Flame retardant composition

• US 20050228087A1
• Filed: 05/27/2003
• Published: 10/13/2005
• Est. Priority Date: 05/28/2002
• Status: Active Grant

• Current Assignee: Asahi Kasei Chemicals Corporation (Asahi Kasei Corporation)
• Original Assignee: Asahi Kasei Corporation
• Inventors: Murakami, Fumiki, Nanasawa, Atsushi, Nakahashi, Junnichi
• Granted Patent: US 7,091,266 B2
• Time in Patent Office: Days
• US Class Current: 524/115
• CPC Class Codes: C08K 5/0066 Flame-proofing or flame-retarding additives
• CPC Class Codes: C08K 5/5399 Phosphorus bound to nitrogen
• CPC Class Codes: C08L 71/12 Polyphenylene oxides
• CPC Class Codes: C08L 71/123 not modified by chemical after-treatment

Abstract

A flame-retardant composition comprises a polyphenylene ether resin having a number average molecular weight in terms of polystyrene of 500 to 5,000 and a phosphazene compound, the content of the polyphenylene ether being 20 to 95% by weight and that of the phosphazene compound being 80 to 5% by weight. The flame-retardant composition is excellent in processability when added to resins, and can provide a resin composition that contains no halogens and has an excellent balance of processability, heat resistance and flame retardancy.

Claims

1. A flame-retardant composition comprising from 20 to 95% by weight of (a) a polyphenylene ether resin having a number average molecular weight of 500 to 5,000, and from 80 to 5% by weight of (b) a phosphazene compound.

2. The flame-retardant composition according to claim 1, wherein said polyphenylene ether resin has a number average molecular weight of 1,200 to 4,000.

3. The flame-retardant resin composition according to claim 1, wherein a part or all of said polyphenylene ether resin is functionalized with a compound having at least one functional group selected from the group consisting of an epoxy group, an amino group, a hydroxy group, a mercapto group, a carboxyl group and a silyl group.

4. The flame-retardant composition according to claims 1, wherein said phosphazene compound comprises a total of 95% by weight or more of a cyclic phosphazene compound represented by formula (1) and/or a straight chain phosphazene compound represented by formula (2):

5. The flame-retardant composition according to claim 4, wherein said phosphazene compound comprises 95% by weight or more of a cyclic phosphazene compound.

6. The flame-retardant composition according to claim 4, wherein 90 mol % or more of the all occurrences of substituent X is a phenoxy group in said phosphazene compound.

8. The flame-retardant composition according to claim 1, wherein said polyphenylene ether resin has an average particle diameter of 5 μ

m to 500 μ

m.

7. The flame-retardant composition according to claim, wherein said phosphazene compound comprises 80% by weight or more of a cyclic phosphazene trimer and/or tetramer.

9. A flame-retardant resin composition comprising a resin and a flame-retardant composition comprising from 20 to 95% by weight of (a) a polyphenylene ether resin having a number average molecular weight of 500 to 5,000, and from 80 to 5% by weight of (b) a phosphazene compound.

10. The flame-retardant resin composition according to claim 9, wherein said resin is at least one thermosetting resin selected from the group consisting of unsaturated polyester resins, vinylester resins, diallylphthalate resins, epoxy resins, cyanate resins, xylene resins, triazine resins, phenol resins, urea resins, melamine resins, benzoguanamine resins, urethane resins, ketone resins, alkyd resins, furan resins, styryl pyridine resins, silicone resins and synthetic rubbers.

11. The flame-retardant resin composition according to claim 9, wherein said resin comprises an epoxy resin.

12. The flame-retardant resin composition according to claim 9, wherein the concentration of phosphorus atoms is from 0.5% to 8.0% by weight.

13. The flame-retardant resin composition according to claim 9, wherein said polyphenylene ether resin is dispersed as particles with an average diameter of 10 μ

m or less.

14. The flame-retardant resin composition according to claim 9, characterized in that said resin is a thermoplastic resin.

15. The flame-retardant resin composition according to claim 9, wherein said resin is at least one thermoplastic resin selected from the group consisting of polycarbonates, polyphenylene ethers, polyphenylene sulfides, polypropylene, polyethylene, polystyrene, ABS resins, polyalkylene terephthalates, polyamides, thermotropic liquid crystal polymers and elastomer-containing polystyrenes.

16. The flame-retardant resin composition according to claim 9, wherein said resin is at least one thermoplastic resin selected from the group consisting of polyphenylene ether/polypropylene, polyphenylene ether/polystyrene, polyphenylene ether/polyamide, polyphenylene ether/thermotropic liquid crystal polymer, polyphenylene ether/polyphenylene sulfide and polyphenylene ether/polyalkylene terephthalate.

17. The flame-retardant resin composition according to claim 9, wherein the sum of the content of component (a) and a double amount of the content of component (b) in the flame-retardant resin composition is 15% by weight or more.

18. The flame-retardant resin composition according to claim 9, wherein the sum of the content of component (a) and a double amount of the content of component (b) in the flame-retardant resin composition is 25% by weight or more.

19. The flame-retardant resin composition according to claim 9, wherein the sum of the content of component (a) and a double amount of the content of component (b) in the flame-retardant resin composition is 40% by weight or more.

20. The flame-retardant resin composition according to claim 9, which is used for electronic equipment, parts or housings usable in a high-frequency range of 1 gigahertz (GHz) or more.