Refractory mass and particles mixture for forming a refractory mass

• US 4,988,647 A
• Filed: 10/04/1988
• Issued: 01/29/1991
• Est. Priority Date: 05/16/1986
• Status: Expired due to Fees

• Current Assignee: Glaverbel
• Original Assignee: Glaverbel
• Inventors: Mottet, Leon-Philippe, Laroche, Pierre, Robyn, Pierre
• Primary Examiner(s): Group, Karl
• Assistant Examiner(s): Brunsman, David M.
• Application Number:
  US07/252,934
• Time in Patent Office: 847 Days
• Field of Search: 501/87, 501/88, 501/89, 501/90, 501/93, 501/94, 501/99, 501/100, 501/101, 501/103, 501/104, 501/105, 501/106, 501/107, 501/108, 501/118, 501/119, 501/120, 501/121, 501/122 , 501/123, 501/125, 501/127, 501/128, 501/133, 501/153, 501/154
• US Class Current: 501/99
• CPC Class Codes: C04B 2111/00155 Sprayable, i.e. concrete-like, materials able to be shaped by spraying instead of by casting, e.g. gunite
• CPC Class Codes: C04B 2235/422 Carbon
• CPC Class Codes: C04B 35/013 containing carbon C04B35/103 takes precedence
• CPC Class Codes: C04B 35/628 Coating the powders or the macroscopic reinforcing agents
• CPC Class Codes: C04B 35/6303 Inorganic additives
• CPC Class Codes: C04B 35/651 Thermite type sintering, e.g. combustion sintering
• CPC Class Codes: C04B 35/66 Monolithic refractories or refractory mortars, including those whether or not containing clay making or repairing of linings F27D1/16
• CPC Class Codes: F27D 1/1652 Flame guniting; Use of a fuel
• CPC Class Codes: F27D 2001/1657 Solid fuel

Abstract

A process of forming a coherent refractory mass on a surface comprises projecting against that surface, together with oxygen, a mixture of refractory particles and fuel which reacts in an exothermic manner with the projected oxygen to release sufficient heat to melt at least the surfaces of the refractory particles and thus form the refractory mass. The projected mixture contains, as fuel, finely divided particles of at least one element which is oxidizable to form a refractory oxide and it also contains carbonaceous particles which are of such a size or composition that carbon particles become occluded in the formed refractory mass. The mixture may contain, as said fuel, finely divided particles having a mean grain size of less than 50 μm of silicon, aluminum and/or magnesium. The carbonaceous particles may comprise a carbonaceous core which is covered by a mantle inhibiting oxidation of the core. The mixture may further contain particles comprising a core of at least one element which is oxidizable to form a refractory oxide which is covered by a mantle inhibiting oxidation of the core. Suitable mantle materials include metallic oxides, nitrides and carbides.

Claims

1. The mixture of particles for use in a ceramic welding process for forming a coherent refractory mass on a surface by projecting against that surface the mixture and oxygen, the mixture comprising:

refractory particles;

fuel particles capable of reacting in an exothermic manner with oxygen to release sufficient heat to melt at least the surfaces of the refractory particles for forming the coherent refractory mass, which fuel particles are finely divided particles having a mean grain size of less than 50 μ

m and are comprised of at least one element which is oxidizable to form a refractory oxide and is selected from the group consisting of silicon, aluminum, and magnesium; and

carbonaceous particles comprising particles of a polymeric material, which carbonaceous particles are of such a size or composition that, when the mixture is projected against the surface in the presence of oxygen under conditions which lead to substantially complete oxidation of the fuel particles and the formation of the coherent refractory mass, the carbonaceous particles will not be completely oxidised, whereby carbon particles become occluded in the coherent refractory mass formed.

2. The mixture of particles for use in a ceramic welding process for forming a coherent refractory mass on a surface by projecting against that surface the mixture and oxygen, the mixture comprising:

refractory particles;

fuel particles capable of reacting in an exothermic manner with oxygen to release sufficient heat to melt at least the surfaces of the refractory particles for forming the coherent refractory mass, which fuel particles are finely divided particles having a mean grain size of less than 50 μ

m and are comprised of at least one element which is oxidisable to form a refractory oxide and is selected from the group consisting of silicon, aluminum, and magnesium; and

carbonaceous particles having a mean grain size in excess of 0.5 mm, which carbonaceous particles are of such a size or composition that, when the mixture is projected against the surface in the presence of oxygen under conditions which lead to substantially complete oxidation of the fuel particles and the formation of the coherent refractory mass, the carbonaceous particles will not be completely oxidized, whereby carbon particles become occluded in the coherent refractory mass formed.

3. A mixture of particles for use in a ceramic welding process for forming a coherent refractory mass on a surface by projecting against that surface the mixture and oxygen, the mixture comprising:

refractory particles;

fuel particles, which fuel particles are capable of reacting in an exothermic manner with oxygen to release sufficient heat to melt at least the surfaces of the refractory particles for forming the coherent refractory mass and which fuel particles are finely divided particles having a mean grain size of less than 50 μ

m and are comprised of at least one element which is oxidizable to form a refractory oxide and is selected from the group consisting of silicon, aluminum, and magnesium; and

carbonaceous particles, which carbonaceous particles are of such a size or composition that, when the mixture is projected against the surface in the presence of oxygen, under conditions which lead to substantially complete oxidation of the fuel particles and the formation of the coherent refractory mass, the carbonaceous particles will not be completely oxidized, whereby carbon particles become occluded in the coherent refractory mass formed,

wherein each of the carbonaceous particles is comprised of a core of carbonaceous material and a mantle comprised of a material which inhibits oxidation of the core, the mantle covering the core.

4. A mixture according to claim 3, wherein the mantle is comprised of at least one material selected from the group consisting of metallic oxides, metallic nitrides and metallic carbides.

5. The mixture according to claim 4, wherein the at least one material is selected from the group consisting of oxides, nitrides and carbides of magnesium, aluminium, silicon, titanium, zirconium and chromium.

6. The mixture according to claim 6, wherein the mantle comprises form 0.02% to 2% by weight of the carbonaceous particles.

7. A mixture of particles for use in a ceramic welding process for forming a coherent refractory mass on a surface by projecting against that surface the mixture and oxygen, the mixture comprising:

refractory particles;

fuel particles, which fuel particles are capable of reacting in an exothermic manner with oxygen to release sufficient heat to melt at least the surfaces of the refractory particles for forming the coherent refractory mass and which fuel particles are finely divided particles having a mean grain size of less than 50 μ

m and are comprised of at least one element which is oxidizable to form a refractory oxide and is selected from the group consisting of silicon, aluminum, and magnesium; and

carbonaceous particles, which carbonaceous particles are of such a size or composition that, when the mixture is projected against the surface in the presence of oxygen, under conditions which lead to substantially complete oxidation of the fuel particles and the formation of the coherent refractory mass, the carbonaceous particles will not be completely oxidized, whereby carbon particles become occluded in the coherent refractory mass formed,

wherein the mixture further comprises further particles comprising at least one element which is oxidizable to form a refractory oxide, which further particles are of such a size or composition that, when the mixture is projected against the surface in the presence of oxygen and under conditions which lead to substantially complete oxidation of the fuel particles and the formation of the coherent refractory mass, such further particles will not be completely oxidized, whereby unoxidized portions of the further particles become occluded in the refractory mass, and

wherein the further particles comprise a core comprised of the at least one element which is oxidizable to form a refractory oxide and a mantle comprised of a material which inhibits oxidation of the core, which mantle covers the core.