Turbine casing formed of a heat resistant austenitic cast steel

• US 4,897,132 A
• Filed: 11/30/1987
• Issued: 01/30/1990
• Est. Priority Date: 10/03/1984
• Status: Expired due to Term

• Current Assignee: Kabushiki Kaisha Toshiba (Toshiba Corporation)
• Original Assignee: Kabushiki Kaisha Tohiba
• Inventors: Yamada, Masayuki, Yamamoto, Masao, Watanabe, Osamu, Yebisuya, Takashi
• Primary Examiner(s): Yee, Deborah
• Application Number:
  US07/127,601
• Time in Patent Office: 792 Days
• Field of Search: 420/53, 148/327
• US Class Current: 148/327
• CPC Class Codes: C22C 38/001 containing N
• CPC Class Codes: C22C 38/44 with molybdenum or tungsten
• CPC Class Codes: C22C 38/46 with vanadium

Abstract

Disclosed is a heat resistant austenitic cast steel consisting essentially of 0.03 to 0.09% by weight of carbon, 2.0% by weight or less of silicon, 3.0% by weight or less of manganese, 0.11 to 0.30% by weight of nitrogen, 6 to 15% by weight of nickel, 15 to 19.5% by weight of chromium, 0.01 to 1.0% by weight of vanadium, 1 to 5% by weight of molybdenum, and the balance of iron. The heat resistant austenitic cast steel exhibits excellent mechanical properties such as mechanical strength, elongation, reduction of area and fracture time caused by creep fracture, particularly, under high temperatures. If a turbine casing is formed of the cast steel, it is possible to increase the steam temperature and pressure.

Claims

1. A turbine casing formed of a heat resistant austenitic cast steel consisting of 0.04 to 0.08% by weight of carbon, 2.0% by weight or less of silicon, 0.5-1.9% by weight of manganese, 0.1 to 0.30% by weight of nitrogen, 8.5 to 12% by weight of nickel, 15 to 19.5% by weight of chromium, 0.05 to 0.35 by weight of vanadium, 2 to 3% by weight of molybdenum, 0 to 0.5% by weight of niobium, 0 to 0.5% by weight of titanium and 0 to 0.01 by weight of boron, the balance being iron apart from incidental impurities, said cast steel having been subjected to a homogenizing heat treatment of the as cast steel.

2. The turbine casing according to claim 1, wherein the silicon content of the cast steel is 0.3 to 0.9% by weight.

3. The turbine casing according to claim 1 wherein the nitrogen content of the cast steel is 0.13 to 0.19% by weight.

4. The turbine casing according to claim 1 wherein the chromium content and nickel content of the cast steel are 16 to 19% and 9.5 to 11.5% by weight, respectively.

5. The turbine casing according to claim 1, wherein the austenitic cast steel contains at least one of 0.01 to 0.5% by weight of niobium, 0.002 to 0.5% by weight of titanium and 0.0005 to 0.01% by weight of boron.

6. The turbine casing according to claim 5, wherein the niobium content of the cast steel is 0.02 to 0.10% by weight.

7. The turbine casing according to claim 6, wherein the titanium content of the cast steel is 0.02 to 0.15% by weight.

8. The turbine casing according to claim 7, wherein the boron content of the cast steel is 0.0003 to 0.007% by weight.

9. A turbine casing according to claim 1, wherein the nicket equivalent and the chromium equivalent of cast steel, which are defined below, are 16 to 24% and 18 to 24% by weight, respectively:

space="preserve" listing-type="equation">Ni equivalent=(Ni)+30 (C)+25.7 (N)+0.5 (Mn)

space="preserve" listing-type="equation">Cr equivalent=(Cr)+1.2 (Si)+(Mo)+5 (V)+0.5 (Nb)+1.5 (Ti)+40 (B).