RESIN COMPOSITION AND USE THEREOF
First Claim
1. An optical element which is obtained by molding a thermoplastic resin composition comprising Polymer [A-1] represented by Formula (1), Compound [B-1], and Compound [B-2], wherein the total amount of Compound [B-1] and Compound [B-2] included is from 0.3 to 5 parts by mass relative to 100 parts by mass of Polymer [A-1], and the mass ratio [B-1]/[B-2] is from 1/10 to 10/1:
0 Assignments
0 Petitions
Accused Products
Abstract
A resin composition suitable for an optical element in which the moldability, thermal resistance, mechanical strength, and low birefringence are not impaired, the deterioration is hardly generated although the laser light nearby the UV is used, change in the optical properties during the use are extremely small, particularly the light transmittance is maintained high, and a foreign substance is hardly deposited on a surface of the molded product such as an optical element. In addition, an optical element obtained by molding the resin composition, and an optical pickup device using the optical element. The thermoplastic resin composition contains the polymer having a specific structure and two kinds of specific optical stabilizers in a specific mass ratio among a hindered amine light stabilizer having the molecular weight of 400 to 5,000.
1 Citation
34 Claims
- 1. An optical element which is obtained by molding a thermoplastic resin composition comprising Polymer [A-1] represented by Formula (1), Compound [B-1], and Compound [B-2], wherein the total amount of Compound [B-1] and Compound [B-2] included is from 0.3 to 5 parts by mass relative to 100 parts by mass of Polymer [A-1], and the mass ratio [B-1]/[B-2] is from 1/10 to 10/1:
- 10. An optical element which is obtained by molding a thermoplastic resin composition comprising Polymer [A-1] represented by Formula (1), Compound [B-1], and Compound [B-2], wherein the total amount of Compound [B-1] and Compound [B-2] included is from 0.3 to 5 parts by mass relative to 100 parts by mass of Polymer [A-1], and the mass ratio [B-1]/[B-2] is from 1/10 to 10/1:
-
18. An optical element which is obtained by molding a thermoplastic resin composition comprising Polymer [A-2] which has an alicyclic structure on at least one moiety of repeated structural units, Compound [B-1], and Compound [B-2], wherein the total amount of Compound [B-1] and Compound [B-2] included is from 0.3 to 5 parts by mass relative to 100 parts by mass of Polymer [A-2], and the mass ratio [B-1]/[B-2] is from 1/10 to 10/1,
wherein, Compound [B-1] is a hindered amine light stabilizer having the molecular weight of 400 or more to less than 1,000, and Compound [B-2] is a hindered amine light stabilizer having the molecular weight of 1,000 or more to 5,000 or less.
-
27. An optical element which is obtained by molding a thermoplastic resin composition comprising Polymer [A-2] which has an alicyclic structure on at least one moiety of repeated structural units, Compound [B-1], and Compound [B-2], wherein the total amount of Compound [B-1] and Compound [B-2] included is from 0.3 to 5 parts by mass relative to 100 parts by mass of Polymer [A-2], and the mass ratio [B-1]/[B-2] is from 1/10 to 10/1,
wherein, Compound [B-1] is a hindered amine light stabilizer having the molecular weight of 400 or more to less than 1,000, and Compound [B-2] is a hindered amine light stabilizer having the molecular weight of 1,000 or more to 5,000 or less, and wherein the optical element is used as an optical component useful for a laser optical system having the wavelength of 350 to 450 nm.
Specification