Infrared reflecting articles

• US 4,179,181 A
• Filed: 04/03/1978
• Issued: 12/18/1979
• Est. Priority Date: 04/03/1978
• Status: Expired due to Term

• Current Assignee: Cabot Safety Intermediate Corporation et al
• Original Assignee: American Optical Corporation
• Inventors: Chang, Leei
• Primary Examiner(s): Hoffman, James R.
• Application Number:
  US05/892,585
• Time in Patent Office: 624 Days
• Field of Search: 427/160, 350/164, 350/166, 350/1.7
• US Class Current: 359/360
• CPC Class Codes: G02B 5/282 reflecting for infrared and transparent for visible light, e.g. heat reflectors, laser protection

Abstract

Articles having an interference coating which reflects infrared energy are disclosed. The coating has a period of three layers in which the first and third layers are a refractory dielectric material and the intermediate, or second layer, is silver. If the period is repeated once, the cut-off between transmission and reflection is sharper than the coating having a single period.

Claims

1. An interference-coated, infrared reflecting article comprising, in sequence,

(a) a substrate having a surface,

(b) a first layer of a refractory dielectric,

(c) a layer of silver having a thickness between about 110 and 250 A,

(d) a second layer of the refractory dielectric.

2. The article according to claim 1 wherein (b), (c) and (d) are repeated in sequence.

3. The article according to claim 2 wherein (b) and (d) are SiO_x.

4. The article according to claim 2 wherein (a) is a synthetic resin, selected from the group consisting of polycarbonate, poly (allyl diglycol carbonate), and polymethyl methacrylate, (b) and (d) are a material selected from the group consisting of SiO, SiO₁.5, SiO₂ and mixtures thereof and have a thickness of about 110 to about 250 A, and (b), (c) and (d) are repeated once to provide the order (a) (b) (c) (d) (b) (c) (d).

5. The article according to claim 4 wherein the surface of (a) is coating with SiO.

6. The article of claim 4 wherein the surfaces of (b) and (c) are coated with palladium before coating with (c) and (d) respectively.

7. The article according to claim 4 further including a final coating of an abrasion-resistant material.

8. The article according to claim 10 wherein each (b) and (d) layer is about 180 A thick.

9. The article according to claim 1 wherein said substrate is glass and the refractory dielectric has an index of refraction at least 1.6.

10. The article in claim 1 wherein said substrate is a transparent plastic having a layer of SiO on the surface and the refractory dielectric has an index of refraction of at least 1.6.

11. The article according to claim 1 wherein said dielectric is selected from the group consisting of TiO₂, CeO₂, ZrO₂, Nd₂ O₃, MgO, Al₂ O₃ and SiO_x where x is 1 to 2.

12. The article according to claim 1 wherein (c) is about 140 to about 220 A thick.

13. The article according to claim 1 further including a final coating of an abrasion resistant material.

14. The article according to claim 1 further including an adhesion promoting material under one of the layers.

15. A method of treating a substrate to cause it to reflect infrared light which comprises,

(1) coating the substrate with a refractory dielectric material,

(2) coating the material of step 1 with about 110 to about 250 A of silver, and

(3) coating the silver of step 2 with the refractory dielectric of 1.