EMBOSSED GLASS ARTICLES FOR ANTI-FINGERPRINTING APPLICATIONS AND METHODS OF MAKING

• US 20100279068A1
• Filed: 11/24/2009
• Published: 11/04/2010
• Est. Priority Date: 05/04/2009
• Status: Abandoned Application

• Current Assignee: Corning Incorporated
• Original Assignee: Corning Incorporated
• Inventors: St. Clair, Todd Parrish, Cook, Glen Bennett, Senaratne, Wageesha
• Application Number:
  US12/624,978
• Publication Number:
  US 20100279068A1
• Time in Patent Office: Days
• US Class Current: 428/141
• CPC Class Codes: C03B 23/26 Punching reheated glass
• CPC Class Codes: C03C 15/00 Surface treatment of glass, not in the form of fibres or filaments, by etching etching or surface-brightening compositions, in general C09K13/00
• CPC Class Codes: C03C 17/23 Oxides C03C17/02 takes precedence
• CPC Class Codes: C03C 17/42 at least one coating of an organic material and at least one non-metal coating
• CPC Class Codes: C03C 19/00 Surface treatment of glass, not in the form of fibres or filaments, by mechanical means sand-blasting, grinding, or polishing glass B24
• CPC Class Codes: C03C 21/002 to perform ion-exchange between alkali ions C03C21/005 takes precedence
• CPC Class Codes: C03C 2204/08 Glass having a rough surface
• CPC Class Codes: C03C 2217/42 consisting of particles only
• CPC Class Codes: C03C 2217/75 Hydrophilic and oleophilic coatings
• CPC Class Codes: C03C 2217/76 Hydrophobic and oleophobic coatings
• CPC Class Codes: C03C 3/083 containing aluminium oxide or an iron compound
• CPC Class Codes: C03C 3/091 containing aluminium
• CPC Class Codes: Y10T 428/24355 Continuous and nonuniform or irregular surface on layer or component [e.g., roofing, etc.]
• CPC Class Codes: Y10T 428/24479 including variation in thickness
• CPC Class Codes: Y10T 428/24612 Composite web or sheet

Abstract

A process for creating hydrophobic and oleophobic glass surfaces. The process consists of heating a glass article to temperatures near the glass softening point and pressing a textured mold into the glass article to create surface texture. The mold texture is selected to have dimensions that convey hydrophobicity and oleophobicity to the glass article when combined with appropriate surface chemistry. The surface features are controlled through choice of mold texture and through process parameters including applied pressure, temperature, and pressing time. Articles made by this process are also described.

Claims

1. A glass article, the glass article comprising at least one embossed surface, the embossed surface having a texture and exhibiting at least one of hydrophobic and oleophobic behavior.

2. The glass article of claim 1, wherein the glass article further comprises a coating disposed on the embossed surface, the coating comprising at least one of a fluoropolymer and a fluorosilane.

3. The glass article of claim 2, wherein the embossed surface coated with the coating has a water contact angle that is greater than or equal to about 110°

.

4. The glass article of claim 2, wherein the embossed surface coated with the coating has an oil contact angle that is greater than about 90°

.

5. The glass article of claim 1, wherein the embossed surface further comprises a refractory material other than glass embedded in the embossed surface.

6. The glass article of claim 5, wherein the refractory material comprises nanoparticles of at least one metal oxide.

7. The glass article of claim 6, wherein the at least one metal oxide is selected from the group consisting of zinc oxide, tin oxide, alumina, ceria, titania, silica, and combinations thereof.

8. The glass article of claim 1, wherein the embossed surface comprises a negative structure.

9. The glass article of claim 1 wherein the embossed surface has multiple levels of surface roughness.

10. The glass article of claim 1, wherein the glass article is an alkali aluminosilicate glass.

11. The glass article of claim 10, wherein the alkali aluminosilicate glass comprises:

60-72 mol % SiO₂;

9-16 mol % Al₂O₃;

5-12 mol % B₂O₃;

8-16 mol % Na₂O; and

0-4 mol % K₂O, wherein the ratio

12. The glass article according to claim 10, wherein the alkali aluminosilicate glass comprises:

61-75 mol % SiO₂;

7-15 mol % Al₂O₃;

0-12 mol % B₂O₃;

9-21 mol % Na₂O;

0-4 mol % K₂O;

0-7 mol % MgO; and

0-3 mol % CaO.

13. The glass article according to claim 10, wherein the alkali aluminosilicate glass comprises:

60-70 mol % SiO₂;

6-14 mol % Al₂O₃;

0-15 mol % B₂O₃;

0-15 mol % Li₂O;

0-20 mol % Na₂O;

0-10 mol % K₂O;

0-8 mol % MgO;

0-10 mol % CaO;

0-5 mol % ZrO₂;

0-1 mol % SnO₂;

0-1 mol % CeO₂;

less than 50 ppm As₂O₃; and

less than 50 ppm Sb₂O₃;

wherein 12 mol %≦

Li₂O+Na₂O+K₂O≦

20 mol % and 0 mol %≦

MgO+CaO≦

10 mol %.

14. The glass article of claim 10, wherein the glass is thermally or chemically strengthened.

15. The glass article of claim 14, wherein the glass is chemically strengthened by ion exchange.

16. The glass article of claim 1, wherein the glass article has a haze of less than about 10%.

17. The glass article of claim 1, wherein the glass article has a haze in a range from about 10% up to about 50%.

18. The glass article of claim 1, wherein the glass article is one of a touch screen, a protective cover glass for a hand-held electronic device, an information-related terminal, and a touch sensor device.

19. A glass substrate, the glass substrate comprising an embossed surface having a roughness that is sufficient to prevent a decrease in contact angle of droplets of water or oils on the embossed surface.

20. A method of making a glass article having a surface that exhibits at least one of hydrophobic and oleophobic behavior, the method comprising the steps of:

a. providing the glass article; and

b. embossing at least one surface of the glass article to form at least one embossed surface, wherein the embossed surface has a texture and exhibits at least one of hydrophobic and oleophobic behavior.

21. The method of claim 20, wherein the step of embossing the at least one surface comprises:

a. contacting the at least one surface with a textured surface of a mold;

b. heating the glass article to a temperature at which the glass article has a viscosity in a range from about 10⁵ poise to 10⁸ poise while the glass article contacts the textured surface; and

c. applying pressure to the at least one surface and the textured surface to form the at least one embossed surface.

22. The method of claim 20, wherein the step of embossing at least one surface comprises:

a. contacting the at least one surface with a plurality of particles of at least one refractory material;

b. heating the glass article to a temperature at which the glass article has a viscosity in a range from about 10⁵ poise to 10⁸ poise while the glass article contacts the refractory material; and

c. pressing the plurality of particles into the at least one surface to form the embossed surface.

23. The method of claim 20, further comprising depositing a coating comprising at least one of a fluoropolymer and a fluorosilane on the at least one embossed surface, wherein the coating enhances at least one of hydrophobic and oleophobic behavior of the embossed surface.

24. The method of claim 20, further comprising the step of etching the embossed surface to form negative features in the embossed surface.

25. The method of claim 20, wherein the textured surface of the mold comprises at least one of glassy carbon, graphite, silicon nitride, silica, silicon, and a nickel-based alloy.