Corrugated coaxial cable

• US 4,368,350 A
• Filed: 05/28/1981
• Issued: 01/11/1983
• Est. Priority Date: 02/29/1980
• Status: Expired due to Term

• Current Assignee: Andrew Corporation (CommScope Holding Company, Inc.)
• Original Assignee: Andrew Corporation (CommScope Holding Company, Inc.)
• Inventors: Perelman, Robert D.
• Primary Examiner(s): Mayewsky, Volodymyr Y.
• Application Number:
  US06/267,901
• Time in Patent Office: 593 Days
• Field of Search: 174/102 D, 174/106 D, 174/107, 174/110 F, 264/53, 264/45.9, 264/DIG. 13, 138/121
• US Class Current: 174/102.00D
• CPC Class Codes: C08J 2327/12 containing fluorine atoms
• CPC Class Codes: C08J 2427/00 Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers
• CPC Class Codes: C08J 9/0061 characterized by the use of several polymeric components
• CPC Class Codes: C08J 9/144 containing carbon, halogen and hydrogen only
• CPC Class Codes: H01B 11/1839 of cellular structure
• CPC Class Codes: H01B 13/142 of cellular material
• CPC Class Codes: Y10S 264/13 Cell size and distribution control while molding a foam

Abstract

An improved foamable dielectric composition comprising a melt extrudable perfluorocarbon resin containing therein (i) a polytetrafluoroethylene (PTFE) nucleating agent and (ii) a volatile blowing agent, preferably a lower fluorocarbon blowing agent having only one or two carbon atoms; a process for forming such a composition; and, products produced therewith. More specifically, a foamed melt extudable fluorinated ethylene-propylene (FEP) polymer containing therein a PTFE nucleating agent and blown to a foamed structure by means of a volatile fluid--e.g., a lower fluorocarbon such as fluoromethane or, preferably, fluoroethane, a process for forming such a foamed composition; and, products produced therewith such as jacketed electrical conductors and/or coaxial cables wherein at least one conductor is bonded to such a foamed melt extrudable resin. The foamed dielectric melt extrudable resin is characterized by its thermal stability, fire resistance, small closed cell structure, low density, and low insulating loss characteristics. In a preferred embodiment, the melt extrudable foamed resin comprises a perfluorocarbon polymer having a closed cellular structure with cells ranging from 10 to 40 mils., a density at least as low as 1.0 g./cc., and an insulation loss of less than 1.8 db/100 ft. at 1000 MHz.

Claims

1. A coaxial cable comprising, in combination, an inner conductor, a generally tubular outer conductor coaxially surrounding said inner conductor in spaced relation thereto, and a continuous unitary layer of a foamed fluorinated ethylene-propylene polymer dielectric containing a polytetrafluoroethylene nucleating agent bonded to said inner conductor along the entire length and around the entire circumference of said inner conductor in the space between said inner and outer conductors and engaging at least portions of the inner surface of said outer conductor so as to maintain a fixed spaced relationship between said inner and outer conductors, said foamed dielectric having closed cells with an average cell size on the order of from 10 to 40 mils., a density of less than about 1.0 g/cc., and an insulation loss of less than about 1.8 db/100 ft. at 1000 MHz.

2. A coaxial cable as set forth in claim 1 wherein said foamed fluorinated ethylene-propylene polymer dielectric is a copolymer of tetrafluoroethylene and hexafluoropropylene.

3. A coaxial cable as set forth in claim 1 wherein said foamed dielectric is adhesively bonded to said inner conductor.

4. A coaxial cable as set forth in claim 1 wherein said outer conductor is corrugated.

5. A coaxial cable as set forth in claim 4 wherein the corrugations in said outer conductor are annular.

6. A coaxial cable as set forth in claim 1 wherein on the order of 0.5 parts by weight of polytetrafluoroethylene are contained within on the order of 100 parts by weight of the fluorinated ethylene-propylene polymer dielectric.

7. A coaxial cable as set forth in claim 1 wherein the average particle size of the polytetrafluoroethylene is less than 200 microns.