B2
• Time in Patent Office: Days
• US Class Current: 340/572.8
• CPC Class Codes: A01K 11/007 Boluses
• CPC Class Codes: B29C 2045/14852 incorporating articles with a data carrier, e.g. chips memory cards, chip cards B29L2017/006
• CPC Class Codes: B29C 45/14065 Positioning or centering articles in the mould
• CPC Class Codes: B29C 45/14073 using means being retractable during injection
• CPC Class Codes: B29C 45/1459 Coating annular articles
• CPC Class Codes: B29C 45/14598 Coating tubular articles
• CPC Class Codes: B29C 45/14639 for obtaining an insulating effect, e.g. for electrical components
• CPC Class Codes: B29C 45/14836 Preventing damage of inserts during injection, e.g. collapse of hollow inserts, breakage B29C45/14434 takes precedence
• CPC Class Codes: G06K 19/04 characterised by the shape
• CPC Class Codes: G06K 19/07724 the record carrier being at least partially made by a molding process molding in general B29C45/14
• CPC Class Codes: G06K 19/07749 the record carrier being capable of non-contact communication, e.g. constructional details of the antenna of a non-contact smart card
• CPC Class Codes: G06K 19/07758 arrangements for adhering the record carrier to further objects or living beings, functioning as an identification tag

Abstract

A method of fabricating, a composition and overmolded components fabricated by the method and with the composition such as an overmolded transponder circuitry for a radio frequency identification device.

Claims

1. An overmolded transponder for an electronic identification system comprising:

an antenna;

a transponder circuit including signal processing circuitry electrically interconnected to said antenna;

a core element on which said antenna and said transponder circuit are mounted; and

an overmolded casing formed by placing said antenna, transponder circuit and core element within a cavity formed by mold tooling in an injection molding machine and injecting an overmolding material into said cavity so as to overmold and encase said core element, said transponder circuit and said antenna.

2. The transponder of claim 1 wherein said overmolded casing has a wall thickness of between about 0.010 inches to one inch.

3. The transponder of claim 1 wherein said overmolding material is selected from the group consisting of plastic, polymeric and epoxy materials.

4. The transponder of claim 1 wherein said overmolding material is a blend of a thermoplastic polyester elastomer (TPE) having properties comparable to that of the TPE sold under the brand name HYTREL 3078™

available from DuPont, mixed with barium sulfate in a ratio of between about 20 to 90% TPE and 80% to 10% barium sulfate.

5. The transponder of claim 1 wherein said overmolding material is a thermoplastic material selected from the group consisting of linear polymers and straight-chain and branch-chained macromolecules that soften or plasticize when exposed to heat and return to a hardened state when cooled.

6. The transponder of claim 1 wherein said overmolding material is a polymer selected from the group consisting of random polymers, block polymers, and graft polymers.

7. The transponder of claim 1 wherein said overmolding material is a thermoplastic material selected from the group consisting of rubber modified polyolefins, mettallocene, polyether-ester block copolymers, polyether-amide block copolymers, thermoplastic based urethanes, copolymers of ethylene with butene and maleic anhydride, hydrogenated maleic anhydride, polyester polycaprolactone, polyester polyadipate, polytetramethylene glycol ether, thermoplastic elastomer, polypropylene, vinyl, chlorinated polyether, polybutylene terephalate, ploymethylpentene, silicone, polyvinyl chloride, thermoplastic polyurethane, polycarbonate, polyurethane, polyamide, polybutylene, polyethylene and blends thereof.

8. The transponder of claim 1 wherein said overmolding material is a rubber modified polyolefin material selected from the group consisting of materials commercially available under the tradenames of VISTAFLEX™

from Advanced Elastomer Systems Corporation, KRATON™

from Shell Corporation, HIFAX™

from Montell Corporation, X1019-28™

from M. A. Hanna, SARLINK™

from DSM Corporation, and SANTOPRENE™

from Advanced Elastomer Systems Corporation.

9. The transponder of claim 1 wherein said overmolding material is a polyether-ester block copolymer commercially available from DuPont under the tradename HYTREL™

.

10. The transponder of claim 3 wherein said overmolding material includes a weighting material selected from the group consisting of barium sulfate, zinc oxide, calcium carbonate, titanium dioxide, carbon black, kaolin, magnesium aluminum silicate, silica, iron oxide, glass spheres and wollastonite.

11. The transponder of claim 10 wherein the weighting material is present in an amount of between about 5 percent by weight to about 70 percent by weight.

12. The transponder of claim 10 wherein said overmolding material further includes a plasticizer in an amount sufficient to adjust the flow properties during the injection molding process.

13. The transponder of claim 1 wherein said overmolding material is a TPE blend sold under the tradename HYTREL 8388™

by DuPont.

14. The transponder of claim 1 wherein said overmolding material is a combination of:

a thermoplastic material selected from at least one of the group consisting of rubber modified polyolefins, mettallocene, polyether-ester block copolymers, polyether-amide block copolymers, thermoplastic based urethanes, copolymers of ethylene with butene and maleic anhydride, hydrogenated maleic anhydride, polyester polycaprolactone, polyester polyadipate, polytetramethylene glycol ether, thermoplastic elastomer, polypropylene, vinyl, chlorinated polyether, polybutylene terephalate, ploymethylpentene, silicone, polyvinyl chloride, thermoplastic polyurethane, polycarbonate, polyurethane, polyamide, polybutylene and, polyethylene; and

a weighting material selected from the group consisting of barium sulfate, zinc oxide, calcium carbonate, titanium dioxide, carbon black, kaolin, magnesium aluminum silicate, silica, iron oxide, glass spheres and wollastonite.

15. The transponder of claim 1 wherein said overmolding material is a thermoplastic polyester elastomer (TPE), mixed with barium sulfate in a ratio of between about 20 to 90% TPE and 80% to 10% barium sulfate to have a specific gravity in the range of between about 1.7 and 2.

16. The transponder of claim 1 wherein said core element is made of a frangible material forming a frangible core.

17. The transponder of claim 16 wherein said frangible core is formed from a material selected from the group consisting of ferrite, powdered metals and high energy product magnets such as samarium cobalt and neodymium-iron-boron materials.

19. The overmolded component of claim 18 wherein said overmolding material is selected from the group consisting of plastic, polymeric and epoxy materials.

20. The overmolded component of claim 19 wherein said frangible material of said core element is a shaped material selected from the group consisting of ferrite, powdered metals and high energy product magnets such as samarium cobalt and neodymium-iron-boron materials.

21. The overmolded component of claim 18 wherein said core element is a radio frequency identification transponder encased in a glass capsule.

18. An overmolded component comprising:

a core element formed from a frangible material; and

an overmolded casing formed by placing said core element within a cavity formed by mold tooling in an injection molding machine and injecting an overmolding material into said cavity so as to overmold and encase said frangible material of said core element without subjecting said frangible material to tensile loading.

22. A method of forming an overmolded transponder for an electronic identification system comprising:

providing a transponder circuit including signal processing circuitry electrically interconnected to an antenna;

mounting said antenna and said transponder circuit on a core element to form an assembly;

placing said transponder circuit and core element assembly within a cavity formed by mold tooling in an injection molding machine, and injecting an overmolding material into said cavity so as to overmold and encase said core element and said transponder circuit.

23. The method of claim 22, further comprising selecting said overmolding material from the group consisting of plastic, polymeric and epoxy materials.

24. The method of claim 22, further comprising blending a thermoplastic polyester elastomer (TPE) mixed with barium sulfate in a ratio of between about 20 to 90% TPE and 80% to 10% barium sulfate to form the overmolding material prior to the injection step.

25. The method of claim 22, further comprising selecting said overmolding material from the group consisting of linear polymers and straight-chain and branch-chained macromolecules that soften or plasticize when exposed to heat and return to a hardened state when cooled.

26. The method of claim 22, further comprising selecting said overmolding material from one or more of the group consisting of rubber modified polyolefins, mettallocene, polyether-ester block copolymers, polyether-amide block copolymers, thermoplastic based urethanes, copolymers of ethylene with butene and maleic anhydride, hydrogenated maleic anhydride, polyester polycaprolactone, polyester polyadipate,polytetramethylene glycol ether, thermoplastic elastomer, polypropylene, vinyl, chlorinated polyether, polybutylene terephalate, ploymethylpentene, silicone, polyvinyl chloride, thermoplastic polyurethane, polycarbonate, polyurethane, polyamide, polybutylene, and polyethylene.

27. The method of claim 22, further comprising plasticizing a polyether-ester block copolymer commercially available from DuPont under the tradename HYTREL™

, and a barium sulfate weighting material to form the overmolding material.

28. The method of claim 22, further comprising blending into said overmolding material a weighting material selected from the group consisting of barium sulfate, zinc oxide, calcium carbonate, titanium dioxide, carbon black, kaolin, magnesium aluminum silicate, silica, iron oxide, glass spheres and wollastonite.

30. The method of claim 29 wherein said frangible core is positioned in said mold tooling by retractile pins during the overmolding process.

31. The method of claim 29 wherein said frangible core is positioned in said mold tooling by a centering element having a plurality of outwardly projecting fins during the overmolding process.

29. A method of overmolding an element having a frangible core, comprising:

placing a frangible core within a cavity formed by mold tooling in an injection molding machine;

positioning said frangible core so as to space said frangible core from said tooling;

injecting an overmolding material into said cavity so as to exert predominantly compressive loads and substantially no tensile and bending loads on said frangible core to encase said frangible core in said overmolding material;

allowing said overmolding material to cure;

and ejecting said element from said cavity.

32. An overmolding material suitable for overmolding electronic core components comprising:

a thermoplastic polyester elastomer (TPE) mixed with barium sulfate in a ratio of between about 20 to 90% TPE and 80% to 10% barium sulfate.

33. An overmolding material suitable for overmolding frangible components, comprising:

a thermoplastic material selected from one or more of the group consisting of rubber modified polyolefins, mettallocene, polyether-ester block copolymers, polyether-amide block copolymers, thermoplastic based urethanes, copolymers of ethylene with butene and maleic anhydride, hydrogenated maleic anhydride, polyester polycaprolactone, polyester polyadipate, polytetramethylene glycol ether, thermoplastic elastomer, polypropylene, vinyl, chlorinated polyether, polybutylene terephalate, ploymethylpentene, silicone, polyvinyl chloride, thermoplastic polyurethane, polycarbonate, polyurethane, polyamide, polybutylene and, polyethylene; and

a weighting material selected from the group consisting of barium sulfate, zinc oxide, calcium carbonate, titanium dioxide, carbon black, kaolin, magnesium aluminum silicate, silica, iron oxide, glass spheres and wollastonite.