Polymerized solutions for depositing optical oxide coatings

• US 4,361,598 A
• Filed: 10/24/1980
• Issued: 11/30/1982
• Est. Priority Date: 08/10/1979
• Status: Expired due to Term

• Current Assignee: Westinghouse Electric Company LLC (Brookfield Asset Management Incorporated)
• Original Assignee: Westinghouse Electric Company LLC (Brookfield Asset Management Incorporated)
• Inventors: Yoldas, Bulent E.
• Primary Examiner(s): Hoffman, James R.
• Application Number:
  US06/200,164
• Time in Patent Office: 767 Days
• Field of Search: 427/74, 427/106, 427/160, 427/162, 427/372.2, 427/380, 427/397.7, 427/164, 106/287.16, 106/287.17, 106/287.18, 106/287.19
• US Class Current: 427/74
• CPC Class Codes: C07F 7/003 without C-Metal linkages
• CPC Class Codes: C07F 7/04 Esters of silicic acids
• CPC Class Codes: C08G 79/00 Macromolecular compounds obtained by reactions forming a linkage containing atoms other than silicon, sulfur, nitrogen, oxygen, and carbon with or without the latter elements in the main chain of the macromolecule
• CPC Class Codes: C09D 185/00 Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing atoms other than silicon, sulfur, nitrogen, oxygen, and carbon; Coating compositions based on derivatives of such polymers
• CPC Class Codes: H01L 31/02168 the coatings being antireflective or having enhancing optical properties for the solar cells
• CPC Class Codes: Y02E 10/50 Photovoltaic [PV] energy

Abstract

A clear solution is prepared by reacting metal alkoxide with a mixture of critical amounts of water and/or acid in an alcohol diluted medium. Alkoxides may be Ti(OR)₄ or Ta(OR)₅, or another metal alkoxide such as Si(OR)₄ in admixture with these alkoxides. Acids may be HCl or HNO₃. Quarter wave inorganic optical coatings are deposited by applying the alkoxide solution to a substrate then heating the coating at over 350° C. The coatings reduce reflectivity on silicon solar cells. The index of refraction of the coating can be varied by several techniques, including altering the proportion of titanium and silicon in the coating firing temperature, firing atmosphere. Thicknesses of the coating can be controlled by varying the rpm in spin application, withdrawal rate in dipping application, by concentration of the solution, by the type of solvent or the degree of polymerization of the titanium complexes.

Claims

1. A clear stable solution which comprises:

(A) alkoxide having the general formula M(OR)_n where M is selected from the group consisting of 0 to 100% Ti, 0 to 25% Si, 0 to 100% Ta, and up to 15% of a metal ion which forms an alkoxide, R is alkyl from C₁ to C₆, and n is the valence of M;

(B) about 1.7 to about 4 moles of water per mole of alkoxide;

(C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and

(D) a sufficient amount of a suitable acid to prevent cloudiness.

2. A solution according to claim 1 wherein the solids content is about 2 to about 8% by weight based on equivalent oxide.

3. A solution according to claim 1 which includes about 0.014 to about 0.2 mole of acid per mole of alkoxide.

4. A solution according to claim 3 wherein said acid is selected from the group consisting of nitric acid, hydrochloric acid, and mixtures thereof.

5. A solution according to claim 1 wherein said alcohol is ethyl alcohol.

6. A solution according to claim 1 wherein R is selected from the group consisting of ethyl, isopropyl, butyl, and mixtures thereof.

7. A solution according to claim 1 wherein M is all Ti.

8. A solution according to claim 1 wherein M is a mixture of Ti and Si.

9. A solution according to claim 1 wherein the amount of water is 1.8 to 2.2 moles per mole of alkoxide.

10. A method of preparing an oxide coating on a substrate, said coating having a predetermined index of refraction between about 1.4 and about 2.4 comprising:

(A) preparing a clear solution according to claim 1 wherein M is a 0 to 25% Si and the remainder Ti;

(B) applying said clear solution to said substrate; and

(C) heating said substrate to about 300°

to about 600°

C.

11. A method according to claim 10 wherein said substrate is heated in a vacuum.

12. A method according to claim 10 wherein said substrate is silicon.

13. A method according to claim 10 wherein said application is by dipping.

14. A method according to claim 10 wherein said method is applied twice to the same substrate so that a two-layered coating is produced.

15. A method according to claim 14 wherein the lower layer is TiO₂ fired in vacuum and the top layer is 90% TiO₂ and 10% SiO₂ fired in air, and each layer is a quarter wavelength in thickness.

16. A method of preparing a clear solution of a metal alkoxide comprising:

(A) adding sufficient alcohol to give a final solids content of about 0.1 to about 15% by weight based on equivalent oxide to either or both of;

(1) alkoxide having the general formula M(OR)_n where M is selected from the group consisting of 0 to 100% Ti, 0 to 30% Si, 0 to 100% Ta, and up to 15% of another metal ion which forms an alkoxide, R is alkyl from C₁ to C₆, and n is the valence of M; and

(2) about 1.7 to about 4 moles of water per mole of alkoxide;

(B) mixing together said alkoxide and said water; and

(C) adding a sufficient amount of a suitable acid to prevent cloudiness.

17. A method according to claim 16 wherein said alcohol is added entirely to said water.

18. A method according to claim 16 wherein titanium alkoxide is added to a mixture of said alcohol and partially hydrolyzed silicon alkoxide.

19. A method according to claim 16 wherein a mixture of alkoxides is used and each alkoxide is partially hydrolyzed before mixing.

20. A method according to claim 16 wherein said acid is added to a mixture of said water and said alcohol, which is then mixed with said alkoxide.

21. A method according to claim 16 wherein the amount of water is 1.8 to 2.2 moles per mole of alkoxide.

22. A method according to claim 16 wherein the solids content is about 2 to about 8% by weight based on equivalent oxide.

23. A method according to claim 16 wherein said acid is selected from the group consisting of nitric acid, hydrochloric acid, and mixtures thereof.

24. A method according to claim 16 wherein said water is diluted with said alcohol, which is then mixed with said alkoxide.

25. A method according to claim 16 wherein the amount of said acid is about 0.014 to about 0.2 moles per mole of alkoxide.

26. A method according to claim 16 wherein said solution is aged for several hours prior to use.

27. A method according to claim 16 wherein said solution is applied to a substrate by dipping said substrate into said solution.

28. A clear stable solution which comprises:

(A) alkoxide having the general formula M(OR)_n where at least 60% of M is selected from one of titanium and tantalum, up to 25% of M is silicon, and up to 15% of M is a metal which forms an alkoxide, each R is independently selected from C₁ to C₆, and n is the valence of each M;

(B) about 1.7 to about 4 moles of water per mole of alkoxide;

(C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and

(D) about 0.014 to about 0.2 moles of acid per mole of alkoxide.

29. A method of coating a substrate with a solid continuous layer of a metal oxide comprising:

(1) preparing a clear stable solution which comprises;

(A) alkoxide having the general formula M(OR)_n where at least 60% of M is selected from one of titanium and tantalum, up to 25% of M is silicon, and up to 15% of M is a metal which forms an alkoxide, each R is independently selected from C₁ to C₆, and n is the valence of each M;

(B) about 1.7 to about 4 moles of water per mole of alkoxide;

(C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and

(D) about 0.014 to about 0.2 moles of acid per mole of alkoxide.

(2) applying said clear stable solution to said substrate;

(3) heating said substrate to about 300°

to about 600°

C.