Graphene-Enhanced cathode materials for lithium batteries

• US 20120058397A1
• Filed: 09/07/2010
• Published: 03/08/2012
• Est. Priority Date: 09/07/2010
• Status: Active Grant

• Current Assignee: Honeycomb Battery Co. (Global Graphene Group, Inc.)
• Original Assignee: Nanotek Instruments, Inc.
• Inventors: Zhamu, Aruna, Shi, Jinjun, Jang, Bor Z., Chen, Guorong, Wang, Ming C.
• Granted Patent: US 8,691,441 B2
• Time in Patent Office: Days
• US Class Current: 429/231.8
• CPC Class Codes: B82Y 30/00 Nanotechnology for materials or surface science, e.g. nanocomposites
• CPC Class Codes: H01B 1/24 the conductive material comprising carbon-silicon compounds, carbon or silicon
• CPC Class Codes: H01M 4/13 Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
• CPC Class Codes: H01M 4/139 Processes of manufacture
• CPC Class Codes: H01M 4/366 as layered products
• CPC Class Codes: H01M 4/587 for inserting or intercalating light metals
• CPC Class Codes: H01M 4/625 Carbon or graphite
• CPC Class Codes: Y02E 60/10 Energy storage using batteries

Abstract

A nano graphene-enhanced particulate for use as a lithium battery cathode active material, wherein the particulate is formed of a single or a plurality of graphene sheets and a plurality of fine cathode active material particles with a size smaller than 10 μm (preferably sub-micron or nano-scaled), and the graphene sheets and the particles are mutually bonded or agglomerated into an individual discrete particulate with at least a graphene sheet embracing the cathode active material particles, and wherein the particulate has an electrical conductivity no less than 10⁻⁴ S/cm and the graphene is in an amount of from 0.01% to 30% by weight based on the total weight of graphene and the cathode active material combined.

Claims

1. A nano graphene-enhanced particulate for use as a lithium battery cathode active material, wherein said particulate is formed of a single or a plurality of graphene sheets and a plurality of fine cathode active material particles with a size smaller than 10 μ

m, and the graphene sheets and the particles are mutually bonded or agglomerated into said particulate with a graphene sheet embracing said cathode active material particles, and wherein said particulate has an electrical conductivity no less than 10<sup>−

4</sup> S/cm and said graphene is in an amount of from 0.01% to 30% by weight based on the total weight of graphene and the cathode active material combined.

2. The particulate of claim 1 wherein the graphene amount is from 0.1% to 20% by weight of the total weight of graphene and the cathode active material combined.

3. The particulate of claim 1 wherein the graphene amount is from 0.5% to 10% by weight of the total weight of graphene and the cathode active material combined.

4. The particulate of claim 1 wherein said particulate has an electrical conductivity greater than 10⁻

2 S/cm.

5. The particulate of claim 1 wherein said particulate is spherical in shape.

6. The particulate of claim 1 wherein said graphene comprises single-layer graphene or few-layer graphene, wherein said few-layer graphene is defined as a graphene platelet formed of less than 10 graphene planes.

7. The particulate of claim 1, wherein said cathode active material is selected from the group consisting of lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphates, metal sulfides, and combinations thereof.

8. The particulate of claim 1, wherein said cathode active material particles in a particulate have a dimension smaller than 1 μ

m.

9. The particulate of claim 1, wherein said cathode active material particles in a particulate have a dimension smaller than 100 nm.

10. The particulate of claim 1, wherein said cathode active material is selected from the group consisting of lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphates, and combinations thereof and wherein said cathode active material contains sub-micron or nano-scaled particles with a size less than 1 μ

m.

11. The particulate of claim 1, wherein said cathode active material is selected from the group consisting of lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphates, and combinations thereof and wherein said cathode active material contains sub-micron or nano-scaled particles with a size less than 100 nm.

12. The particulate of claim 1, further comprising a carbon material in electronic contact with said cathode active material and a graphene sheet.

13. The particulate of claim 1, further comprising a carbon material coated on at least one of said cathode active material particles, wherein said carbon material is selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, carbon black, acetylene black, activated carbon, fine expanded graphite particle with a dimension smaller than 100 nm, artificial graphite particle, natural graphite particle, or a combination thereof.

14. The particulate of claim 1, wherein said particulate is prepared from a process comprising:

(a) Preparing a precursor mixture of graphene or graphene precursor with a cathode active material or active material precursor; and

(b) Thermally and/or chemically converting said precursor mixture to said graphene-enhanced cathode particulate.

15. The particulate of claim 14, wherein said step of preparing a precursor mixture comprises preparing a suspension of graphene or graphene precursor in a liquid medium and mixing a cathode active material or active material precursor in said suspension to form a multi-component suspension.

16. The particulate of claim 15, wherein the process further comprises a step of drying said multi-component suspension to form said precursor mixture.

17. The particulate of claim 15, wherein the process further comprises a step of drying said multi-component suspension to form said precursor mixture using a spray-drying, spray-pyrolysis, or fluidized-bed drying procedure.

18. The particulate of claim 14, wherein said step of converting comprises a sintering, heat-treatment, spray-pyrolysis, or fluidized bed drying or heating procedure.

19. The particulate of claim 14, wherein said step of converting comprises a procedure of chemically or thermally reducing said graphene precursor to reduce or eliminate oxygen content and other non-carbon elements of said graphene precursor.

20. The particulate of claim 1, wherein said graphene precursor contains graphene oxide or graphene fluoride.

21. The particulate of claim 1 wherein said graphene in said particulate has an oxygen content less than 25% by weight.

22. The particulate of claim 1 wherein said graphene in said particulates has an oxygen content less than 5% by weight.

23. The particulate of claim 1 wherein said graphene in said particulates has an oxygen content in the range of 5% to 25% by weight.

24. The particulate of claim 14, wherein said step of preparing said precursor mixture comprises:

A) dispersing or exposing a laminar graphite material in a fluid of an intercalant and/or an oxidant to obtain a graphite intercalation compound (GIC) or graphite oxide (GO);

B) exposing the resulting GIC or GO to a thermal shock at temperature for a period of time sufficient to obtain exfoliated graphite or graphite worms;

C) dispersing the exfoliated graphite or graphite worms in a liquid medium containing an acid, an oxidizing agent, and/or an organic solvent at a desired temperature for a duration of time until the exfoliated graphite is converted into a graphene oxide dissolved in the liquid medium to form a graphene solution; and

D) adding a desired amount of said cathode precursor material to said graphene solution to form said precursor mixture in a suspension, slurry or paste form.

25. The particulate of claim 14, wherein said step of preparing said precursor mixture comprises:

(a) preparing a suspension containing pristine nano graphene platelets (NGPs) dispersed in a liquid medium;

(b) adding an acid and/or an oxidizing agent into said suspension at a temperature for a period of time sufficient to obtain a graphene solution or suspension; and

(c) adding a desired amount of cathode active material or precursor in the graphene solution or suspension to form a paste or slurry.

26. A lithium battery cathode comprising multiple nano graphene-enhanced cathode particulates of claim 1.

27. A lithium battery cathode comprising multiple nano graphene-enhanced cathode particulates of claim 13.

28. A lithium battery cathode comprising multiple nano graphene-enhanced cathode particulates of claim 1, wherein said multiple particulates are packed together with graphene sheets forming a three-dimensional electron-conducting pathway.

29. A lithium battery cathode comprising multiple nano graphene-enhanced cathode particulates of claim 13, wherein said multiple particulates are packed together with graphene sheets and said carbon material together forming a three-dimensional electron-conducting pathway.

30. A lithium battery comprising an anode, a cathode of claim 26, a separator disposed between the anode and the cathode, and electrolyte in physical contact with both the anode and the cathode.

31. A lithium battery comprising an anode, a cathode of claim 27, a separator disposed between the anode and the cathode, and electrolyte in physical contact with both the anode and the cathode.

32. A lithium battery comprising an anode, a cathode of claim 28, a separator disposed between the anode and the cathode, and electrolyte in physical contact with both the anode and the cathode.

33. A lithium battery comprising an anode, a cathode of claim 29, a separator disposed between the anode and the cathode, and electrolyte in physical contact with both the anode and the cathode.