NEGATIVE ELECTRODE ACTIVE MATERIAL, NEGATIVE ELECTRODE, LITHIUM ION SECONDARY BATTERY, METHOD FOR PRODUCING NEGATIVE ELECTRODE MATERIAL FOR NON-AQUEOUS ELECTROLYTE SECONDARY BATTERY AND METHOD FOR PRODUCING LITHIUM ION SECONDARY BATTERY

• US 20190140271A1
• Filed: 10/27/2016
• Published: 05/09/2019
• Est. Priority Date: 11/20/2015
• Status: Active Grant

• Current Assignee: Shin-Etsu Chemical Company Limited
• Original Assignee: Shin-Etsu Chemical Company Limited
• Inventors: HIROSE, Takakazu, KAMO, Hiromichi, YOSHIKAWA, Hiroki
• Granted Patent: US 10,811,681 B2
• Time in Patent Office: Days
• CPC Class Codes: C22C 19/03 based on nickel
• CPC Class Codes: C22C 9/00 Alloys based on copper
• CPC Class Codes: H01M 10/0525 Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
• CPC Class Codes: H01M 2004/027 Negative electrodes
• CPC Class Codes: H01M 4/13 Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
• CPC Class Codes: H01M 4/131 Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
• CPC Class Codes: H01M 4/134 Electrodes based on metals, Si or alloys
• CPC Class Codes: H01M 4/362 Composites
• CPC Class Codes: H01M 4/366 as layered products
• CPC Class Codes: H01M 4/386 Silicon or alloys based on silicon
• CPC Class Codes: H01M 4/483 for non-aqueous cells H01M4/485 takes precedence
• CPC Class Codes: H01M 4/625 Carbon or graphite
• CPC Class Codes: H01M 4/661 Metal or alloys, e.g. alloy coatings H01M4/669 take precedence
• CPC Class Codes: Y02E 60/10 Energy storage using batteries

Abstract

A negative electrode active material contains particles of negative electrode active material, wherein the particles of negative electrode active material contain a silicon compound represented by SiO_x (0.5≤x≤1.6), and when the particles of negative electrode active material are measured by an atom probe method, and an Si 75% equivalent concentration surface obtained by the atom probe method is defined to be a boundary surface of a silicon grain, an average diameter of the silicon grains at a center portion of the particle in the particles of negative electrode active material is in the range of 0.25 nm to 5 nm. According to this constitution, when it is used as the negative electrode active material of a secondary battery, a negative electrode active material is capable of increasing battery capacity and improving cycle characteristics.

Claims

1-16. -16. (canceled)

17. A negative electrode active material which comprises:

a negative electrode active material containing particles of negative electrode active material, wherein the particles of negative electrode active material contain a silicon compound represented by SiO_x (0.5≤

x≤

1.6), and when the particles of negative electrode active material are measured by an atom probe method and an Si 75% equivalent concentration surface obtained by the atom probe method is defined to be a boundary surface of a silicon grain, an average diameter of the silicon grains at a center portion of the particle in the particles of negative electrode active material is in the range of 0.25 nm to 5 nm.

18. The negative electrode active material according to claim 17, wherein a ratio A/B of a maximum length A and a minimum length B of the silicon grain is calculated, an average value of the ratio A/B of the silicon grains contained at a surface layer portion of the particle in the particles of negative electrode active material is larger than an average value of the ratio A/B of the silicon grains contained at a center portion of the particle in the particles of negative electrode active material.

19. The negative electrode active material according to claim 17, wherein the particles of negative electrode active material are measured by the atom probe method, silicon and oxygen each have a concentration distribution of 1 at % or more and 10 at % or less at the center portion of the particle in the particles of negative electrode active material.

20. The negative electrode active material according to claim 17, wherein the particles of negative electrode active material have a carbon material on a surface thereof.

21. The negative electrode active material according to claim 20, wherein an average thickness of the carbon material is 5 nm or more and 5,000 nm or less.

22. The negative electrode active material according to claim 17, wherein, when the particles of negative electrode active material are measured by the atom probe method, silicon and oxygen each have a concentration distribution of 10 at % or more in the depth direction at the surface layer portion of the particle in the particles of negative electrode active material.

23. The negative electrode active material according to claim 17, wherein, when the particles of negative electrode active material are measured by the atom probe method, a silicon concentration at the surface layer portion of the particle in the particles of negative electrode active material is higher than a silicon concentration at the center portion of the particle in the particles of negative electrode active material.

24. The negative electrode active material according to claim 17, wherein, when an aspect ratio of the silicon grain is calculated, an average value of the aspect ratio of the silicon grains contained in the surface layer portion of the particle in the particles of negative electrode active material is larger than an average value of the aspect ratio of the silicon grains contained in the center portion of the particle in the particles of negative electrode active material.

25. The negative electrode active material according to claim 17, wherein the negative electrode active material has a half value width (2θ

) of a diffraction peak attributable to a Si (111) crystal plane by X-ray diffraction of 1.2°

or more and has a crystallite size corresponding to the crystal face is 7.5 nm or less.

26. The negative electrode active material according to claim 17, wherein a median diameter of the particles of negative electrode active material is 1 μ

m or more and 15 μ

m or less.

27. A negative electrode which comprises:

a negative electrode active material layer containing the negative electrode active material according to claim 17, and

a negative electrode current collector,

wherein, the negative electrode active material layer is formed on the negative electrode current collector, and

the negative electrode current collector contains carbon and sulfur, and contents of which are each 100 ppm by mass or less.

28. The negative electrode according to claim 27, wherein a length of the silicon grains in the negative electrode active material is increased by repeating charge and discharge of the negative electrode.

29. A lithium ion secondary battery which comprises:

the negative electrode according to claim 27, wherein the negative electrode according to claim 27 is used as a negative electrode.

30. A method for producing a negative electrode material for a non-aqueous electrolyte secondary battery containing particles of negative electrode active material, which comprises:

preparing particles of negative electrode active material containing a silicon compound represented by the general formula;

SiO_x (0.5≤

x≤

1.6),

measuring the particles of negative electrode active material by an atom probe method,

when an Si 75% equivalent concentration surface obtained by the atom probe method is defined to be a boundary surface of a silicon grain, selecting particles of negative electrode active material having an average diameter of the silicon grains at a center portion of the particle in the particles of negative electrode active material of in the range of 0.25 nm to 5 nm, and

producing a negative electrode material for a non-aqueous electrolyte secondary battery using the selected particles of negative electrode active material.

31. The method for producing a negative electrode material for a non-aqueous electrolyte secondary battery according to claim 30, wherein the method further comprises forming a carbon material on a surface of the particles of negative electrode active material before the step of measuring.

32. A method for producing a lithium ion secondary battery which comprises producing a negative electrode by using the negative electrode material for a non-aqueous electrolyte secondary battery produced by the method for producing a negative electrode material for a non-aqueous electrolyte secondary battery according to claim 30, and producing a lithium ion secondary battery using the produced negative electrode.