Process of bending thermoplastics sheets and manufacturing laminated light transmitting panels

• US 4,842,664 A
• Filed: 08/10/1987
• Issued: 06/27/1989
• Est. Priority Date: 08/09/1986
• Status: Expired due to Term

• Current Assignee: Glaverbel
• Original Assignee: Glaverbel
• Inventors: Baudin, Pol
• Primary Examiner(s): Dawson, Robert A.
• Application Number:
  US07/083,275
• Time in Patent Office: 687 Days
• Field of Search: 156/99, 156/102, 156/242, 156/278, 428/412, 264/241, 264/320
• US Class Current: 156/102
• CPC Class Codes: B29C 35/16 Cooling cooling extruded material B29C48/911; cooling preforms for blow moulding B29C49/6427; cooling blown articles B29C49/66; cooling tyres during post cure inflation B29D30/0643
• CPC Class Codes: B29C 53/04 of plates or sheets B29C63/04 takes precedence; bending or folding paper B31F1/0003; folding films B65H45/00
• CPC Class Codes: B29C 53/84 Heating or cooling
• CPC Class Codes: B29L 2009/00 Layered products
• CPC Class Codes: B32B 17/10005 laminated safety glass or glazing
• CPC Class Codes: B32B 17/10018 comprising only one glass sheet
• CPC Class Codes: B32B 17/10036 comprising two outer glass sheets
• CPC Class Codes: B32B 17/1077 containing polyurethane
• CPC Class Codes: B32B 17/10889 shaping the sheets, e.g. by using a mould B32B17/10816 takes precedence
• CPC Class Codes: B32B 17/1099 After-treatment of the layered product, e.g. cooling
• CPC Class Codes: B32B 2369/00 Polycarbonates
• CPC Class Codes: Y10T 428/31507 Of polycarbonate

Abstract

A process of imparting a predetermined curvature to a sheet of thermoplastics material in which a thermoplastics sheet is bent by placing it against a face of a bending form. The form having a moulding surface area of the required curvature. The process includes heating the thermoplastics sheet and causing or allowing it to conform to the moulding surface area. The thermoplastics sheet is formed oversized and is bent by placing it against a bending form having a moulding surface area portion of the required dimensions and curvature which is surrounded by a bending form surround. Next, the thermoplastics sheet is heated and caused or allowed to conform to the moulding surface area portion while its oversized margins are supported by the bending form surround. Thereafter, the thermoplastics sheet is cooled at a rate slow enough to maintain such conformity, and then the thermoplastics sheet is trimmed to size.

Claims

1. A process of imparting a predetermined curvature to a sheet of thermoplastics material in which a said thermoplastic sheet is bent by placing it against a face of a bending form having a moulding surface area of the required curvature, heating said thermoplastics sheet and causing or allowing it to conform to said moulding surface area, wherein said thermoplastics sheet is formed oversized and is bent by placing it against a bending form having a moulding surface area portion of the required dimensions and curvature which is surrounded by a bending form surround, said thermoplastics sheet being heated and caused or allowed to conform to said moulding surface area portion while its oversized margins are supported by said bending form surround, and said thermoplastics sheet is thereafter cooled at a rate slow enough to maintain such conformity, and wherein said thermoplastics sheet is thereafter trimmed to size and, while it remains in contact with said bending form moulding surface, the thermoplastics material is caused or allowed to cool from its maximum temperature for a first period at a first cooling rate and thereafter for a second period at a second cooling rate which is higher than said first cooling rate.

2. A process according to claim 1, wherein the surfaces of a said thermoplastics sheet are conditioned by a process comprising sandwiching the thermoplastics sheet between a pair of glass moulding plates and subjecting the sandwich to temperature and pressure conditions such as to soften the thermoplastics material and bring about the required surface conditioning, in which process, prior to removal of said moulding plates, the thermoplastics material is caused or allowed to cool from its maximum temperature for a first period at a first cooling rate and thereafter for a second period at a second cooling rate which is higher than said first cooling rate.

3. A process according to claim 2, wherein a plurality of said thermoplastics sheets is interleaved with glass moulding plates to form a multilayer sandwich whereby said plurality of thermoplastics sheets is conditioned simultaneously.

4. A process according to claim 2, wherein such surface conditioning treatment is performed before the thermoplastics material is curved.

5. A process according to claim 1, wherein during the or at least one, and preferably each said first cooling period, the thermoplastics material is caused or allowed to cool at a rate which does not exceed 2°

C. per minute, and which preferably does not exceed 1°

C. per minute.

6. A process according to claim 1, wherein during the or at least one, and preferably each said second cooling period, the thermoplastics material is caused or allowed to cool at a rate which does not exceed 5°

C. per minute, and which preferably does not exceed 2.5°

C. per minute.

7. A process according to claim 1, wherein the or at least one, and preferably each said first cooling period lasts until the temperature of the thermoplastics material has dropped by between 20°

C. and 60°

C.

8. A process according to claim 1, wherein the or at least one, and preferably each said first cooling period lasts between 40 and 90 minutes.

9. A process according to claim 1, wherein the or at least one, and preferably each consecutive first and second cooling periods together last between 90 and 150 minutes.

10. A process according to claim 1, wherein the or at least one, and preferably each said second cooling period lasts at least until the temperature of the thermoplastics material has dropped to 100°

C.

11. A process according to claim 16, wherein the or at least one, and preferably each said second cooling period lasts at least until the temperature of the thermoplastics material has dropped to 80°

C.

12. A process according to claim 1, wherein a sheet of float glass defines the moulding surface of the or each said glass moulding plate.

13. A process according to claim 1, wherein the or at least one said thermoplastics sheet is a sheet of polycarbonate.

14. A process according to claim 1, wherein the or at least one said thermoplastics sheet bears at least one surface coating which is, or is curable to become, harder than the thermoplastics material of that sheet.

15. A process according to claim 2, wherein the or at least one said thermoplastics sheet bears at least one surface coating which is, or is curable to become, harder than the thermoplastics material of that sheet, and curing of said surface coating(s) is effected during said surface conditioning.

16. A process according to claim 14, wherein said surface coating is a melamine coating.

17. A process according to claim 1, wherein said bending form and said bending form surround are constituted by separable elements.

18. A process according to claim 17, wherein said bending form moulding surface area of the required size and curvature is constituted by a face of a curved sheet of glass.

19. A process according to claim 2, wherein said bending form and said bending form surround are constituted by separable elements and wherein said bending form moulding surface area of the required size and curvature is constituted by a face of a curved sheet of glass and wherein said bending form moulding surface area of the required size and curvature is constituted by a face of a curved sheet of glass to which the thermoplastics sheet is subsequently bonded.

20. A process according to claim 1, wherein said thermoplastics sheet is caused or allowed to conform to a concave bending form moulding surface.

21. A process according to claim 1, wherein the transition from said bending form moulding surface area of the required size and curvature to such bending form surround is of sharper curvature than the margin of said bending form moulding surface area.