Process for the production of polymers from silicon alkoxides

• US 4,671,990 A
• Filed: 07/01/1986
• Issued: 06/09/1987
• Est. Priority Date: 07/01/1986
• Status: Expired due to Fees

• Current Assignee: Manville Corporation Ken-Caryl Ranch Colorado
• Original Assignee: Manville Corporation (Berkshire Hathaway Incorporated)
• Inventors: Hucks, Robert T. Jr., Jada, Sivananda S.
• Primary Examiner(s): McCamish, Marion C.
• Application Number:
  US06/881,998
• Time in Patent Office: 343 Days
• Field of Search: 428/266, 428/268, 428/273, 428/288, 428/290, 428/429, 428/447, 528/12, 528/20
• US Class Current: 442/136
• CPC Class Codes: C08K 5/098 Metal salts of carboxylic acids
• CPC Class Codes: C08L 83/02 Polysilicates
• CPC Class Codes: C08L 83/04 Polysiloxanes
• CPC Class Codes: Y10T 428/31612 As silicone, silane or siloxane
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane
• CPC Class Codes: Y10T 442/2631 Coating or impregnation provides heat or fire protection
• CPC Class Codes: Y10T 442/273 Coating or impregnation provides wear or abrasion resistance
• CPC Class Codes: Y10T 442/2992 Coated or impregnated glass fiber fabric

Abstract

Polymeric silicon alkoxide solutions are produced and then stabilized by the addition of calcium acetate. The calcium acetate serves to prevent the rapid evaporation of the polymerized silicon solution when applied as a coating to various substrates. Glass fiber substrates are preferred.

Claims

1. A novel process for the production of a polymeric substance from silicon alkoxide comprising in order the steps of:

(a) mixing an alcohol and silicon alkoxide in the presence of an esterification catalyst;

(b) adding to said mixture in 1(a) a carboxylic acid in order to form a polymeric network of silicon alkoxide; and

(c) adding calcium acetate to said polymeric network of silicon alkoxide formed in 1(b) in an amount of from about 0.1-2 wt % of the weight of said polymeric network of silicon alkoxide solution.

2. A process according to claim 1 wherein said silicon alkoxide is tetraethoxysilane.

3. A substrate coated with the polymeric substance of claim 2.

4. A coated substrate according to claim 3 wherein said substrate is a fiber glass mat.

5. A process according to claim 1 wherein said polymeric network of silicon alkoxide formed in step 1(b) is diluted with an inert diluent before said calcium acetate is added in step 1(c).

6. A process according to claim 5 wherein said inert diluent is added in an amount from about 12 to about 15 wt % of the total silica content of said polymeric network of silicon alkoxide solution.

7. A process according to claim 5 wherein said inert diluent consists essentially of a mixture of alcohol and water in a weight ratio of 1:

1.

8. A process according to claim 1 wherein said carboxylic acid is added to said mixture in 1(b) over a period of eight (8) hours.

9. A substrate coated with the polymeric substance of claim 1.

10. A coated substrate according to claim 9 wherein said substrate is a fiber glass mat.