Method of producing a container

• US 4,564,495 A
• Filed: 11/23/1982
• Issued: 01/14/1986
• Est. Priority Date: 11/26/1981
• Status: Expired due to Term

• Current Assignee: PLM AB Malmo Sweden
• Original Assignee: PLM AB (Ball Corporation)
• Inventors: Nilsson, Torsten, Jakobsen, Kjell M.
• Primary Examiner(s): SILBAUGH, JAN H
• Application Number:
  US06/443,918
• Time in Patent Office: 1,148 Days
• Field of Search: 264/523, 264/531, 264/532, 264/533, 264/534, 264/535, 264/291, 264/292, 264/235, 264/346, 425/525, 425/526, 425/529, 425/392, 425/393
• US Class Current: 264/291
• CPC Class Codes: B29C 2949/072 having variable wall thickness
• CPC Class Codes: B29C 2949/0725 at bottom portion
• CPC Class Codes: B29C 2949/073 having variable diameter
• CPC Class Codes: B29C 2949/0731 at neck portion
• CPC Class Codes: B29C 2949/0733 at body portion
• CPC Class Codes: B29C 2949/0734 at bottom portion
• CPC Class Codes: B29C 2949/0771 Wide-mouth
• CPC Class Codes: B29C 2949/078 characterised by the bottom
• CPC Class Codes: B29C 2949/22 at neck portion
• CPC Class Codes: B29C 2949/24 at flange portion
• CPC Class Codes: B29C 2949/26 at body portion
• CPC Class Codes: B29C 2949/28 at bottom portion
• CPC Class Codes: B29C 49/071 Preforms or parisons characterised by their configuration, e.g. geometry, dimensions or physical properties
• CPC Class Codes: B29C 49/10 using mechanical means for prestretching
• CPC Class Codes: B29C 49/48 Moulds
• CPC Class Codes: B29C 49/4802 with means for locally compressing part(s) of the parison in the main blowing cavity
• CPC Class Codes: B29C 49/6409 Thermal conditioning of preforms B29C49/68 takes precedence
• CPC Class Codes: B29C 55/30 Drawing through a die pultrusion B29C70/52
• CPC Class Codes: B29C 67/0014 for shaping tubes or blown tubular films
• CPC Class Codes: B29K 2067/00 Use of polyesters or derivatives thereof, as moulding material
• CPC Class Codes: B29L 2031/716 : of the wide mouth type, i.e. the diameters of the bottle opening and its body are substantially identical

Abstract

A method of producing a container of polyethylene terephthalate or similar thermoplastic material from a tubular blank of amorphous material. A mechanical forming element moves a transitional zone between amorphous (thicker) material and thinner oriented material stretched to flow during simultaneous elongation of the blank in the direction of movement of the transitional zone. The stretched and oriented material is heated to a temperature higher than the temperature of the material immediately before stretching. As a result, the internal stresses produced in the material during earlier stretching are relieved. Heating causes the length of the material in the direction of stretching also to be reduced. Each subsequent forming stage for shaping the container takes place at a temperature lower than the temperature at the immediately preceding forming stage.

Claims

1. A method of producing a container of thermoplastic material, preferably of polyethylene terephthalate (PET) from a tubular blank of amorphous material, said container having a body and a mouth portion, said method comprising reducing the wall thickness of a tubular blank of amorphous material while concurrently elongating the blank at a temperature conducive to orientation to orient the material of the thus stretched blank by engaging a mechanical forming element with said blank to form a transition zone between amorphous, thicker material and oriented, thinner material and relatively moving said blank and forming element to move said transition zone axially of the blank while concurrently elongating the blank, heating the thus stretched blank to a temperature above the temperature of the blank immediately before stretching to relieve internal stresses produced in said material during stretching, forming the container from the stretched blank in successive forming stages, and maintaining the temperature in each forming stage lower than the temperature in the immediately preceding forming stage.

2. A method as claimed in claim 1 wherein the temperature of the material in the last of said successive forming stages is higher than the highest temperature at which the formed container is to be used.

3. A method as claimed in claim 1 wherein the length of the amorphous blank and the length of the stretched blank are correlated with the highest temperature of the material during said forming of the blank into the container such that the length of the stretched material of the blank after heating to the highest temperature is substantially equal to the corresponding profile length of the material in the formed container.

4. A method as claimed in claim 1 wherein said material is polyethylene terephthalate (PET) and the highest temperature of the material during said forming of the blank to the container is a maximum of approximately 160°

C. in the first forming stage, the material in each subsequent forming stage having a temperature lower than the temperature in the immediately preceding forming stage by approximately 5°

C.

5. A method as claimed in claim 1 wherein the temperature of the material, when it passes the mechanical forming element to undergo flow, has a temperature in the range of or slightly higher than the glass transformation temperature (TG) of the material.

6. A method as claimed in claim 5 wherein said material is polyethylene terephthalate (PET), the material having a temperature of at least 70°

C. when passing the mechanical forming element to undergo flow.

7. A method as claimed in claim 6 wherein the temperature of the material when passing the mechanical forming element is between 70°

and 105°

C.