STEEL SHEET FOR THREE-PIECE CAN AND METHOD FOR MANUFACTURING THE SAME
First Claim
1. A steel sheet for a three-piece can, the steel sheet having a chemical composition containing, by mass %, C:
- 0.0005% or more and 0.0035% or less, Si;
0.050% or less, Mn;
more than 0.60% and 1.00% or less, P;
0.030% or less, S;
0.020% or less, Al;
0.010% or more and 0.100% or less, N;
0.0030% or less, B;
0.0005% or more, and the balance being Fe and inevitable impurities, wherein;
the relationship B/N≧
0.50 is satisfied (where B/N represents (B(mass %/10.81)/(N(mass %)/14.01)); and
a Young'"'"'s modulus in a direction at an angle of 90°
to the rolling direction is 220 GPa or more.
1 Assignment
0 Petitions
Accused Products
Abstract
Provided are a steel sheet for a can having high buckling strength for a can body against an external force and excellent formability when being formed into a shape having a design effect by additionally giving elongation strain in the circumferential direction after the steel sheet having been formed into a cylindrical shape and a method for manufacturing the steel sheet. The chemical composition is controlled to contain, by mass %, C: 0.0005% or more and 0.0035% or less, Si: 0.050% or less, Mn: more than 0.60% and 1.00% or less, P: 0.030% or less, S: 0.020% or less, Al: 0.010% or more and 0.100% or less, N: 0.0030% or less, B: 0.0005% or more, and the balance being Fe and inevitable impurities, in which the relationship B/N≧0.50 is satisfied where B/N represents
(B(mass %)/10.81)/(N(mass %)/14.01), and a Young'"'"'s modulus in a direction at an angle of 90° to the rolling direction is 220 GPa or more.
-
Citations
5 Claims
-
1. A steel sheet for a three-piece can, the steel sheet having a chemical composition containing, by mass %, C:
- 0.0005% or more and 0.0035% or less, Si;
0.050% or less, Mn;more than 0.60% and 1.00% or less, P;
0.030% or less, S;
0.020% or less, Al;
0.010% or more and 0.100% or less, N;
0.0030% or less, B;
0.0005% or more, and the balance being Fe and inevitable impurities, wherein;the relationship B/N≧
0.50 is satisfied (where B/N represents (B(mass %/10.81)/(N(mass %)/14.01)); anda Young'"'"'s modulus in a direction at an angle of 90°
to the rolling direction is 220 GPa or more. - View Dependent Claims (2, 3, 4)
- 0.0005% or more and 0.0035% or less, Si;
-
5. A method for manufacturing a steel sheet for a three-piece can, the method comprising:
-
performing hot rolling on a steel slab under a condition that the reheating temperature is higher than 1100°
C. and 1300°
C. or lower and that the final finish rolling temperature is 850°
C. or higher and lower than 950°
C., the steel slab having a chemical composition containing, by mass %, C;
0.0005% or more and 0.0035% or less, Si;
0.050% or less, Mn;
more than 0.60% and 1.00% or less, P;
0.030% or less, S;
0.020% or less, Al;
0.010% or more and 0.100% or less, N;
0.0030% or less, B;
0.0005% or more, and the balance being Fe and inevitable impurities, in which a relationship B/N≧
0.50 is satisfied where B/N represents (B(mass %)/10.81)/(N(mass %)/14.01);coiling the hot-rolled steel sheet at a temperature of 500°
C. or higher and lower than 650°
C.;pickling and thereafter cold rolling the coiled steel sheet with a rolling reduction of more than 92.0%; recrystallization annealing at a temperature of higher than 700°
C. and 800°
C. or lower using a continuous annealing process; andskin pass rolling the recrystallization annealed steel sheet with an elongation ratio of 0.5% or more and 5.0% or less.
-
Specification