FABRICATION OF MIRROR-LIKE COATINGS

• US 20120295121A1
• Filed: 05/11/2012
• Published: 11/22/2012
• Est. Priority Date: 05/20/2011
• Status: Abandoned Application

• Current Assignee: S.T. Trading Company Limited (S.T. Corporation)
• Original Assignee: S.T. Trading Company Limited (S.T. Corporation)
• Inventors: Miao, Jianying, Li, Wei, Ng, Shing Hang, Keung, Lok Hang, Gong, Tao
• Application Number:
  US13/469,605
• Publication Number:
  US 20120295121A1
• Time in Patent Office: Days
• US Class Current: 428/450
• CPC Class Codes: B05D 2202/00 Metallic substrate
• CPC Class Codes: B05D 2420/01 first layer from the substrate side
• CPC Class Codes: B05D 2504/00 Epoxy polymers
• CPC Class Codes: B05D 5/068 achieved by multilayers B05D5/066 takes precedence
• CPC Class Codes: B05D 7/56 Three layers or more
• CPC Class Codes: C23C 18/1689 After-treatment
• CPC Class Codes: C23C 18/1844 with use of organic or inorganic compounds other than metals, first
• CPC Class Codes: C23C 18/44 using reducing agents

Abstract

Multi-layer coatings suitable for imparting a decorative, durable mirror-like finish to substrates such as metals are provided which contain a base coating of epoxy, a mirror-like coating, and a scratch-resistant surface coating.

Claims

1. A method of providing a substrate with a multi-layer coating, the method comprising the steps of:

a) forming a base coating comprised of epoxy on a surface of the substrate;

b) forming a decorative mirror-like coating on the base coating by reacting an amine complex of silver, a reducing sugar and an acetylenic compound; and

c) forming a surface coating on the decorative mirror-like coating which is capable of protecting the decorative mirror-like coating against scratching.

2. The method of claim 1, wherein the substrate is selected from the group consisting of metal substrates.

3. The method of claim 1, comprising an additional step prior to step a) of pretreating the surface of the substrate.

4. The method of claim 3, wherein the additional step comprises contacting the surface of the substrate with one or more silanes.

5. The method of claim 1, wherein the base coating is formed by reaction of an epoxy resin with a solidifier.

6. The method of claim 5, wherein the epoxy resin is a glycidyl ether of bisphenol A.

7. The method of claim 1, wherein the base coating is additionally comprised of a leveling agent.

8. The method of claim 1, wherein the amine complex of silver is [Ag(NH₃)₂]⁺.

9. The method of claim 1, wherein the reducing sugar is glucose.

10. The method of claim 1, wherein the acetylenic compound is butynediol.

11. The method of claim 1, wherein the surface coating is based on one or more organic silicon-containing compounds.

12. The method of claim 11, wherein the organic silicon-containing compounds are selected from the group consisting of silanes, tetraalkyl silicates, alkylalkoxysilanes and mixtures thereof.

13. The method of claim 11, wherein the surface coating is obtained by combining at least one silane, at least one tetraalkyl silicate, at least one alkylalkoxysilane with water and acid to provide a surface coating composition, contacting the surface coating composition with the decorative mirror-like coating, and heating the substrate.

14. The method of claim 13, wherein the surface coating composition is additionally comprised of a violet dye.

15. The method of claim 1, wherein after step a) and before step b) the base coating is contacted with an acidic solution containing stannous ions.

16. The method of claim 1, comprising an additional step prior to step a) of polishing the surface of the substrate.

17. The method of claim 1, comprising an additional step prior to step a) of cleaning the surface of the substrate.

18. The method of claim 1, comprising an additional step after step a) and before step b) of contacting the base coating with one or more organic solvents selected from the group consisting of C1-C6 aliphatic alcohols and C3-C6 aliphatic ketones.

19. The method of claim 1, comprising an additional step after step b) and before step c) of contacting the mirror-like coating with a solution comprised of a thiol and a surfactant.

20. A method of providing a metal substrate with a multi-layer coating, the method comprising the steps of:

a) pretreating a surface of the metal substrate by contacting the surface with a silane;

b) forming a base coating on the pretreated surface by first forming a lower layer comprised of leveling agent and solidifier on the pretreated surface followed by an upper layer on top of the lower layer, the upper layer being comprised of reactive diluent, leveling agent and epoxy resin;

c) forming a decorative mirror-like coating on the base coating by contacting the base coating with a stannous ion-containing solution and then a mixture comprised of [Ag(NH₃)₂]⁺, glucose, carboxylic acid and butynediol;

d) forming a surface coating on the decorative mirror-like coating by contacting the decorative mirror-like coating with a surface coating composition obtained by at least one silane, at least one tetraalkyl silicate, at least one alkylalkoxysilane with water and acid, contacting the surface coating composition with the decorative mirror-like coating, and heating the substrate.

21. A substrate having a multi-layer coating on at least one surface, the multi-layer coating comprising a base coating comprised of cured epoxy, a decorative mirror-like coating comprised of silver on top of the base coating, and a surface coating comprised of polysilicone on top of the decorative mirror-like coating.