Process for the production of a shaped parts from pieces of sheet metal of different thicknesses

• US 4,827,100 A
• Filed: 12/18/1987
• Issued: 05/02/1989
• Est. Priority Date: 12/22/1986
• Status: Expired due to Term

• Current Assignee: Thyssen Stahl AG Kaiser-Silhelm-Strasse 100 4100 Duisburg 11
• Original Assignee: Thyssen Stahl AG
• Inventors: Prange, Wilfried, Frings, Adam
• Primary Examiner(s): ALBRITTON, CLARENCE
• Application Number:
  US07/135,194
• Time in Patent Office: 501 Days
• Field of Search: 219/121 L, 219/121 LM, 219/121 LC, 219/121 LD, 219/121.6, 219/121.85, 219/121.63, 219/121.64
• US Class Current: 219/121.64
• CPC Class Codes: B23K 2101/35 Surface treated articles
• CPC Class Codes: B23K 2103/08 Non-ferrous metals or alloys
• CPC Class Codes: B23K 2103/50 Inorganic material, e.g. metals, not provided for in B23K2103/02 – B23K2103/26
• CPC Class Codes: B23K 26/24 Seam welding
• CPC Class Codes: B23K 26/244 Overlap seam welding
• CPC Class Codes: B23K 26/32 taking account of the properties of the material involved
• CPC Class Codes: Y10T 428/12389 having variation in thickness
• CPC Class Codes: Y10T 428/12799 Next to Fe-base component [e.g., galvanized]

Abstract

A process for making a shaped member from sheet metal pieces (37,38) of different thicknesses. In the process flat sheet metal pieces (37,38) are butt welded at their cut edges by laser beam welding. Then the unit, welded together from a number of sheet metal pieces (37,38) of different thickness, are converted into a shaped member by pressing or deep drawing. Since the material of sheet metal pieces (37,38) is not much affected by laser beam welding and the laser-beam-welded joint (39) does not expand much, the joint (39) has no adverse effect on shaping, nor is any anti-corrosion protection, for example, of zinc lost during laser beam welding.

Claims

1. A process for producing shaped parts shaped by pressing from welded sheet metal pieces of different thicknesses, characterized in that flat pieces of sheet metal of different thicknesses are butt welded with a laser beam without adding filler material and then shaped as a unit by pressing.

2. A process according to claim 1, characterized in that the pieces of sheet metal are welded from one side, the surfaces of the pieces of sheet metal on that side being offset in relation to one another.

3. A process according to claim 1, characterized in that the laser beam is so guided that the thicker piece of sheet metal contains the larger proportion of the welding zone.

4. A process according to claim 3, characterized in that welding is performed with the welding beam directed at an inclination to the surfaces of the pieces of sheet metal, one component of the laser beam direction being directed towards the exposed cut edge of the thicker piece of sheet metal.

5. A process according to claim 4, characterized in that the laser beam is kept away from the transitional zone between the exposed cut edge and the surface of the thicker piece of sheet metal.

6. A process according to claim 1, characterized in that a gas cushion, acts on the root side of the pieces of sheet metal in the welding joint zone at least during the molten liquid phase.

7. A process according to claim 1, wherein the sheet metal pieces have a metallic anti-corrosion protection on at least one side.

8. A process according to claim 1, wherein at least one side of the sheet metal pieces are covered by zinc.

9. A process according to claim 1, wherein the gas cushion is an inert gas.

10. A process according to claim 1, wherein the press shaping is deep drawing.