Method for preparing the matte anti-fingerprint stainless steel decorative plate

• US 20150267072A1
• Filed: 11/20/2014
• Published: 09/24/2015
• Est. Priority Date: 03/18/2014
• Status: Active Grant

• Current Assignee: Haimen Senda Decoration Material Co.,Ltd. (Wuchan Zhongda Geron Co., Ltd.)
• Original Assignee: Haimen Senda Decoration Material Co.,Ltd. (Wuchan Zhongda Geron Co., Ltd.)
• Inventors: HUANG, LIXIN, HONG, LIANG, SANG, ZHIHONG, CHEN, GANG, JIANG, HUI
• Granted Patent: US 9,227,223 B2
• Time in Patent Office: Days
• US Class Current: 1/1
• CPC Class Codes: B05D 1/02 performed by spraying
• CPC Class Codes: B05D 2202/15 Stainless steel
• CPC Class Codes: B05D 3/002 Pretreatement
• CPC Class Codes: B05D 3/0272 with ovens
• CPC Class Codes: B05D 5/06 to obtain multicolour or other optical effects B05D5/02 takes precedence
• CPC Class Codes: B05D 5/08 to obtain an anti-friction or anti-adhesive surface rendering particulate materials free-flowing in general, e.g. making them hydrophobic B01J2/30
• CPC Class Codes: B05D 7/16 using synthetic lacquers or varnishes
• CPC Class Codes: B08B 17/06 by giving articles subject to fouling a special shape or arrangement
• CPC Class Codes: B44C 1/00 Processes, not specifically provided for elsewhere, for producing decorative surface effects decorating textiles D06Q
• CPC Class Codes: B44C 5/0415 containing metallic elements
• CPC Class Codes: C08K 3/00 Use of inorganic substances as compounding ingredients
• CPC Class Codes: C08L 2205/03 containing three or more polymers in a blend
• CPC Class Codes: C08L 63/00 Compositions of epoxy resins; Compositions of derivatives of epoxy resins
• CPC Class Codes: C08L 79/00 Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen with or without oxygen or carbon only, not provided for in groups C08L61/00 - C08L77/00
• CPC Class Codes: C09D 133/08 Homopolymers or copolymers of acrylic acid esters

Abstract

The present invention provides a method for preparing a matte anti-fingerprint stainless steel decorative plate. The method comprises the steps of: 1) selecting a polymer coating material, wherein the polymer coating material is formed by mixing acrylic resin, a film forming material, an inorganic nano-filler, a solvent and an auxiliary agent, wherein the film forming material comprises the following ingredients based on the weight ratio: 30-50 parts of acrylate composite resin, 5-20 parts of amino resin, 5-15 parts of epoxy resin, 1-5 parts of an inorganic nano-filler, 40-50 parts of a solvent and 10-20 parts of an auxiliary agent; and 1-8 parts of a matting agent and 1-8 parts of an anti-settling agent are added; and 2) performing a spray coating using the polymer coating material, wherein a coating film has a thickness of 1.5-2.5 μm, the precision of the atomization air pressure of a spray gun is controlled at ±0.1 bar during spray coating, and the coating is dried to obtain a finished product and then a matte anti-fingerprint stainless steel decorative plate which has a high-standard matte and anti-fingerprint index is prepared.

Claims

1. A method for preparing a matte anti-fingerprint stainless steel decorative plate, comprising:

1) selecting a polymer coating material, wherein the polymer coating material is formed by mixing acrylic resin, a film forming material, an inorganic nano-filler, a solvent and an auxiliary agent, and wherein the film forming material comprises the following ingredients based on the weight ratio;

30-50 parts of acrylate composite resin, 5-20 parts of amino resin, 5-15 parts of epoxy resin, 1-5 parts of an inorganic nano-filler, 40-50 parts of a solvent and 10-20 parts of an auxiliary agent; and

1-8 parts of a matting agent and 1-8 parts of an anti-settling agent are added;

2) performing a spray coating using the polymer coating material to form a coating film, wherein the coating film has a thickness of 1.5-2.5 μ

m, and a precision of the atomization air pressure of a spray gun is controlled at ±

0.1 bar during the spray coating; and

drying the coating is dried to obtain a finished product.

2. The method according to claim 1, further comprises:

pretreating before the spray coating step by washing the stainless steel plate by a neutral detergent, and rinsing the stainless steel plate with deionized water using ultrasonic wash.

3. The method according to claim 1, wherein the drying step further comprises,

drying the stainless steel plate in a drying oven placed in a clean environment, wherein the oven is equipped with high temperature-resistant high-efficiency filter at an air inlet and an air outlet of the air passage of the oven.