Method for manufacturing coconut based activated carbon polyester fiber with high percentage of carbon and the coconut based activated carbon polyester fiber made by the method
First Claim
1. A method for manufacturing coconut based activated carbon polyester fiber with high percentage of carbon;
- the method comprising the steps of;
mixing 5 wt %˜
15 wt % (weight percentages) coconut based activated carbon particles which have sizes smaller than 7 μ
m with 85 wt %˜
95 wt % polyester fibers by high temperature so as to get spinning fabrics which are in melted form;
extruding and ejecting the spinning fabrics to pass through a fabric ejection plate so as to form a melt ejection flow;
forming an initial fiber;
cooling the ejection flow leaving from the fabric ejection plate in low temperature and with a high speed to form an initial fiber; and
extending, coating oil, activating, drying, shaping, and packaging to form coconut based activated carbon polyester fibers with high percentage of carbons.
1 Assignment
0 Petitions
Accused Products
Abstract
A method for manufacturing coconut based activated carbon polyester fiber with high percentage of carbon includes the steps of: mixing 5 wt %˜15 wt % (weight percentages) coconut based activated carbon particles which have sizes smaller than 7 μm with 85 wt %˜95 wt % polyester fibers by high temperature so as to get spinning fabrics which are in melted form; extruding and ejecting the spinning fabrics to pass through a fabric ejection plate so as to form a melt ejection flow; forming an initial fiber: cooling the ejection flow leaving from the fabric ejection plate in lower temperature and with a high speed to form an initial fiber; and extending, coating oil, activating, drying, shaping, and packaging to form coconut based activated carbon polyester fibers with high percentage of carbons. A coconut based activated carbon with high percentage of carbon manufactured by the method is also included.
2 Citations
2 Claims
-
1. A method for manufacturing coconut based activated carbon polyester fiber with high percentage of carbon;
- the method comprising the steps of;
mixing 5 wt %˜
15 wt % (weight percentages) coconut based activated carbon particles which have sizes smaller than 7 μ
m with 85 wt %˜
95 wt % polyester fibers by high temperature so as to get spinning fabrics which are in melted form;extruding and ejecting the spinning fabrics to pass through a fabric ejection plate so as to form a melt ejection flow; forming an initial fiber;
cooling the ejection flow leaving from the fabric ejection plate in low temperature and with a high speed to form an initial fiber; andextending, coating oil, activating, drying, shaping, and packaging to form coconut based activated carbon polyester fibers with high percentage of carbons.
- the method comprising the steps of;
-
2. A coconut based activated carbon polyester fiber with high percentage of carbon comprising 5 wt %˜
- 15 wt % (weight percentages) coconut based activated carbon particles which have sizes smaller than 7 μ
m and 85 wt %˜
95 wt % polyester fibers by high temperature.
- 15 wt % (weight percentages) coconut based activated carbon particles which have sizes smaller than 7 μ
Specification