Process for producing porous products

• US 3,953,566 A
• Filed: 07/03/1973
• Issued: 04/27/1976
• Est. Priority Date: 05/21/1970
• Status: Expired due to Term

• Current Assignee: W. L. Gore & Associates (W.L. Gore & Associates)
• Original Assignee: W. L. Gore & Associates (W.L. Gore & Associates)
• Inventors: Gore, Robert W.
• Primary Examiner(s): Woo, Jay H.
• Application Number:
  US05/376,188
• Time in Patent Office: 1,029 Days
• Field of Search: 260/29.6 F, 260/2.5, 264/191, 264/288, 264/290, 264/188, 264/184, 264/175
• US Class Current: 264/505
• CPC Class Codes: B01D 71/36 Polytetrafluoroethene
• CPC Class Codes: B29C 55/005 characterised by the choice of materials
• CPC Class Codes: B29C 55/12 biaxial
• CPC Class Codes: B29C 55/18 by squeezing between surfaces, e.g. rollers
• CPC Class Codes: B29K 2027/18 PTFE, i.e. polytetrafluorethene , e.g. ePTFE, i.e. expanded polytetrafluorethene
• CPC Class Codes: B29K 2105/04 cellular or porous
• CPC Class Codes: B32B 2038/0088 Expanding, swelling
• CPC Class Codes: B32B 2266/025 Polyolefin vinyl or acrylic copolymers B32B2266/0221, B32B2266/0242
• CPC Class Codes: B32B 2305/026 Porous
• CPC Class Codes: B32B 2307/54 Yield strength; Tensile strength
• CPC Class Codes: B32B 2307/702 Amorphous
• CPC Class Codes: B32B 5/18 characterised by features of a layer of foamed material
• CPC Class Codes: B32B 5/32 at least two layers being foamed and next to each other
• CPC Class Codes: C08J 2327/18 Homopolymers or copolymers of tetrafluoroethylene
• CPC Class Codes: C08J 5/124 using adhesives based on a macromolecular component
• CPC Class Codes: C08J 5/18 Manufacture of films or sheets
• CPC Class Codes: H01B 3/445 from vinylfluorides or other fluoroethylenic compounds
• CPC Class Codes: Y10S 264/70 Processes for forming screens or perforating articles
• CPC Class Codes: Y10S 384/902 Porous member
• CPC Class Codes: Y10S 55/05 Methods of making filter
• CPC Class Codes: Y10T 428/139 : Open-ended, self-supporting conduit, cylinder, or tube-type article
• CPC Class Codes: Y10T 428/1397 : Single layer [continuous layer]
• CPC Class Codes: Y10T 428/249978 : Voids specified as micro
• CPC Class Codes: Y10T 428/249994 : Composite having a component wherein a constituent is liquid or is contained within preformed walls [e.g., impregnant-filled, previously void containing component, etc.]
• CPC Class Codes: Y10T 428/25 : Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles
• CPC Class Codes: Y10T 428/251 : Mica
• CPC Class Codes: Y10T 428/252 : Glass or ceramic [i.e., fired or glazed clay, cement, etc.] [porcelain, quartz, etc.]
• CPC Class Codes: Y10T 428/254 : Polymeric or resinous material
• CPC Class Codes: Y10T 428/259 : Silicic material
• CPC Class Codes: Y10T 428/2913 : Rod, strand, filament or fiber
• CPC Class Codes: Y10T 428/31544 : Addition polymer is perhalogenated

Abstract

This invention provides a tetrafluoroethylene polymer in a porous form which has an amorphous content exceeding about 5% and which has a micro-structure characterized by nodes interconnected by fibrils. The material has high porosity and high strength. It can be used to produce all kinds of shaped articles such as films, tubes, rods, and continuous filaments. Laminations can be employed and impregnation and bonding can readily be used to produce a large variety of articles. Compressed articles of very high strength can also be produced from these porous forms.

Claims

1. A process for the production of a porous article of manufacture of a polymer of tetrafluoroethylene which process comprises expanding a shaped article consisting essentially of highly crystalline poly(tetrafluoroethylene) made by a paste-forming extrusion technique, after removal of lubricant, by stretching said unsintered shaped article at a rate exceeding about 10% per second and maintaining said shaped article at a temperature between about 35°

C. and the crystalline melt point of said tetrafluoroethylene polymer during said stretching.

2. The process of claim 1 in which the rate of stretch is about 30% per second.

3. The process of claim 1 in which the rate of stretch is about 100% per second.

4. The process of claim 1 in which the rate of stretch is about 500% per second.

5. The process of claim 1 in which the rate of stretch is about 1000% per second.

6. The process of claim 1 in which the rate of stretch is about 5000% per second.

7. The process of claim 1 in which the rate of stretch is about 10,000% per second.

8. The process of claim 1 in which the rate of stretch is about 40,000% per second.

9. A process in accordance with claim 1 in which said shaped article has an amorphous content not exceeding about 3.5%.

10. A process in accordance with claim 1 in which said expanding is effected by clamping said shaped article and rapidly forming a vacuum on one side of said article to rapidly stretch said shaped article.

11. A process in accordance with claim 1 in which said expanding is effected in only one direction.

12. A process in accordance with claim 1 in which said expanding is effected biaxially.

13. A process in accordance with claim 1 in which said expanding produces a porosity of about 40% to about 97% in said resultant, porous stretched article.

14. A process according to claim 1 including the step of compressing the resultant porous article.

15. The process of claim 1 in which said shaped article is expanded by rapidly creating a pressure differential across said shaped article to cause said shaped article to stretch.

16. The process of claim 1 in which the expanding step is effected at a temperature above about 93°

C.

17. The process of claim 1 in which the shaped article is expanded such that its final length in the direction of expansion is greater than about twice the original length.

18. The process of claim 17 in which said final length is greater than about three times the original length.

19. The process of claim 17 in which said final length is greater than about five times the original length.

20. The process of claim 17 in which said final length is greater than about seven times the original length.

21. The process of claim 17 in which said final length is about fifteen times the original length.

22. The process of claim 17 in which said final length is greater than about 24 times the original length.

23. A process in accordance with claim 1 which includes the subsequent step of heating the stretched-shaped article to a temperature above the crystalline melting temperature of said polymer.

24. The process of claim 23 in which said heating produces in said stretched-shaped article an increase in amorphous content exceeding about 1%.