Process for producing iron ore oxidized pellets from magnetite concentrate

• US 3,980,465 A
• Filed: 10/02/1974
• Issued: 09/14/1976
• Est. Priority Date: 10/02/1973
• Status: Expired due to Term

• Current Assignee: Kobe Steel Limited
• Original Assignee: Kobe Steel Limited
• Inventors: Takeda, Kunio, Nishida, Reijiro, Uchida, Kunio, Kaneko, Dentaro
• Primary Examiner(s): Rosenberg, Peter D.
• Application Number:
  US05/511,371
• Time in Patent Office: 713 Days
• Field of Search: 75/3-5, 75/41
• US Class Current: 75/322
• CPC Class Codes: C22B 1/2413 enduration of pellets

Abstract

Iron-ore oxidized pellets are produced from magnetite concentrate by the addition to the magnetite concentrate of at least one calcium compound selected from the group consisting of slaked lime, quicklime and limestone, to a basicity of 1 to 5, granulating the mixture thus prepared, drying the same, preheating the same at a temperature of from 1000° to 1150°C for 3 to 10 minutes, and thereafter firing the same.

Claims

1. A process for producing iron-ore oxidized pellets from magnetite concentrate, comprising the steps of:

adding to said magnetite concentrate at least one calcium compound selected from the group consisting of slaked lime, quicklime, limestone and mixtures thereof, to basicity of 1 to 5;

granulating the resulting mixture;

drying the same;

preheating the granules thus prepared at a temperature of 1000°

to 1150°

C for 3 to 10 minutes; and

firing the thus preheated granules.

2. The process for producing iron-ore oxidized pellets as defined in claim 1, wherein said preheating is carried out at a temperature of 1050°

to 1100°

C for 4 to 6 minutes.

3. The process for producing iron-ore oxidized pellets as defined in claim 2, wherein slaked lime is added as a calcium compound to a magnetite concentrate to a basicity of 1 to 2.

4. The process for producing iron-ore oxidized pellets, as defined in claim 1, wherein said calcium compound is quicklime.

5. The process for producing iron-ore oxidized pellets, as defined in claim 1, wherein said mixture is granulated to a grain size of 8 to 20 mm in diameter.

6. Iron-ore oxidized pellets produced by the process of claim 1.