COMPOSITIONS OF ETHYLENE/ALPHA-OLEFIN MULTI-BLOCK INTERPOLYMER FOR ELASTIC FILMS AND LAMINATES
First Claim
Patent Images
1. An elastic breathable film comprising:
- at least one ethylene/α
-olefin interpolymer elastomer, wherein the ethylene/α
-olefin interpolymer elastomer (a) has a Mw/Mn from about 1.7 to about 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, wherein the numerical values of Tm and d correspond to the relationship;
Tm>
−
2002.9+4538.5(d)−
2422.2(d)2;
or(b) has a Mw/Mn from about 1.7 to about 3.5, and is characterized by a heat of fusion, Δ
H in J/g, and a delta quantity, Δ
T, in degrees Celsius defined as the temperature difference between the tallest DSC peak and the tallest CRYSTAF peak, wherein the numerical values of Δ
T and Δ
H have the following relationships;
Δ
T>
−
0.1299(Δ
H)+62.81 for Δ
H greater than zero and up to 130 J/g,
Δ
T≧
48°
C. for Δ
H greater than 130 J/g,wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30°
C.;
or(c) is characterized by an elastic recovery, Re, in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/α
-olefin interpolymer, and has a density, d, in grams/cubic centimeter, wherein the numerical values of Re and d satisfy the following relationship when ethylene/α
-olefin interpolymer is substantially free of a cross-linked phase;
Re>
1481−
1629(d);
or(d) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content of at least 5 percent higher than that of a comparable random ethylene interpolymer fraction eluting between the same temperatures, wherein said comparable random ethylene interpolymer has the same comonomer(s) and has a melt index, density, and molar comonomer content (based on the whole polymer) within 10 percent of that of the ethylene/α
-olefin interpolymer;
(e) has a storage modulus at 25°
C., G′
(25°
C.), and a storage modulus at 100°
C., G′
(100°
C.), wherein the ratio of G′
(25°
C.) to G′
(100°
C.) is in the range of about 1;
1 to about 9;
1;
or(f) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a block index of at least 0.5 and up to about 1 and a molecular weight distribution, Mw/Mn, greater than about 1.3;
or(g) has an average block index greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn, greater than about 1.3; and
optionally,a styrenic block copolymer, or a combination thereofwherein the ethylene/α
-olefin interpolymer has a density of from about 0.85 to about 0.885 g/cc.
1 Assignment
0 Petitions
Accused Products
Abstract
This invention relates to polyolefin compositions. In particular, the invention pertains to elastic polymer compositions that can be more easily processed on cast film lines, extrusion lamination or coating lines. The compositions of the present invention preferably comprise an elastomeric polyolefin resin and a high pressure low density type resin.
172 Citations
23 Claims
-
1. An elastic breathable film comprising:
-
at least one ethylene/α
-olefin interpolymer elastomer, wherein the ethylene/α
-olefin interpolymer elastomer (a) has a Mw/Mn from about 1.7 to about 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, wherein the numerical values of Tm and d correspond to the relationship;
Tm>
−
2002.9+4538.5(d)−
2422.2(d)2;
or(b) has a Mw/Mn from about 1.7 to about 3.5, and is characterized by a heat of fusion, Δ
H in J/g, and a delta quantity, Δ
T, in degrees Celsius defined as the temperature difference between the tallest DSC peak and the tallest CRYSTAF peak, wherein the numerical values of Δ
T and Δ
H have the following relationships;
Δ
T>
−
0.1299(Δ
H)+62.81 for Δ
H greater than zero and up to 130 J/g,
Δ
T≧
48°
C. for Δ
H greater than 130 J/g,wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30°
C.;
or(c) is characterized by an elastic recovery, Re, in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/α
-olefin interpolymer, and has a density, d, in grams/cubic centimeter, wherein the numerical values of Re and d satisfy the following relationship when ethylene/α
-olefin interpolymer is substantially free of a cross-linked phase;
Re>
1481−
1629(d);
or(d) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content of at least 5 percent higher than that of a comparable random ethylene interpolymer fraction eluting between the same temperatures, wherein said comparable random ethylene interpolymer has the same comonomer(s) and has a melt index, density, and molar comonomer content (based on the whole polymer) within 10 percent of that of the ethylene/α
-olefin interpolymer;(e) has a storage modulus at 25°
C., G′
(25°
C.), and a storage modulus at 100°
C., G′
(100°
C.), wherein the ratio of G′
(25°
C.) to G′
(100°
C.) is in the range of about 1;
1 to about 9;
1;
or(f) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a block index of at least 0.5 and up to about 1 and a molecular weight distribution, Mw/Mn, greater than about 1.3;
or(g) has an average block index greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn, greater than about 1.3; and
optionally,a styrenic block copolymer, or a combination thereof wherein the ethylene/α
-olefin interpolymer has a density of from about 0.85 to about 0.885 g/cc.- View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20)
-
-
21. A method for forming an elastic, breathable film comprising aperturing the film, wherein the film comprises:
-
at least one ethylene/α
-olefin interpolymer, wherein the ethylene/α
-olefin interpolymer(a) has a Mw/Mn from about 1.7 to about 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, wherein the numerical values of Tm and d correspond to the relationship;
Tm>
−
2002.9+4538.5(d)−
2422.2(d)2;
or(b) has a Mw/Mn from about 1.7 to about 3.5, and is characterized by a heat of fusion, Δ
H in J/g, and a delta quantity, Δ
T, in degrees Celsius defined as the temperature difference between the tallest DSC peak and the tallest CRYSTAF peak, wherein the numerical values of Δ
T and Δ
H have the following relationships;
Δ
T>
−
0.1299(Δ
H)+62.81 for Δ
H greater than zero and up to 130 J/g,
Δ
T≧
48°
C. for Δ
H greater than 130 J/g,wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30°
C.;
or(c) is characterized by an elastic recovery, Re, in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/α
-olefin interpolymer, and has a density, d, in grams/cubic centimeter, wherein the numerical values of Re and d satisfy the following relationship when ethylene/α
-olefin interpolymer is substantially free of a cross-linked phase;
Re>
1481−
1629(d);
or(d) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content of at least 5 percent higher than that of a comparable random ethylene interpolymer fraction eluting between the same temperatures, wherein said comparable random ethylene interpolymer has the same comonomer(s) and has a melt index, density, and molar comonomer content (based on the whole polymer) within 10 percent of that of the ethylene/α
-olefin interpolymer;(e) has a storage modulus at 25°
C., G′
(25°
C.), and a storage modulus at 100°
C., G′
(100°
C.), wherein the ratio of G′
(25°
C.) to G′
(100°
C.) is in the range of about 1;
1 to about 9;
1;
or(f) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a block index of at least 0.5 and up to about 1 and a molecular weight distribution, Mw/Mn, greater than about 1.3;
or(g) has an average block index greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn, greater than about 1.3; and
optionally,a styrenic block copolymer, or a combination thereof wherein the ethylene/α
-olefin interpolymer has a density of from about 0.85 to about 0.885 g/cc.
-
-
22. A method for forming an elastic, breathable film/nonwoven layer laminate comprising:
-
filling a higher crystalline, predominantly linear polymer with a filler to form a filled polymer such that the filled polymer contains at least 60 percent by weight filler; dry-blending a thermoplastic elastomer with the filled polymer to form a blended elastomeric composition, such that the blended elastomeric composition includes between about 25 and 70 percent filler by weight, between about 5 and 30 percent higher crystalline polymer by weight, and between about 15 and 60 percent by weight elastomer; extruding the blended elastomeric composition into a film; and
,bonding the film to a nonwoven layer to produce a film/nonwoven layer laminate wherein the elastomer comprises at least one ethylene/α
-olefin interpolymer, wherein the ethylene/α
-olefin interpolymer(a) has a Mw/Mn from about 1.7 to about 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, wherein the numerical values of Tm and d correspond to the relationship;
Tm>
−
2002.9+4538.5(d)−
2422.2(d)2;
or(b) has a Mw/Mn from about 1.7 to about 3.5, and is characterized by a heat of fusion, Δ
H in J/g, and a delta quantity, Δ
T, in degrees Celsius defined as the temperature difference between the tallest DSC peak and the tallest CRYSTAF peak, wherein the numerical values of Δ
T and Δ
H have the following relationships;
Δ
T>
−
0.1299(Δ
H)+62.81 for Δ
H greater than zero and up to 130 J/g,Δ
T≧
48°
C. for Δ
H greater than 130 J/g,wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30°
C.;
or(c) is characterized by an elastic recovery, Re, in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/α
-olefin interpolymer, and has a density, d, in grams/cubic centimeter, wherein the numerical values of Re and d satisfy the following relationship when ethylene/α
-olefin interpolymer is substantially free of a cross-linked phase;
Re>
1481−
1629(d);
or(d) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content of at least 5 percent higher than that of a comparable random ethylene interpolymer fraction eluting between the same temperatures, wherein said comparable random ethylene interpolymer has the same comonomer(s) and has a melt index, density, and molar comonomer content (based on the whole polymer) within 10 percent of that of the ethylene/α
-olefin interpolymer;(e) has a storage modulus at 25°
C., G′
(25°
C.), and a storage modulus at 100°
C., G′
(100°
C.), wherein the ratio of G′
(25°
C.) to G′
(100°
C.) is in the range of about 1;
1 to about 9;
1;
or(f) has a molecular fraction which elutes between 40°
C. and 130°
C. when fractionated using TREF, characterized in that the fraction has a block index of at least 0.5 and up to about 1 and a molecular weight distribution, Mw/Mn, greater than about 1.3;
or(g) has an average block index greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn, greater than about 1.3; and
optionally,a styrenic block copolymer, or a combination thereof wherein the ethylene/α
-olefin interpolymer has a density of from about 0.85 to about 0.885 g/cc.- View Dependent Claims (23)
-