Ultrathin film, process for production thereof, and use thereof for concentrating a specified gas in a gaseous mixture

• US 4,493,714 A
• Filed: 05/04/1983
• Issued: 01/15/1985
• Est. Priority Date: 05/06/1982
• Status: Expired due to Term

• Current Assignee: Teijin Limited
• Original Assignee: Teijin Limited
• Inventors: Yamada, Takeyoshi, Ueda, Fumio, Hashimoto, Eiichi, Mori, Koh
• Primary Examiner(s): Spitzer, Robert
• Application Number:
  US06/491,536
• Time in Patent Office: 622 Days
• Field of Search: 55/16, 55/68, 55/158, 210/500.2
• US Class Current: 95/45
• CPC Class Codes: B01D 69/125 In situ manufacturing by polymerisation, polycondensation, cross-linking or chemical reaction
• CPC Class Codes: B01D 71/54 Polyureas; Polyurethanes
• CPC Class Codes: B01D 71/70 Polymers having silicon in the main chain, with or without sulfur, nitrogen, oxygen or carbon only
• CPC Class Codes: C08G 18/3225 Polyamines
• CPC Class Codes: C08G 18/3893 containing silicon
• CPC Class Codes: C08G 18/72 Polyisocyanates or polyisothiocyanates
• CPC Class Codes: C08G 18/778 silicon

Abstract

An ultrathin film composed substantially of silicon-containing polyurea comprising polyaddition bonded units derived from

(A) at least one polyamine selected from the group consisting of silicon-containing polyamines and hydrocarbon-type polyamines, each of said polyamines containing at least two primary or secondary amino groups in the molecule, and

(B) at least one polyisocyanate compound selected from the group consisting of silicon-containing polyisocyanates and hydrocarbon-type polyisocyanates, each of said polyisocyanates having at least two isocyanate groups in the molecular chains;

provided that when the polyisocyanate compound is the hydrocarbon-type polyisocyanate alone, at least one of the selected polyamines is a silicon-containing polyamine containing at least one terminal amino group in the molecule.

A composite structure composed of a microporous supporting film and the ultrathin film supported thereon is useful for the production of a gaseous mixture containing a specified gas in a high concentration from a mixture of two or more gases including said specified gas, and is prepared by subjecting the polyamine and the polyisocyante compound to interfacial polyaddition reaction on a microporous supporting film to form an ultrathin film composed substantially of a silicon-containing polyurea on the microporous supporting film.

Claims

1. An ultrathin film composed substantially of silicon-containing polyurea comprising polyaddition bonded units derived from

(A) at least one polyamine selected from the group consisting of silicon-containing polyamines having in the molecule at least two units of the following formula ##STR98## wherein R³ represents a monovalent hydrocarbon group or a fluorocarbon group, R¹ and R² are identical or different and represent a hydrogen atom or a monovalent hydrocarbon group which may have a primary or secondary amino group, or R¹ and R² may be bonded to each other to form an alkylene group interrupted by the nitrogen atom forming the secondary amino group, and n is an integer of 1 to 10, provided that R¹ and R² are not simultaneously aliphatic, alicyclic or aromatic groups free from the amino group,

not all, but at least one, of the units of formula (I) forming a unit represented by the following formula ##STR99## wherein R¹, R², R³ and n are as defined, the free bond from the silicon atom is bonded directly to another carbon atom or another oxygen atom, and the free bond from the oxygen is bonded directly to another siloxane atom,

and hydrocarbon-type polyamines containing at least two primary or secondary amino groups in the molecule, and

(B) at least one polyisocyanate compound selected from the group consisting of silicon-containing polyisocyanates having at least 2 isocyanate groups in the molecular chains and hydrocarbon-type polyisocyanates having at least 2 isocyanate groups in the molecular chains;

provided that when the polyisocyanate compound is the hydrocarbon-type polyisocyanate alone, at least one of the selected polyamines is a silicon-containing polyamine containing in the molecule at least one unit of formula (I)-a in which the free bond from the silicon atom is bonded to a monovalent hydrocarbon group.

2. The film of claim 1 wherein the silicon-containing polyamine has a unit of the following formula ##STR100## wherein R⁴ and R⁵ are identical or different and each represents a monovalent hydrocarbon group or a fluorocarbon group, in addition to the units of formulae (I) and (I)-a.

3. The film of claim 1 wherein in formulae (I) and (I)-a, R³ is an alkyl group having 1 to 10 carbon atoms, a cycloalkyl group having 5 or 6 carbon atoms, a phenyl group or a tolyl group, or a corresponding fluorocarbon group resulting from substitution of each said hydrocarbon group by fluorine.

4. The film of claim 1 wherein in formulae (I) and (I)-a, at least one of R¹ and R² is a hydrogen atom.

5. The film of claim 1 wherein in formulae (I) and (I)-a, the hydrocarbon group respresented by R¹ and R² which may have a primary or secondary amino group is an alkyl group having 1 to 12 carbon atoms, an alicyclic group having 6 to 15 carbon atoms, an aromatic group having 6 to 15 carbon atoms, or an aralkyl group having 7 to 15 carbon atoms which may have a primary or secondary amino group.

6. The film of claim 1 wherein in formulae (I) and (I)-a, n is 2 to 6.

7. The film of claim 1 wherein the silicon-containing polyamine is represented by the following formula ##STR101## wherein R⁴ and R⁵ are identical or different and each represents a monovalent hydrocarbon group or a fluorocarbon group, R¹¹, R¹², R¹³ and R¹⁴ are identical or different and are selected from the group defined for R¹ and R², x and y are identical or different and represent an integer of 1 to 10, and r is a number of 1 to 250.

8. The film of claim 1 wherein the silicon-containing polyamine is represented by the following formula ##STR102## wherein R¹⁵ and R¹⁶ are identical or different and each represents a monovalent hydrocarbon group, a fluorocarbon group or a group of the formula ##STR103## in which R¹⁹ and R²⁰ are identical or different and are selected from the groups defined for R¹ and R² above and z is an integer of 1 to 10, R¹⁷ and R¹⁸ are identical or different and each represents a hydroxyl group, a monovalent hydrocarbon group, a fluorocarbon group, or a monovalent hydrocarbon-O--group, and p is a number of 1 to 250, provided that R¹⁵ and R¹⁶ bonded to the silicon atoms are not simultaneously the group of formula (a), and the compound of formula (IV) contains at least two primary or secondary amino groups based on the group of formula (a).

9. The film of claim 1 wherein the hydrocarbon-type polyamine is an aliphatic diamine having 2 to 12 carbon atoms, an aliphatic triamine having 4 to 12 carbon atoms, an aliphatic tetramine having 4 to 12 carbon atoms, an alicyclic diamine having 6 to 15 carbon atoms, or an aromatic diamine having 6 to 15 carbon atoms.

10. The film of claim 1 wherein the siloxane-containing polyisocyanate compound is represented by the following formula ##STR104## wherein R⁴ and R⁵ are identical or different and represent a monovalent hydrocarbon group or a fluorocarbon group, X¹ and X² are identical or different and represent a single bond, or a group of the following formula ##STR105## wherein Y³ represents a hydrocarbon group having 3 to 15 carbon atoms, Z³ represents ##STR106## --O-- or --S--, R⁸ represents a hydrogen atom or a hydrocarbon group having 1 to 6 carbon atoms, provided that Y³ in the group of formula (b) is bonded to the isocyanate group of formula in formula (V), l and m are identical or different and represent an integer of 1 to 10, and q is a number of 1 to 250.

11. The film of claim 1 wherein the hydrocarbon-type polyisocyanate is an aliphatic diisocyanate having 3 to 17 carbon atoms, an alicyclic diisocyanate having 8 to 17 carbon atoms, an aralkyl diisocyanate having 9 to 17 carbon atoms, a monocyclic or dicyclic aromatic diisocyanate having 8 to 17 carbon atoms, a tricyclic or higher aromatic tri- to dodeca-isocyanate having about 23 to about 100 carbon atoms.

12. The film of claim 1 wherein the silicon-containing polyurea consists substantially of said polyaddition bonded units.

13. The film of claim 1 which has a thickness of about 0.01 to about 1 micron.

14. The film of claim 1 which has a thickness of about 0.03 to about 0.5 micron.

15. A composite structure composed of a microporous supporting film and the film of claim 1 supported on said supporting film.

16. The composite structure of claim 15 which is in the form of a hollow fiber.

17. The composite structure of claim 15 which is in the form of a flat membrane.

18. A process for producing a composite structure composed of a microporous supporting film and an ultrathin film supported thereon, which comprises subjecting at least one of the polyamines defined in claim 1 and at least one of the polyisocyanate compounds defined in claim 1 to interfacial polyaddition reaction on a microporous supporting film to form an ultrathin film composed substantially of a silicon-containing polyurea on the microporous supporting film, wherein when the polyisocyanate compound is the hydrocarbon-type polyisocyanate alone, a silicon-containing polyamine having in the molecule at least one unit of formula (I)-a in which the free bond from the silicon atom is bonded to a monovalent hydrocarbon group is used as at least a part of the polyamine.

19. The process of claim 18 which comprises applying a solution of at least one of the polyamines defined in claim 1 in a solvent capable of dissolving said polyamine to the microporous supporting film to form a layer of the solution on the surface of the porous supporting film, then applying the polyisocyanate compound in the form of a solution in a solvent capable of dissolving said polyisocyanate compound and being substantially immiscible with the solvent of the polyamine solution, or in the form of a vapor in an inert gas, to the solution layer, thus subjecting the polyamine and the polyisocyanate compound to interfacial polyaddition reaction to form a silicon-containing polyurea on the microporous supporting film.

20. A composite structure composed of a microporous supporting film for the production of a gaseous mixture containing a specified gas in a high concentration from a mixture of two or more gases including said specified gas, wherein said microporous supporting film is made up of the film of claim 1.

21. The use of claim 20 for the production of a gaseous mixture containing oxygen, helium or argon, and carbon dioxide or hydrogen respectively from air, a gaseous mixture composed mainly of helium or argon and nitrogen, a gaseous mixture containing consisting mainly of carbon dioxide and nitrogen, or a gaseous mixture consisting mainly of hydrogen, carbon monoxide and methane.