Transparencies

• US 4,959,257 A
• Filed: 07/12/1988
• Issued: 09/25/1990
• Est. Priority Date: 07/17/1987
• Status: Expired due to Term

• Current Assignee: GKN Aerospace Services Limited (Melrose Industries Plc)
• Original Assignee: Lucas Industries Limited (Zeppelin - Stiftung der Stadt Friedrichshafen)
• Inventors: Mukherjee, Arabinda
• Primary Examiner(s): HERBERT JR, THOMAS
• Application Number:
  US07/217,934
• Time in Patent Office: 805 Days
• Field of Search: 430/50, 430/57, 428/621, 428/469, 428/434, 428/432, 428/901, 428/156, 428/216, 427/108, 427/109, 427/110, 204/192.15, 65/60.2
• US Class Current: 428/156
• CPC Class Codes: B64C 1/1492 Structure and mounting of the transparent elements in the window or windscreen
• CPC Class Codes: C03C 17/36 at least one coating being a metal
• CPC Class Codes: C03C 17/3605 Coatings of the type glass/metal/inorganic compound
• CPC Class Codes: C03C 17/3642 the multilayer coating containing a metal layer
• CPC Class Codes: C03C 17/3649 made of metals other than silver
• CPC Class Codes: C03C 17/3673 specially adapted for use in heating devices for rear window of vehicles
• CPC Class Codes: C03C 17/3681 the multilayer coating being used in glazing, e.g. windows or windscreens
• CPC Class Codes: C03C 17/38 at least one coating being a coating of an organic material
• CPC Class Codes: Y10T 428/24479 including variation in thickness
• CPC Class Codes: Y10T 428/24975 No layer or component greater than 5 mils thick
• CPC Class Codes: Y10T 428/265 1 mil or less

Abstract

A transparency such as an aircraft front window has an electrically conductive metal, e.g. gold, film vacuum deposited thereon for demisting and/or defrosting purposes. To increase the reliability of such metal film, a layer of an oxide of indium, e.g. indium tin oxide, is formed on the metal film by a sputtering operation to a typical thickness of 10 to 200 nm.

Claims

1. A transparency comprising a transparent substrate having an electrically conductive de-misting and/or de-icing metal film thereon and electrical supply contacts connected to said metal film for conducting electricity therethrough, with the optional inclusion of a transparent resin layer between said substrate and said electrically conductive metal layer;

and a sputtered layer containing an oxide of indium is provided on said electrically conducting metal film, wherein the thickness of said metal film varies over the surface of the transparency so that the power dissipation of said metal film is uniform over the area of the substrate.

2. The transparency according to claim 1, wherein the thickness of said metal film lies in the range of 0.5 to 15 nm.

3. The transparency according to claim 1, wherein said metal film comprises the product of vacuum deposition of said metal.

4. The transparency according to claim 1, wherein the metal of said metal film is selected from the group consisting of gold, silver, platinum, palladium, copper/silver alloy and copper/aluminium alloy.

5. The transparency according to claim 1, wherein said sputtered layer has a resistivity of about 500 ohm/square.

6. The transparency according to claim 1, wherein said sputtered layer is formed of an oxide of indium selected from the group consisting of indium tin oxide, indium bismuth oxide, indium antimony oxide, indium aluminium oxide and indium zinc oxide.

7. The transparency according to claim 1, wherein the thickness of said metal film lies in the range of 0.6 to 2.5 nm.

8. The transparency according to claim 1, wherein the metal of said film is gold, and said sputtered layer is indium tin oxide.

9. The transparency according to claim 1, wherein the sputtered layer has a thickness of 10 to 200 nm.

10. The transparency according to claim 9, wherein said sputtered layer has a thickness of 30 to 70 nm.