PROCESS FOR PRODUCING NEGATIVE PLATE FOR LEAD STORAGE BATTERY, AND LEAD STORAGE BATTERY

• US 20120094174A1
• Filed: 03/19/2010
• Published: 04/19/2012
• Est. Priority Date: 04/23/2009
• Status: Active Grant

• Current Assignee: Commonwealth Scientific & Industrial Research Organisation (Commonwealth Of Australia As Represented By Department Of Industry, Innovation, Climate Change, Science, Research And Tertiary Education), Furukawa Battery Company Limited (Furukawa Electric Company Limited)
• Original Assignee: Furukawa Battery Company Limited (Furukawa Electric Company Limited)
• Inventors: Furukawa, Jun, Takada, Toshimichi, Momma, Daisuke, Lam, Trieu Lan, Louey, Rosalie, Haigh, Peter Nigel
• Granted Patent: US 9,450,232 B2
• Time in Patent Office: Days
• US Class Current: 429/204
• CPC Class Codes: H01M 10/06 Lead-acid accumulators semi-lead accumulators H01M10/20
• CPC Class Codes: H01M 2004/027 Negative electrodes
• CPC Class Codes: H01M 4/0416 involving impregnation with a solution, dispersion, paste or dry powder H01M4/0438 takes precedence
• CPC Class Codes: H01M 4/0445 Forming after manufacture of the electrode, e.g. first charge, cycling
• CPC Class Codes: H01M 4/0452 from solutions
• CPC Class Codes: H01M 4/20 of pasted electrodes
• CPC Class Codes: H01M 4/22 Forming of electrodes
• CPC Class Codes: H01M 4/366 as layered products
• CPC Class Codes: H01M 4/622 being polymers
• CPC Class Codes: H01M 4/623 fluorinated polymers
• CPC Class Codes: H01M 4/625 Carbon or graphite
• CPC Class Codes: Y02E 60/10 Energy storage using batteries
• CPC Class Codes: Y02P 70/50 Manufacturing or production processes characterised by the final manufactured product

Abstract

To provide a method for producing a lead-acid battery negative plate for use in a storage battery which provides improved deteriorated rapid discharge characteristics by preventing an interfacial separation between a negative active material-filled plate and a carbon mixture-coated layer, which is a problem in a negative plate having such a configuration that the carbon mixture coated layer is formed on the surface of the negative active material-filled plate.

A coating layer of a carbon mixture is formed at least in a part of a surface of a negative active material-filled plate. The carbon mixture is prepared by mixing two kinds of carbon materials consisting of a first carbon material having conductive properties and a second carbon material having capacitive capacitance and/or pseudo capacitive capacitance and a binding agent. Subsequently, a sufficient amount of lead ions are generated enough to be moved from the negative active Material-filled plate into the carbon mixture-coated layer. Thereafter, a formation treatment or an initial charge treatment is performed to precipitate lead so that the carbon mixture-coated layer and the negative plate are connected and integrated, at least in a part of a respective interfacial surface thereof, by the precipitated lead.

Claims

1. A method for producing a negative plate for use in a lead-acid battery, comprising the steps of:

forming a coating layer of a carbon mixture at least in a part of a surface of a negative active material-filled plate, the carbon mixture being prepared by mixing two kinds of carbon materials consisting of a first carbon material having conductive properties and a second carbon material having capacitive capacitance and/or pseudo capacitive capacitance and a binding agent;

generating lead ions in an amount sufficient to enable movement of lead ions from the negative active material-filled plate into the carbon mixture-coated layer by performing, before charging, at least one of a) soaking treatment of the plate in an electrolyte solution, and b) discharging treatment of the plate; and

performing a charge treatment to precipitate lead so that the carbon mixture-coated layer and the negative active material-filled plate are connected and integrated, by the precipitated lead at the region of the interface between the carbon mixture-coated layer and the negative active material-filled plate.

2. A negative plate or a lead-acid battery comprising the negative plate obtainable or produced according to claim 1.

3. The method of claim 1, wherein the step of forming the coating layer of the carbon mixture comprises an air drying step such that porosity is introduced into the coating layer and the negative active material is at least partially oxidised.

4. The method of claim 1, wherein the soaking treatment of step a) is carried out for about one hour.

5. The method of claim 1, wherein the discharging treatment of step b) is carried out for about 30 hours.

6. The method of claim 1, wherein the step of generating lead ions consists of the soaking treatment and the discharging treatment.

7. The method of claim 1, wherein the carbon mixture is provided in an amount of 1-15 parts per 100 parts of active battery material.

8. The method of claim 1, wherein the porosity of the coating layer of the carbon mixture is 40-90%.

9. The method of claim 1, wherein the composition of the carbon mixture comprises 5-70 parts by weight of the first carbon material, 20-80 parts by weight of the second carbon material, 1-20 parts by weight of a binding agent, 0-10 parts by weight of a thickening agent, 0-16 parts by weight of a short fibre reinforcing agent.

10. The method of claim 9, wherein the composition of the carbon mixture comprises 10-60 parts by weight of the first carbon material.

11. The method of claim 9, wherein the composition of the carbon mixture comprises 30-70 parts by weight of the second carbon material.

12. The method of claim 9, wherein the composition of the carbon mixture comprises 5-15 parts by weight of the binding agent.

13. The method of claim 9, wherein for the composition:

the first carbon material is selected from at least one of carbon black, Ketjen black and graphite;

the second carbon material is selected from at least one of activated carbon, carbon black and graphite;

the binding agent is a polymer selected from at least one of polychloroprene, styrene-butadiene, polytetrafluoroethylene, and polyvinylidene fluoride;

the thickening agent, when present, is selected from an aqueous paste agent or an organic paste agent;

the short fibre reinforcing agent, when present, is selected from at least one of carbon, glass, polyethyleneterephthalate, and polytetrafluoroethylene.

14. The method of claim 9, wherein the reinforcing agent, when present, comprises fibres having a diameter of 20 um or less and a length of between 0.1 to 4 mm.