SOLAR ENERGY REFLECTOR

• US 20110017202A1
• Filed: 12/19/2008
• Published: 01/27/2011
• Est. Priority Date: 12/21/2007
• Status: Active Grant

• Current Assignee: AGC Glass Europe SA (AGC, Inc.)
• Original Assignee: AGC Glass Europe SA (AGC, Inc.)
• Inventors: Ventelon, Lionel, Cosijns, Bruno, Bouesnard, Olivier
• Granted Patent: US 9,322,575 B2
• Time in Patent Office: Days
• US Class Current: 126/684
• CPC Class Codes: F24S 23/77 with flat reflective plates
• CPC Class Codes: F24S 23/82 characterised by the material or the construction of the reflector
• CPC Class Codes: F24S 70/30 Auxiliary coatings, e.g. anti-reflective coatings
• CPC Class Codes: F24S 80/20 Working fluids specially adapted for solar heat collectors
• CPC Class Codes: G02B 5/0808 having a single reflecting layer G02B5/0883, G02B5/0891 take precedence
• CPC Class Codes: Y02E 10/40 Solar thermal energy, e.g. solar towers

Abstract

A solar energy reflector (1) comprises a mirror (5) with no copper layer laminated to a supporting sheet (7) by means of a bonding material (6). The edges of the mirror (5) are provided, at least on a portion forming the major part of their height and closest to the metallic sheet, with an edge protection (8) made of a material comprising silicone, polyurethane and/or acrylic and the material forming the edge protection (8) is different from the bonding material (6).

Claims

1. A solar energy reflector comprising a mirror with no copper layer laminated to a supporting sheet by a bonding material, wherein the edges of the mirror are provided, at least on a portion forming the major part of their height and closest to the supporting sheet, with an edge protection made of a material comprising at least one of the group consisting of silicone, polyurethane and acrylic, and wherein the material forming the edge protection is different from the bonding material.

2. A solar energy reflector according to claim 1, wherein the material forming the edge protection consists essentially of silicone.

3. A solar energy reflector according to claim 1, wherein the mirror comprises a glass substrate, a silver coating layer provided at a surface of the glass substrate and at least one paint layer covering the silver coating layer.

4. A solar energy reflector according to claim 3, wherein the mirror is laminated to the supporting sheet so that the at least one paint layer is facing the supporting sheet.

5. A solar energy reflector according to claim 1, wherein the bonding material comprises an acrylic resin.

6. A solar energy reflector according to claim 5, wherein the bonding material comprises an acrylic pressure-sensitive adhesive.

7. A solar energy reflector according to claim 1, wherein the bonding material comprises at least one film of the group consisting of an acetate-based polymer film, a PVB film, an ionomer-based film and a TPU film.

8. A solar energy reflector according to claim 1, wherein the edges of the mirror are provided substantially on their total height with the edge protection.

9. A solar energy reflector comprising a mirror with no copper layer laminated to a supporting sheet by means of a bonding material, wherein the reflector has an average edge corrosion of less than 50 μ

m after having been subjected to a 15 days CASS test.

10. A solar energy reflector according to claim 10, wherein the edges of the mirror are provided, at least on a portion forming the major part of their height and closest to the supporting sheet, with an edge protection made of a material which is different from the bonding material.

11. A method for manufacturing a solar energy reflector comprising:

a) laminating a mirror with no copper layer comprising a glass substrate, a silver coating layer provided at a surface of the glass substrate and at least one paint layer covering the silver coating layer to a supporting sheet by means of a bonding material

b) applying to the edges of the mirror, at least against the glass/silver and silver/paint interfaces, an edge protection made of a material which is different from the bonding material and which, at the time it is applied on the edges of the mirror, has a viscosity with at least one of the following values;

i. extrusion rate greater than or equal to 50 g/min when measured according to method A as herein defined

ii. extrusion rate greater than or equal to 5 g/min when measured according to method B as herein defined

iii. viscosity less than or equal to 800 Pa·

s when measured according to method C as herein defined

iv. melt flow index greater than or equal to 30 ml/10 min when measured according to method D as herein defined

v. extrusion rate greater than or equal to 60 g/min when measured according to method E as herein defined.

12. A method according to claim 11, wherein the viscosity of the bonding material, at the time it is applied on the edges of the mirror, has at least one of the following values:

i. extrusion rate greater than or equal to 100 g/min when measured according to method A as herein defined

ii. extrusion rate greater than or equal to 10 g/min when measured according to method B as herein defined

iii. viscosity less than or equal to 700 Pa·

s when measured according to method C as herein defined

iv. melt flow index greater than or equal to 50 ml/10 min when measured according to method D as herein defined

v. extrusion rate greater than or equal to 180 g/min when measured according to method E as herein defined.

13. A method according to claim 11, wherein the edge protection is applied to the edges of the mirror on at least a portion forming the major part of their height.

14. A method according to claim 11, wherein the edge protection is applied by extrusion.