Method for making a fluid cooled acyclic generator rotor

• US 4,679,314 A
• Filed: 12/23/1985
• Issued: 07/14/1987
• Est. Priority Date: 12/23/1985
• Status: Expired due to Fees

• Current Assignee: General Dynamics Defense Systems Incorporated (General Dynamics Corporation)
• Original Assignee: General Electric Company
• Inventors: Coffman, Leonard, Lenz, Henry G., Beltran, Adrian M.
• Primary Examiner(s): Hall, Carl E.
• Application Number:
  US06/812,033
• Time in Patent Office: 568 Days
• Field of Search: 310/58, 310/61, 310/178, 310/60 A, 310/44, 29/598, 228/175
• US Class Current: 29/598
• CPC Class Codes: H02K 31/00 Acyclic motors or generators, i.e. DC machines having drum or disc armatures with continuous current collectors
• CPC Class Codes: H02K 9/197 in which the rotor or stator space is fluid-tight, e.g. to provide for different cooling media for rotor and stator
• CPC Class Codes: Y10T 29/49012 Rotor

Abstract

An internally cooled rotor for an acyclic generator is disclosed as having a ferromagnetic steel core to which is diffusion bonded a cylinder copper conductor in which is embedded a multiplicity of cooling tubes communicating with coolant passages formed in the core. The cooling tubes are implanted in a hot isostatic pressure process during which the copper cylinder is at least in part created by the densification of copper powder to a non-porous mass.

Claims

1. A method for manufacturing a fluid cooled rotor for an acyclic electromagnetic machine comprising the steps of:

A. providing a rotor core of a ferromagnetic steel having a peripheral surface;

B. machining internal passages in said core opening into said core peripheral surface for accommodating the circulation of a coolant;

C. providing a plurality of coolant tubes;

D. fixedly supporting said coolant tubes in spaced relation to said peripheral surface, said tubes being distributed about the periphery of said core;

E. coupling inlet and outlet ends of said tubes in coolant flow connection with said passages at said peripheral surface; and

F. forming a current conductor enveloping said tubes and diffusion bonded to said core peripheral surface from a metallic powder by hot isostatic pressure, said passages being vented to the isostatic pressure to prevent collapse of said tubes.

2. The method defined in claim 1, wherein said metallic powder consists predominately of copper.

3. The method defined in claim 1, which further includes the step of sealingly affixing a container about the periphery of said core for containing said metallic powder during the application of said hot isostatic pressure.

4. The method defined in claim 3, which further includes the steps of removing said container and machining said formed current conductor to a desired surface configuration.

5. The method defined in claim 1, wherein said coolant tube supporting step is achieved by providing a layer of current conductor material about said core periphery and secured to said peripheral surface thereof, machining elongated surface grooves in the periphery of said layer, seating said tubes in said grooves, and affixing said tubes in place, whereby said current conductor is formed by said hot isostatic pressure as an integral composite of said layer diffusion bonded to said core peripheral surface and said metallic powder as a densified non-porous mass diffusion bonded to the peripheral surface of said layer and limited portions of said core peripheral surface beyond said layer, whereby said coolant tubes are fully embedded in said current conductor.

6. The method defined in claim 5, wherein said layer is provided as a sheet wrapped about the core periphery.

7. The method defined in claim 5, wherein said layer is also created as a densified non-porous mass from metallic powder by the application of hot isostatic pressure.

8. The method defined in claim 5, wherein said layer and said mass consist predominately of copper.

9. The method defined in claim 5, which further includes the step of sealingly affixing a container about the periphery of said core for containing said metallic powder during the application of said hot isostatic pressure.

10. The method defined in claim 9, which further includes the steps of removing said container, heat treating the core-current conductor assembly, and machining said formed current conductor to a desired surface configuration.

11. The method defined in claim 10, wherein said layer and said mass consist predominately of copper.

12. The method defined in claim 11, which further includes the step of nickel plating said core peripheral surface to promote diffusion bonding of said layer and said mass thereto.

13. The method defined in claim 12, wherein said hot isostatic pressure is applied at a temperature of approximately 1825°

F. and a pressure of approximately 15,000 psi for approximately two hours.

14. The method defined in claim 13, which further includes the step of heating said container under a vacuum to outgas said metallic powder therein.